Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_10081936_yn1wzS.cif"

There are 288 T-atoms per unit cell
There are 576 O-atoms per unit cell

Framework density = 2.42 T-atoms per nm^3
Material density = 0.241 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5878 Angstrom
T1  -- O2  = 1.6480 Angstrom
T1  -- O3  = 1.7447 Angstrom
T1  -- O4  = 1.7477 Angstrom
      mean = 1.6821 Angstrom
        t1 = 0.092560  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.052388  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6619 Angstrom
T2  -- O5  = 1.6526 Angstrom
T2  -- O6  = 1.6938 Angstrom
T2  -- O2  = 1.6619 Angstrom
      mean = 1.6676 Angstrom
        t1 = 0.045702  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.020120  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6311 Angstrom
T3  -- O7  = 1.5508 Angstrom
T3  -- O8  = 1.6566 Angstrom
T3  -- O8  = 1.6566 Angstrom
      mean = 1.6237 Angstrom
        t1 = 0.070718  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.066280  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O3  = 1.6452 Angstrom
T4  -- O3  = 1.6452 Angstrom
T4  -- O9  = 1.6316 Angstrom
T4  -- O10 = 1.4884 Angstrom
      mean = 1.6026 Angstrom
        t1 = 0.099928  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.075028  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O4  = 1.6452 Angstrom
T5  -- O4  = 1.6452 Angstrom
T5  -- O10 = 1.4843 Angstrom
T5  -- O11 = 1.6334 Angstrom
      mean = 1.6020 Angstrom
        t1 = 0.101474  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.103358  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4843 A <--> 1.7477 A
          Mean   = 1.6433 A
          StdDev = 0.0679 A

       t1 Range  = 0.0457 <-- 0.0821 --> 0.1015
       t2 Range  = 0.0201 <-- 0.0634 --> 0.1034

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  =  90.232 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  = 107.148 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 107.310 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 119.703 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 119.637 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.396 deg; O3  -- O4  = 3 A
       90.232 deg <-- 108.904 deg --> 119.703 deg

O2  -- T2  -- O5  = 106.526 deg; O2  -- O5  = 3 A
O2  -- T2  -- O6  = 106.050 deg; O2  -- O6  = 3 A
O2  -- T2  -- O2  = 117.223 deg; O2  -- O2  = 3 A
O5  -- T2  -- O6  = 114.837 deg; O5  -- O6  = 3 A
O5  -- T2  -- O2  = 106.526 deg; O5  -- O2  = 3 A
O6  -- T2  -- O2  = 106.050 deg; O6  -- O2  = 3 A
       106.050 deg <-- 109.535 deg --> 117.223 deg

O6  -- T3  -- O7  =  98.327 deg; O6  -- O7  = 2 A
O6  -- T3  -- O8  = 118.997 deg; O6  -- O8  = 3 A
O6  -- T3  -- O8  = 118.997 deg; O6  -- O8  = 3 A
O7  -- T3  -- O8  = 100.347 deg; O7  -- O8  = 2 A
O7  -- T3  -- O8  = 100.347 deg; O7  -- O8  = 2 A
O8  -- T3  -- O8  = 113.735 deg; O8  -- O8  = 3 A
       98.327 deg <-- 108.458 deg --> 118.997 deg

O3  -- T4  -- O3  = 127.448 deg; O3  -- O3  = 3 A
O3  -- T4  -- O9  = 113.962 deg; O3  -- O9  = 3 A
O3  -- T4  -- O10 =  92.107 deg; O3  -- O10 = 2 A
O3  -- T4  -- O9  = 113.962 deg; O3  -- O9  = 3 A
O3  -- T4  -- O10 =  92.107 deg; O3  -- O10 = 2 A
O9  -- T4  -- O10 = 108.684 deg; O9  -- O10 = 3 A
       92.107 deg <-- 108.045 deg --> 127.448 deg

