Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_489716_zIdJOa.cif"

There are 480 T-atoms per unit cell
There are 960 O-atoms per unit cell

Framework density = 1.76 T-atoms per nm^3
Material density = 0.176 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6305 Angstrom
T1  -- O2  = 1.6085 Angstrom
T1  -- O3  = 1.6276 Angstrom
T1  -- O4  = 1.6348 Angstrom
      mean = 1.6253 Angstrom
        t1 = 0.018387  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010790  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6319 Angstrom
T2  -- O5  = 1.6053 Angstrom
T2  -- O6  = 1.6242 Angstrom
T2  -- O7  = 1.6390 Angstrom
      mean = 1.6251 Angstrom
        t1 = 0.021605  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.012323  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.6392 Angstrom
T3  -- O8  = 1.6053 Angstrom
T3  -- O9  = 1.6256 Angstrom
T3  -- O10 = 1.6368 Angstrom
      mean = 1.6267 Angstrom
        t1 = 0.024543  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014318  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O10 = 1.6414 Angstrom
T4  -- O11 = 1.6135 Angstrom
T4  -- O12 = 1.6190 Angstrom
T4  -- O13 = 1.6403 Angstrom
      mean = 1.6286 Angstrom
        t1 = 0.022561  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.012275  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O13 = 1.6571 Angstrom
T5  -- O14 = 1.6046 Angstrom
T5  -- O15 = 1.6427 Angstrom
T5  -- O16 = 1.6369 Angstrom
      mean = 1.6353 Angstrom
        t1 = 0.019367  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.009098  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6046 A <--> 1.6571 A
          Mean   = 1.6282 A
          StdDev = 0.0144 A

       t1 Range  = 0.0184 <-- 0.0213 --> 0.0245
       t2 Range  = 0.0091 <-- 0.0118 --> 0.0143

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.673 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.128 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 113.495 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.325 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 106.789 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.304 deg; O3  -- O4  = 3 A
       106.789 deg <-- 109.452 deg --> 113.495 deg

O4  -- T2  -- O5  = 106.859 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.297 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 114.786 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 109.164 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 106.976 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.592 deg; O6  -- O7  = 3 A
       106.859 deg <-- 109.446 deg --> 114.786 deg

O7  -- T3  -- O8  = 106.554 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 109.508 deg; O7  -- O9  = 3 A
O7  -- T3  -- O10 = 115.744 deg; O7  -- O10 = 3 A
O8  -- T3  -- O9  = 109.085 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 106.617 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.117 deg; O9  -- O10 = 3 A
       106.554 deg <-- 109.437 deg --> 115.744 deg

O10 -- T4  -- O11 = 106.956 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 109.057 deg; O10 -- O12 = 3 A
O10 -- T4  -- O13 = 115.182 deg; O10 -- O13 = 3 A
O11 -- T4  -- O12 = 108.992 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 108.159 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 108.358 deg; O12 -- O13 = 3 A
       106.956 deg <-- 109.451 deg --> 115.182 deg

O13 -- T5  -- O14 = 108.825 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 109.496 deg; O13 -- O15 = 3 A
O13 -- T5  -- O16 = 110.239 deg; O13 -- O16 = 3 A
O14 -- T5  -- O15 = 108.927 deg; O14 -- O15 = 3 A
O14 -- T5  -- O16 = 108.420 deg; O14 -- O16 = 3 A
O15 -- T5  -- O16 = 110.888 deg; O15 -- O16 = 3 A
       108.420 deg <-- 109.466 deg --> 110.888 deg

        O-T-O SUMMARY
          Range  = 106.5538 deg <--> 115.7440 deg
          Mean   = 109.4984 deg
          StdDev = 2.5651 deg

        O--O SUMMARY
          Range  = 2.5998 A <--> 2.7744 A
          Mean   = 2.6606 A
          StdDev = 0.0509 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  88.455 deg; T1  -- T1  = 4.1616 A
T1  - O1  - T1  - O3  - T2  = 175.598 deg; T1  -- T2  = 5.4517 A
T1  - O1  - T1  - O4  - T1  =  91.545 deg; T1  -- T1  = 4.1616 A
T1  - O2  - T1  - O3  - T2  =  88.334 deg; T1  -- T2  = 4.2026 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.4909 A
T2  - O3  - T1  - O4  - T1  =  91.465 deg; T2  -- T1  = 4.2072 A

T1  - O4  - T2  - O5  - T2  =  88.535 deg; T1  -- T2  = 4.2072 A
T1  - O4  - T2  - O6  - T3  = 175.413 deg; T1  -- T3  = 5.5184 A
T1  - O4  - T2  - O7  - T2  =  91.666 deg; T1  -- T2  = 4.2026 A
T2  - O5  - T2  - O6  - T3  =  88.317 deg; T2  -- T3  = 4.1960 A
T2  - O5  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.4773 A
T3  - O6  - T2  - O7  - T2  =  91.669 deg; T3  -- T2  = 4.1994 A

T2  - O7  - T3  - O8  - T3  =  88.331 deg; T2  -- T3  = 4.1994 A
T2  - O7  - T3  - O9  - T4  = 174.633 deg; T2  -- T4  = 5.5290 A
T2  - O7  - T3  - O10 - T3  =  91.683 deg; T2  -- T3  = 4.1960 A
T3  - O8  - T3  - O9  - T4  =  87.377 deg; T3  -- T4  = 4.1745 A
T3  - O8  - T3  - O10 - T3  =  90.000 deg; T3  -- T3  = 4.4766 A
T4  - O9  - T3  - O10 - T3  =  91.539 deg; T4  -- T3  = 4.2025 A

