Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_5928084_XHj7la.cif"

There are 480 T-atoms per unit cell
There are 960 O-atoms per unit cell

Framework density = 22.14 T-atoms per nm^3
Material density = 2.209 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6449 Angstrom
T1  -- O2  = 1.6589 Angstrom
T1  -- O3  = 1.5920 Angstrom
T1  -- O4  = 1.6100 Angstrom
      mean = 1.6264 Angstrom
        t1 = 0.053808  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.038397  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6487 Angstrom
T2  -- O5  = 1.6604 Angstrom
T2  -- O6  = 1.6640 Angstrom
T2  -- O7  = 1.5843 Angstrom
      mean = 1.6393 Angstrom
        t1 = 0.055559  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.033969  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6396 Angstrom
T3  -- O8  = 1.6006 Angstrom
T3  -- O9  = 1.6177 Angstrom
T3  -- O10 = 1.6217 Angstrom
      mean = 1.6199 Angstrom
        t1 = 0.016679  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.009842  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6773 Angstrom
T4  -- O11 = 1.6052 Angstrom
T4  -- O12 = 1.5428 Angstrom
T4  -- O13 = 1.6858 Angstrom
      mean = 1.6278 Angstrom
        t1 = 0.059396  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.046308  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6389 Angstrom
T5  -- O13 = 1.6551 Angstrom
T5  -- O14 = 1.8304 Angstrom
T5  -- O15 = 1.6561 Angstrom
      mean = 1.6951 Angstrom
        t1 = 0.107250  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.069755  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5428 A <--> 1.8304 A
          Mean   = 1.6417 A
          StdDev = 0.0552 A

       t1 Range  = 0.0167 <-- 0.0585 --> 0.1073
       t2 Range  = 0.0098 <-- 0.0397 --> 0.0698

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.532 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 115.033 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.034 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 112.877 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 118.160 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  95.067 deg; O3  -- O4  = 2 A
       95.067 deg <-- 109.451 deg --> 118.160 deg

O3  -- T2  -- O5  = 121.459 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 105.563 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 102.810 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 106.977 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 101.061 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 120.023 deg; O6  -- O7  = 3 A
       101.061 deg <-- 109.649 deg --> 121.459 deg

O4  -- T3  -- O8  = 107.533 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 108.858 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 113.645 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 110.105 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 107.787 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 108.880 deg; O9  -- O10 = 3 A
       107.533 deg <-- 109.468 deg --> 113.645 deg

O7  -- T4  -- O11 = 108.529 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 103.756 deg; O7  -- O12 = 3 A
O7  -- T4  -- O13 = 123.961 deg; O7  -- O13 = 3 A
O11 -- T4  -- O12 = 108.541 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 108.756 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 102.217 deg; O12 -- O13 = 3 A
       102.217 deg <-- 109.293 deg --> 123.961 deg

O10 -- T5  -- O13 =  95.098 deg; O10 -- O13 = 2 A
O10 -- T5  -- O14 =  96.127 deg; O10 -- O14 = 3 A
O10 -- T5  -- O15 = 105.881 deg; O10 -- O15 = 3 A
O13 -- T5  -- O14 = 139.624 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 109.312 deg; O13 -- O15 = 3 A
O14 -- T5  -- O15 = 104.593 deg; O14 -- O15 = 3 A
       95.098 deg <-- 108.439 deg --> 139.624 deg

        O-T-O SUMMARY
          Range  = 95.0665 deg <--> 139.6238 deg
          Mean   = 109.4155 deg
          StdDev = 9.2628 deg

        O--O SUMMARY
          Range  = 2.3620 A <--> 3.2719 A
          Mean   = 2.6714 A
          StdDev = 0.1728 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 119.207 deg ; T1  -- T1   2.8375 A

T1  -- O2  -- T1  = 130.806 deg ; T1  -- T1   3.0167 A

T1  -- O3  -- T2  = 137.061 deg ; T1  -- T2   3.0158 A

T1  -- O4  -- T3  = 137.510 deg ; T1  -- T3   3.0288 A

T2  -- O5  -- T2  = 115.713 deg ; T2  -- T2   2.8119 A

T2  -- O6  -- T2  = 103.380 deg ; T2  -- T2   2.6113 A

T2  -- O7  -- T4  = 131.211 deg ; T2  -- T4   2.9706 A

T3  -- O8  -- T3  = 134.835 deg ; T3  -- T3   2.9557 A

T3  -- O9  -- T3  = 146.232 deg ; T3  -- T3   3.0960 A

T3  -- O10 -- T5  = 170.318 deg ; T3  -- T5   3.2490 A

T4  -- O11 -- T4  =  99.945 deg ; T4  -- T4   2.4583 A

T4  -- O12 -- T4  = 146.567 deg ; T4  -- T4   2.9552 A

T4  -- O13 -- T5  = 125.791 deg ; T4  -- T5   2.9740 A

T5  -- O14 -- T5  = 145.214 deg ; T5  -- T5   3.4933 A

T5  -- O15 -- T5  = 151.464 deg ; T5  -- T5   3.2100 A


        T-O-T SUMMARY
          Range  = 99.9450° <--> 170.3176 deg
          Mean   = 133.0169 deg
          StdDev = 17.8968 deg

        T--T SUMMARY
          Range  = 2.4583 A <--> 3.4933 A
          Mean   = 2.9789 A
          StdDev = 0.2403 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

T-T-T analysis was not conducted.
T2  -- T2  = 2.6113 Angstrom
T4  -- T4  = 2.4583 Angstrom

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T5  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T5  -- T3  = 3.2490 Angstrom
  T5  -- T4  = 2.9740 Angstrom
  T5  -- T5  = 3.4933 Angstrom
  T5  -- T5  = 3.2100 Angstrom
  T5  -- T5  = 3.4928 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 12 23 33 49 74 108 144 171 204 258 328 404 466 513 577
TD10 = 823
Circuit symbol = 6.6_{2}.6_{2}.6_{2}.6_{2}.8
Weight = 23
Vertex symbol  = 6.6_{2}.6_{2}.6_{2}.6_{2}.12_{12}
Weight = 42

T2 (Si): multiplicity = 96
Coordination Sequence =
    1 4 10 21 38 59 78 96 128 180 236 283 324 375 452 542 624
TD10 = 851
Circuit symbol = 4.6_{2}.4.6_{2}.6.6
Weight = 19
Vertex symbol  = 4.6_{2}.4.6_{2}.6.12_{6}
Weight = 33

T3 (Si): multiplicity = 96
Coordination Sequence =
    1 4 9 17 32 55 76 93 124 177 234 275 308 364 452 551 642
TD10 = 822
Circuit symbol = 4.6.4.6.4.6_{2}
Weight = 17
Vertex symbol  = 4.6.4.6.4.6_{2}
Weight = 17

T4 (Si): multiplicity = 96
Coordination Sequence =
    1 4 10 20 34 54 80 111 147 186 231 286 350 419 484 545 616
TD10 = 878
Circuit symbol = 4.4.6.8_{2}.6.8_{2}
Weight = 22
Vertex symbol  = 4.4.6.8.6.8
Weight = 22

T5 (Si): multiplicity = 96
Coordination Sequence =
    1 4 8 15 29 50 76 105 141 187 233 272 311 366 448 540 622
TD10 = 849
Circuit symbol = 4.4.4.6.4.6_{2}
Weight = 12
Vertex symbol  = 4.4.4.6.4.8
Weight = 17

<TD10> = 844.600
Average ring size = 6.5231