Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_5928082_0V4phA.cif"

There are 480 T-atoms per unit cell
There are 960 O-atoms per unit cell

Framework density = 21.91 T-atoms per nm^3
Material density = 2.186 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6361 Angstrom
T1  -- O2  = 1.6964 Angstrom
T1  -- O3  = 1.6187 Angstrom
T1  -- O4  = 1.6853 Angstrom
      mean = 1.6591 Angstrom
        t1 = 0.062723  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.034835  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6654 Angstrom
T2  -- O5  = 1.6608 Angstrom
T2  -- O6  = 1.6188 Angstrom
T2  -- O7  = 1.5582 Angstrom
      mean = 1.6258 Angstrom
        t1 = 0.042050  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.025868  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.7057 Angstrom
T3  -- O8  = 1.6045 Angstrom
T3  -- O9  = 1.6180 Angstrom
T3  -- O10 = 1.6606 Angstrom
      mean = 1.6472 Angstrom
        t1 = 0.043345  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.023297  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6031 Angstrom
T4  -- O11 = 1.6058 Angstrom
T4  -- O12 = 1.5096 Angstrom
T4  -- O13 = 1.5812 Angstrom
      mean = 1.5749 Angstrom
        t1 = 0.058557  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.044133  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6559 Angstrom
T5  -- O13 = 1.6397 Angstrom
T5  -- O14 = 1.6809 Angstrom
T5  -- O15 = 1.6853 Angstrom
      mean = 1.6655 Angstrom
        t1 = 0.045182  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.024321  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5096 A <--> 1.7057 A
          Mean   = 1.6345 A
          StdDev = 0.0484 A

       t1 Range  = 0.0420 <-- 0.0504 --> 0.0627
       t2 Range  = 0.0233 <-- 0.0305 --> 0.0441

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 106.149 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 113.843 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 106.199 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 111.307 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 122.682 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  96.733 deg; O3  -- O4  = 2 A
       96.733 deg <-- 109.485 deg --> 122.682 deg

O3  -- T2  -- O5  = 119.902 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 107.116 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 105.771 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 108.688 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 105.080 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 110.047 deg; O6  -- O7  = 3 A
       105.080 deg <-- 109.434 deg --> 119.902 deg

O4  -- T3  -- O8  = 105.960 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 108.732 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 118.441 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 107.155 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 106.821 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.157 deg; O9  -- O10 = 3 A
       105.960 deg <-- 109.378 deg --> 118.441 deg

O7  -- T4  -- O11 = 112.107 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 103.962 deg; O7  -- O12 = 2 A
O7  -- T4  -- O13 = 119.163 deg; O7  -- O13 = 3 A
O11 -- T4  -- O12 = 110.237 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 112.049 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 =  97.691 deg; O12 -- O13 = 2 A
       97.691 deg <-- 109.201 deg --> 119.163 deg

O10 -- T5  -- O13 = 105.184 deg; O10 -- O13 = 3 A
O10 -- T5  -- O14 = 113.127 deg; O10 -- O14 = 3 A
O10 -- T5  -- O15 = 109.653 deg; O10 -- O15 = 3 A
O13 -- T5  -- O14 = 103.480 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 110.929 deg; O13 -- O15 = 3 A
O14 -- T5  -- O15 = 113.958 deg; O14 -- O15 = 3 A
       103.480 deg <-- 109.389 deg --> 113.958 deg

        O-T-O SUMMARY
          Range  = 96.7327 deg <--> 122.6823 deg
          Mean   = 109.3902 deg
          StdDev = 5.9806 deg

        O--O SUMMARY
          Range  = 2.3276 A <--> 2.9674 A
          Mean   = 2.6656 A
          StdDev = 0.1323 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 119.530 deg ; T1  -- T1   2.8271 A