O4  -- T5  -- O4  = 127.564 deg; O4  -- O4  = 3 A
O4  -- T5  -- O10 =  91.868 deg; O4  -- O10 = 2 A
O4  -- T5  -- O11 = 113.991 deg; O4  -- O11 = 3 A
O4  -- T5  -- O10 =  91.868 deg; O4  -- O10 = 2 A
O4  -- T5  -- O11 = 113.991 deg; O4  -- O11 = 3 A
O10 -- T5  -- O11 = 108.792 deg; O10 -- O11 = 3 A
       91.868 deg <-- 108.012 deg --> 127.564 deg

        O-T-O SUMMARY
          Range  = 90.2325 deg <--> 127.5644 deg
          Mean   = 108.4785 deg
          StdDev = 10.6270 deg

        O--O SUMMARY
          Range  = 2.2514 A <--> 2.9518 A
          Mean   = 2.6528 A
          StdDev = 0.2298 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T4  = 131.502 deg; T2  -- T4  = 5.1746 A
T2  - O1  - T1  - O3  - T5  = 135.009 deg; T2  -- T5  = 5.2492 A
T2  - O1  - T1  - O4  - T1  =  57.711 deg; T2  -- T1  = 2.9569 A
T4  - O2  - T1  - O3  - T5  =  65.481 deg; T4  -- T5  = 2.9428 A
T4  - O2  - T1  - O4  - T1  =  87.396 deg; T4  -- T1  = 4.0724 A
T5  - O3  - T1  - O4  - T1  =  87.402 deg; T5  -- T1  = 4.0766 A

T1  - O2  - T2  - O5  - T2  = 124.528 deg; T1  -- T2  = 5.5393 A
T1  - O2  - T2  - O6  - T3  = 131.770 deg; T1  -- T3  = 5.4281 A
T1  - O2  - T2  - O2  - T1  =  64.579 deg; T1  -- T1  = 3.1591 A
T2  - O5  - T2  - O6  - T3  =  85.896 deg; T2  -- T3  = 4.2909 A
T2  - O5  - T2  - O2  - T1  = 124.528 deg; T2  -- T1  = 5.5393 A
T3  - O6  - T2  - O2  - T1  = 131.770 deg; T3  -- T1  = 5.4281 A

T2  - O6  - T3  - O7  - T3  =  94.104 deg; T2  -- T3  = 4.2909 A
T2  - O6  - T3  - O8  - T3  = 134.526 deg; T2  -- T3  = 5.2663 A
T2  - O6  - T3  - O8  - T3  = 134.526 deg; T2  -- T3  = 5.2663 A
T3  - O7  - T3  - O8  - T3  =  58.130 deg; T3  -- T3  = 2.7186 A
T3  - O7  - T3  - O8  - T3  =  58.130 deg; T3  -- T3  = 2.7186 A
T3  - O8  - T3  - O8  - T3  =  63.741 deg; T3  -- T3  = 2.8709 A

T1  - O3  - T4  - O3  - T1  = 114.468 deg; T1  -- T1  = 4.5700 A
T1  - O3  - T4  - O9  - T5  =  57.364 deg; T1  -- T5  = 2.7237 A
T1  - O3  - T4  - O10 - T4  =  92.604 deg; T1  -- T4  = 4.0724 A
T1  - O3  - T4  - O9  - T5  =  57.364 deg; T1  -- T5  = 2.7237 A
T1  - O3  - T4  - O10 - T4  =  92.604 deg; T1  -- T4  = 4.0724 A
T5  - O9  - T4  - O10 - T4  =  90.000 deg; T5  -- T4  = 4.1401 A

T1  - O4  - T5  - O4  - T1  = 114.051 deg; T1  -- T1  = 4.5700 A
T1  - O4  - T5  - O10 - T4  =  57.155 deg; T1  -- T4  = 2.7174 A
T1  - O4  - T5  - O11 - T5  =  92.598 deg; T1  -- T5  = 4.0766 A
T1  - O4  - T5  - O10 - T4  =  57.155 deg; T1  -- T4  = 2.7174 A
T1  - O4  - T5  - O11 - T5  =  92.598 deg; T1  -- T5  = 4.0766 A
T4  - O10 - T5  - O11 - T5  =  90.000 deg; T4  -- T5  = 4.1401 A