T3  - O10 - T4  - O11 - T4  =  88.461 deg; T3  -- T4  = 4.2025 A
T3  - O10 - T4  - O12 - T5  = 175.068 deg; T3  -- T5  = 5.6095 A
T3  - O10 - T4  - O13 - T4  =  92.623 deg; T3  -- T4  = 4.1745 A
T4  - O11 - T4  - O12 - T5  =  89.451 deg; T4  -- T5  = 4.2799 A
T4  - O11 - T4  - O13 - T4  =  90.000 deg; T4  -- T4  = 4.4040 A
T5  - O12 - T4  - O13 - T4  =  91.845 deg; T5  -- T4  = 4.1909 A

T4  - O13 - T5  - O14 - T5  =  90.549 deg; T4  -- T5  = 4.2799 A
T4  - O13 - T5  - O15 - T5  = 134.421 deg; T4  -- T5  = 5.4122 A
T4  - O13 - T5  - O16 - T5  =  88.155 deg; T4  -- T5  = 4.1909 A
T5  - O14 - T5  - O15 - T5  = 135.000 deg; T5  -- T5  = 5.7351 A
T5  - O14 - T5  - O16 - T5  =  90.000 deg; T5  -- T5  = 4.4915 A
T5  - O15 - T5  - O16 - T5  =  90.000 deg; T5  -- T5  = 4.3904 A

        T-T-T SUMMARY
          Range  = 87.3771 deg <--> 175.5976 deg
          Mean   = 104.4654 deg
          StdDev = 30.0729 deg

        T--T SUMMARY
          Range  = 4.1616 A <--> 5.7351 A
          Mean   = 4.5127 A
          StdDev = 0.5158 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 111.273 deg ; T1  -- T1   2.6918 A

T1  -- O2  -- T1  = 149.293 deg ; T1  -- T1   3.1021 A

T1  -- O3  -- T1  = 172.045 deg ; T1  -- T1   3.2473 A

T1  -- O4  -- T2  = 115.577 deg ; T1  -- T2   2.7639 A

T2  -- O5  -- T2  = 148.030 deg ; T2  -- T2   3.0865 A

T2  -- O6  -- T2  = 173.634 deg ; T2  -- T2   3.2434 A

T2  -- O7  -- T3  = 114.620 deg ; T2  -- T3   2.7590 A

T3  -- O8  -- T3  = 147.382 deg ; T3  -- T3   3.0814 A

T3  -- O9  -- T3  = 174.424 deg ; T3  -- T3   3.2473 A

T3  -- O10 -- T4  = 115.735 deg ; T3  -- T4   2.7761 A

T4  -- O11 -- T4  = 136.105 deg ; T4  -- T4   2.9932 A

T4  -- O12 -- T4  = 172.161 deg ; T4  -- T4   3.2304 A

T4  -- O13 -- T5  = 118.822 deg ; T4  -- T5   2.8386 A

T5  -- O14 -- T5  = 163.506 deg ; T5  -- T5   3.1760 A

T5  -- O15 -- T5  = 150.331 deg ; T5  -- T5   3.1760 A

T5  -- O16 -- T5  = 135.626 deg ; T5  -- T5   3.0313 A


        T-O-T SUMMARY
          Range  = 111.2732° <--> 174.4236 deg
          Mean   = 143.6603 deg
          StdDev = 22.5975 deg

        T--T SUMMARY
          Range  = 2.6918 A <--> 3.2473 A
          Mean   = 3.0278 A
          StdDev = 0.1929 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.6918 Angstrom
T1  -- T2  = 2.7639 Angstrom
T2  -- T1  = 2.7639 Angstrom
T2  -- T3  = 2.7590 Angstrom
T3  -- T2  = 2.7590 Angstrom
T3  -- T4  = 2.7761 Angstrom
T4  -- T3  = 2.7761 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 8 8 8 9 13 19 23 24 24 24 24 24 24 25
TD10 = 124
Circuit symbol = 4.4.4.4.4.6_{2}
Weight = 10
Vertex symbol  = 4.4.4.4.4.*
Weight = 10

T2 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 8 8 9 12 15 17 20 23 24 24 24 24 25 29
TD10 = 124
Circuit symbol = 4.4.4.4.4.6_{2}
Weight = 10
Vertex symbol  = 4.4.4.4.4.*
Weight = 10

T3 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 8 9 12 15 16 16 17 20 23 24 24 25 29 36
TD10 = 125
Circuit symbol = 4.4.4.4.4.6_{2}
Weight = 10
Vertex symbol  = 4.4.4.4.4.*
Weight = 10

T4 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 9 12 15 16 16 16 16 17 20 23 25 29 36 43
TD10 = 129
Circuit symbol = 4.4.4.4.4.6_{2}
Weight = 10
Vertex symbol  = 4.4.4.4.4.*
Weight = 10

T5 (Si): multiplicity = 96
Coordination Sequence =
    1 4 8 12 15 16 16 16 16 16 16 17 21 28 36 43 47
TD10 = 136
Circuit symbol = 4.4.4.6.4.6
Weight = 9
Vertex symbol  = 4.4.4.8.4.*
Weight = 14

<TD10> = 127.600
Average ring size = 4.0816