Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_536089_94hIko.cif"

There are 480 T-atoms per unit cell
There are 960 O-atoms per unit cell

Framework density = 1.94 T-atoms per nm^3
Material density = 0.193 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6177 Angstrom
T1  -- O2  = 1.6262 Angstrom
T1  -- O3  = 1.6155 Angstrom
T1  -- O4  = 1.6243 Angstrom
      mean = 1.6209 Angstrom
        t1 = 0.008012  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003353  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6243 Angstrom
T2  -- O5  = 1.6607 Angstrom
T2  -- O6  = 1.7197 Angstrom
T2  -- O7  = 1.7258 Angstrom
      mean = 1.6826 Angstrom
        t1 = 0.050014  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.015403  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6315 Angstrom
T3  -- O8  = 1.6317 Angstrom
T3  -- O9  = 1.4542 Angstrom
T3  -- O10 = 1.6318 Angstrom
      mean = 1.5873 Angstrom
        t1 = 0.094769  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.096392  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6382 Angstrom
T4  -- O9  = 1.4513 Angstrom
T4  -- O11 = 1.6335 Angstrom
T4  -- O12 = 1.6360 Angstrom
      mean = 1.5897 Angstrom
        t1 = 0.097513  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.077266  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.7227 Angstrom
T5  -- O12 = 1.7253 Angstrom
T5  -- O13 = 1.6622 Angstrom
T5  -- O14 = 1.6267 Angstrom
      mean = 1.6842 Angstrom
        t1 = 0.050656  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014765  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4513 A <--> 1.7258 A
          Mean   = 1.6330 A
          StdDev = 0.0708 A

       t1 Range  = 0.0080 <-- 0.0602 --> 0.0975
       t2 Range  = 0.0034 <-- 0.0414 --> 0.0964

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.628 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.389 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.899 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.052 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.450 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.407 deg; O3  -- O4  = 3 A
       108.899 deg <-- 109.471 deg --> 110.450 deg

O4  -- T2  -- O5  = 107.655 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 108.338 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 109.381 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 110.660 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 110.595 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 110.141 deg; O6  -- O7  = 3 A
       107.655 deg <-- 109.462 deg --> 110.660 deg

O6  -- T3  -- O8  = 114.811 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  =  94.020 deg; O6  -- O9  = 2 A
O6  -- T3  -- O10 = 123.265 deg; O6  -- O10 = 3 A
O8  -- T3  -- O9  = 108.997 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 115.014 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 =  94.087 deg; O9  -- O10 = 2 A
       94.020 deg <-- 108.366 deg --> 123.265 deg

O7  -- T4  -- O9  =  93.596 deg; O7  -- O9  = 2 A
O7  -- T4  -- O11 = 115.116 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 123.438 deg; O7  -- O12 = 3 A
O9  -- T4  -- O11 = 108.807 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 =  93.521 deg; O9  -- O12 = 2 A
O11 -- T4  -- O12 = 115.138 deg; O11 -- O12 = 3 A
       93.521 deg <-- 108.269 deg --> 123.438 deg

O10 -- T5  -- O12 = 110.159 deg; O10 -- O12 = 3 A
O10 -- T5  -- O13 = 110.668 deg; O10 -- O13 = 3 A
O10 -- T5  -- O14 = 108.560 deg; O10 -- O14 = 3 A
O12 -- T5  -- O13 = 110.587 deg; O12 -- O13 = 3 A
O12 -- T5  -- O14 = 108.860 deg; O12 -- O14 = 3 A
O13 -- T5  -- O14 = 107.936 deg; O13 -- O14 = 3 A
       107.936 deg <-- 109.462 deg --> 110.668 deg

        O-T-O SUMMARY
          Range  = 93.5210 deg <--> 123.4380 deg
          Mean   = 109.0061 deg
          StdDev = 7.3198 deg

        O--O SUMMARY
          Range  = 2.2526 A <--> 2.8834 A
          Mean   = 2.6575 A
          StdDev = 0.1848 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  87.719 deg; T1  -- T1  = 4.3295 A
T1  - O1  - T1  - O3  - T2  = 128.422 deg; T1  -- T2  = 5.4417 A
T1  - O1  - T1  - O4  - T1  =  92.281 deg; T1  -- T1  = 4.3295 A
T1  - O2  - T1  - O3  - T2  =  91.080 deg; T1  -- T2  = 4.4271 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3590 A
T2  - O3  - T1  - O4  - T1  = 139.294 deg; T2  -- T1  = 5.5853 A

T1  - O4  - T2  - O5  - T3  = 148.844 deg; T1  -- T3  = 5.4652 A
T1  - O4  - T2  - O6  - T4  = 145.317 deg; T1  -- T4  = 5.4279 A
T1  - O4  - T2  - O7  - T2  =  88.920 deg; T1  -- T2  = 4.4271 A
T3  - O5  - T2  - O6  - T4  =  64.616 deg; T3  -- T4  = 2.8656 A
T3  - O5  - T2  - O7  - T2  =  85.232 deg; T3  -- T2  = 4.0820 A
T4  - O6  - T2  - O7  - T2  =  85.309 deg; T4  -- T2  = 4.0923 A

T2  - O6  - T3  - O8  - T4  =  57.907 deg; T2  -- T4  = 2.6871 A
T2  - O6  - T3  - O9  - T5  = 114.942 deg; T2  -- T5  = 4.5110 A
T2  - O6  - T3  - O10 - T3  =  94.768 deg; T2  -- T3  = 4.0820 A
T4  - O8  - T3  - O9  - T5  =  57.906 deg; T4  -- T5  = 2.6877 A
T4  - O8  - T3  - O10 - T3  =  90.050 deg; T4  -- T3  = 4.0572 A
T5  - O9  - T3  - O10 - T3  =  94.792 deg; T5  -- T3  = 4.0839 A