T1  -- O2  -- T1  = 134.781 deg ; T1  -- T1   3.1321 A

T1  -- O3  -- T2  = 137.525 deg ; T1  -- T2   3.0612 A

T1  -- O4  -- T3  = 139.528 deg ; T1  -- T3   3.1817 A

T2  -- O5  -- T2  = 112.947 deg ; T2  -- T2   2.7690 A

T2  -- O6  -- T2  = 107.002 deg ; T2  -- T2   2.6026 A

T2  -- O7  -- T4  = 122.262 deg ; T2  -- T4   2.7686 A

T3  -- O8  -- T3  = 149.563 deg ; T3  -- T3   3.0964 A

T3  -- O9  -- T3  = 146.907 deg ; T3  -- T3   3.1020 A

T3  -- O10 -- T5  = 145.881 deg ; T3  -- T5   3.1706 A

T4  -- O11 -- T4  =  97.084 deg ; T4  -- T4   2.4069 A

T4  -- O12 -- T4  = 140.686 deg ; T4  -- T4   2.8432 A

T4  -- O13 -- T5  = 127.673 deg ; T4  -- T5   2.8910 A

T5  -- O14 -- T5  = 134.015 deg ; T5  -- T5   3.0947 A

T5  -- O15 -- T5  = 157.361 deg ; T5  -- T5   3.3050 A


        T-O-T SUMMARY
          Range  = 97.0844° <--> 157.3607 deg
          Mean   = 131.5163 deg
          StdDev = 16.3632 deg

        T--T SUMMARY
          Range  = 2.4069 A <--> 3.3050 A
          Mean   = 2.9501 A
          StdDev = 0.2382 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 2.8271 Angstrom
  T1  -- T1  = 3.1321 Angstrom
  T1  -- T2  = 3.0612 Angstrom
  T1  -- T3  = 3.1817 Angstrom
  T1  -- T3  = 3.3471 Angstrom
T2  -- T2  = 2.6026 Angstrom
T2  -- T4  = 2.7686 Angstrom
T2  -- T2  = 2.7690 Angstrom
T3  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T1  = 3.1817 Angstrom
  T3  -- T1  = 3.3471 Angstrom
  T3  -- T3  = 3.1020 Angstrom
  T3  -- T5  = 3.1706 Angstrom
  T3  -- T3  = 3.0964 Angstrom
T4  -- T2  = 2.7686 Angstrom
T4  -- T4  = 2.4069 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 12 24 38 59 84 114 152 193 245 306 364 425 492 576 680
TD10 = 926
Circuit symbol = 6.6_{2}.6_{2}.6_{2}.6_{2}.8
Weight = 23
Vertex symbol  = 6.6_{2}.6_{2}.6_{2}.6_{2}.12_{14}
Weight = 51

T2 (Si): multiplicity = 96
Coordination Sequence =
    1 4 10 20 35 57 82 107 141 188 240 296 359 426 494 562 641
TD10 = 885
Circuit symbol = 4.6_{2}.4.6_{2}.6.6
Weight = 19
Vertex symbol  = 4.6_{2}.4.6_{2}.6.12_{6}
Weight = 33

T3 (Si): multiplicity = 96
Coordination Sequence =
    1 4 10 21 39 64 89 115 157 212 263 311 372 456 545 614 674
TD10 = 975
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 16
Vertex symbol  = 4.6.4.6.6_{2}.8
Weight = 21

T4 (Si): multiplicity = 96
Coordination Sequence =
    1 4 9 17 30 50 77 111 151 192 234 282 340 412 494 577 660
TD10 = 876
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 13
Vertex symbol  = 4.4.4.6.6.8
Weight = 18

T5 (Si): multiplicity = 96
Coordination Sequence =
    1 4 9 18 33 56 89 127 166 209 259 318 383 449 520 599 682
TD10 = 971
Circuit symbol = 4.4.4.8_{4}.6.6_{2}
Weight = 17
Vertex symbol  = 4.4.4.8.6.8
Weight = 21

<TD10> = 926.600
Average ring size = 6.7347