        T-T-T SUMMARY
          Range  = 57.1545 deg <--> 135.0094 deg
          Mean   = 93.1044 deg
          StdDev = 28.3813 deg

        T--T SUMMARY
          Range  = 2.7174 A <--> 5.5393 A
          Mean   = 4.0682 A
          StdDev = 1.0055 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 168.328 deg ; T1  -- T1   3.1591 A

T1  -- O2  -- T2  = 126.597 deg ; T1  -- T2   2.9569 A

T1  -- O3  -- T4  = 106.528 deg ; T1  -- T4   2.7174 A

T1  -- O4  -- T5  = 106.756 deg ; T1  -- T5   2.7237 A

T2  -- O5  -- T2  = 172.935 deg ; T2  -- T2   3.2989 A

T2  -- O6  -- T3  = 128.132 deg ; T2  -- T3   2.9902 A

T3  -- O7  -- T3  = 135.526 deg ; T3  -- T3   2.8709 A

T3  -- O8  -- T3  = 110.282 deg ; T3  -- T3   2.7186 A

T4  -- O9  -- T4  = 126.368 deg ; T4  -- T4   2.9122 A

T4  -- O10 -- T5  = 163.713 deg ; T4  -- T5   2.9428 A

T5  -- O11 -- T5  = 126.107 deg ; T5  -- T5   2.9122 A


        T-O-T SUMMARY
          Range  = 106.5283° <--> 172.9346 deg
          Mean   = 131.9654 deg
          StdDev = 23.8449 deg

        T--T SUMMARY
          Range  = 2.7174 A <--> 3.2989 A
          Mean   = 2.9173 A
          StdDev = 0.1768 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 2.2931 A
O1  -- O2  = 2.2931 A
O3  -- O10 = 2.2588 A
O4  -- O10 = 2.2514 A
T1  -- T4  = 2.7174 Angstrom
T1  -- T5  = 2.7237 Angstrom
T3  -- T3  = 2.7186 Angstrom
T3  -- T3  = 2.7186 Angstrom
T4  -- T1  = 2.7174 Angstrom
T4  -- T1  = 2.7174 Angstrom
T5  -- T1  = 2.7237 Angstrom
T5  -- T1  = 2.7237 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 5 7 8 11 15 12 16 16 21 26 30 40 30 36 36
TD10 = 116
Circuit symbol = 3.3.4.5.4.5
Weight = 7
Vertex symbol  = 3.3.4.20_{64}.4.20_{64}
Weight = 39

T2 (Si): multiplicity = 48
Coordination Sequence =
    1 4 9 8 7 11 11 13 16 25 26 21 26 28 36 38 56
TD10 = 131
Circuit symbol = *.*.*.*.3.4
Weight = 6
Vertex symbol  = 3.4.20_{128}.*.20_{128}.*
Weight = 42

T3 (Si): multiplicity = 48
Coordination Sequence =
    1 4 5 10 14 7 5 11 21 24 27 32 19 14 28 54 60
TD10 = 129
Circuit symbol = 3.4.3.5.3.5
Weight = 6
Vertex symbol  = 3.4.3.*.3.*
Weight = 6

T4 (Si): multiplicity = 48
Coordination Sequence =
    1 4 5 4 10 12 12 18 12 14 16 28 40 32 40 28 32
TD10 = 108
Circuit symbol = 3.4.3.4.4.4
Weight = 8
Vertex symbol  = 3.4.3.4.4.20_{64}
Weight = 40

T5 (Si): multiplicity = 48
Coordination Sequence =
    1 4 5 4 10 12 12 18 12 14 16 28 40 32 40 28 32
TD10 = 108
Circuit symbol = 3.4.3.4.4.4
Weight = 8
Vertex symbol  = 3.4.3.4.4.20_{64}
Weight = 40

<TD10> = 118.000
Average ring size = 17.0256