T2  - O7  - T4  - O9  - T3  =  57.477 deg; T2  -- T3  = 2.6744 A
T2  - O7  - T4  - O11 - T5  = 114.127 deg; T2  -- T5  = 4.5110 A
T2  - O7  - T4  - O12 - T4  =  94.691 deg; T2  -- T4  = 4.0923 A
T3  - O9  - T4  - O11 - T5  =  57.507 deg; T3  -- T5  = 2.6759 A
T3  - O9  - T4  - O12 - T4  =  89.950 deg; T3  -- T4  = 4.0572 A
T5  - O11 - T4  - O12 - T4  =  94.717 deg; T5  -- T4  = 4.0936 A

T3  - O10 - T5  - O12 - T4  =  64.587 deg; T3  -- T4  = 2.8656 A
T3  - O10 - T5  - O13 - T5  = 141.643 deg; T3  -- T5  = 5.3667 A
T3  - O10 - T5  - O14 - T5  =  85.208 deg; T3  -- T5  = 4.0839 A
T4  - O12 - T5  - O13 - T5  = 152.882 deg; T4  -- T5  = 5.5346 A
T4  - O12 - T5  - O14 - T5  =  85.283 deg; T4  -- T5  = 4.0936 A
T5  - O13 - T5  - O14 - T5  =  90.000 deg; T5  -- T5  = 4.4755 A

        T-T-T SUMMARY
          Range  = 57.4769 deg <--> 152.8823 deg
          Mean   = 95.9593 deg
          StdDev = 28.1469 deg

        T--T SUMMARY
          Range  = 2.6744 A <--> 5.5853 A
          Mean   = 4.1474 A
          StdDev = 0.8896 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 140.507 deg ; T1  -- T1   3.0452 A

T1  -- O2  -- T1  = 130.928 deg ; T1  -- T1   2.9587 A

T1  -- O3  -- T1  = 164.420 deg ; T1  -- T1   3.2011 A

T1  -- O4  -- T2  = 134.735 deg ; T1  -- T2   2.9985 A

T2  -- O5  -- T2  = 172.455 deg ; T2  -- T2   3.3141 A

T2  -- O6  -- T3  = 105.855 deg ; T2  -- T3   2.6744 A

T2  -- O7  -- T4  = 105.999 deg ; T2  -- T4   2.6871 A

T3  -- O8  -- T3  = 123.117 deg ; T3  -- T3   2.8696 A

T3  -- O9  -- T4  = 160.993 deg ; T3  -- T4   2.8656 A

T3  -- O10 -- T5  = 105.791 deg ; T3  -- T5   2.6759 A

T4  -- O11 -- T4  = 123.258 deg ; T4  -- T4   2.8746 A

T4  -- O12 -- T5  = 106.154 deg ; T4  -- T5   2.6877 A

T5  -- O13 -- T5  = 172.131 deg ; T5  -- T5   3.3166 A

T5  -- O14 -- T5  = 134.932 deg ; T5  -- T5   3.0050 A


        T-O-T SUMMARY
          Range  = 105.7910° <--> 172.4553 deg
          Mean   = 134.3767 deg
          StdDev = 23.9421 deg

        T--T SUMMARY
          Range  = 2.6744 A <--> 3.3166 A
          Mean   = 2.9410 A
          StdDev = 0.2158 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O6  -- O9  = 2.2604 A
O7  -- O9  = 2.2556 A
O9  -- O10 = 2.2618 A
O9  -- O12 = 2.2526 A
T2  -- T3  = 2.6744 Angstrom
T2  -- T4  = 2.6871 Angstrom
T3  -- T2  = 2.6744 Angstrom
T3  -- T5  = 2.6759 Angstrom
T4  -- T2  = 2.6871 Angstrom
T4  -- T5  = 2.6877 Angstrom
T5  -- T3  = 2.6759 Angstrom
T5  -- T4  = 2.6877 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 8 11 11 10 11 11 10 13 21 30 33 31 32 33 30
TD10 = 111
Circuit symbol = 4.4.4.6.4.6
Weight = 9
Vertex symbol  = 4.4.4.32_{256}.4.*
Weight = 46

T2 (Si): multiplicity = 96
Coordination Sequence =
    1 4 6 7 11 12 9 11 14 15 17 20 29 35 30 31 38
TD10 = 107
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.32_{128}.4.32_{128}
Weight = 44

T3 (Si): multiplicity = 96
Coordination Sequence =
    1 4 5 6 8 10 12 12 16 18 14 16 22 28 34 36 42
TD10 = 106
Circuit symbol = 3.4.3.4.4.4
Weight = 8
Vertex symbol  = 3.4.3.4.4.32_{128}
Weight = 44

T4 (Si): multiplicity = 96
Coordination Sequence =
    1 4 5 6 8 10 12 12 16 18 14 16 22 28 34 36 42
TD10 = 106
Circuit symbol = 3.4.3.4.4.4
Weight = 8
Vertex symbol  = 3.4.3.4.4.32_{128}
Weight = 44

T5 (Si): multiplicity = 96
Coordination Sequence =
    1 4 6 5 5 8 13 17 16 15 17 16 15 21 34 47 48
TD10 = 107
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.32_{128}.4.32_{128}
Weight = 44

<TD10> = 107.400
Average ring size = 27.5263