Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_10081718_6Q6NL0.cif"

There are 288 T-atoms per unit cell
There are 576 O-atoms per unit cell

Framework density = 2.58 T-atoms per nm^3
Material density = 0.257 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6173 Angstrom
T1  -- O2  = 1.6801 Angstrom
T1  -- O3  = 1.6526 Angstrom
T1  -- O4  = 1.7108 Angstrom
      mean = 1.6652 Angstrom
        t1 = 0.050852  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.033441  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6258 Angstrom
T2  -- O5  = 1.6022 Angstrom
T2  -- O6  = 1.7098 Angstrom
T2  -- O3  = 1.6258 Angstrom
      mean = 1.6409 Angstrom
        t1 = 0.046605  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037394  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6686 Angstrom
T3  -- O7  = 1.5503 Angstrom
T3  -- O8  = 1.6610 Angstrom
T3  -- O8  = 1.6610 Angstrom
      mean = 1.6353 Angstrom
        t1 = 0.075832  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.071587  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O4  = 1.6422 Angstrom
T4  -- O4  = 1.6422 Angstrom
T4  -- O9  = 1.6407 Angstrom
T4  -- O10 = 1.5483 Angstrom
      mean = 1.6183 Angstrom
        t1 = 0.057016  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037684  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.5143 Angstrom
T5  -- O11 = 1.5247 Angstrom
T5  -- O12 = 1.6073 Angstrom
T5  -- O12 = 1.6073 Angstrom
      mean = 1.5634 Angstrom
        t1 = 0.034811  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013448  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5143 A <--> 1.7108 A
          Mean   = 1.6314 A
          StdDev = 0.0536 A

       t1 Range  = 0.0348 <-- 0.0530 --> 0.0758
       t2 Range  = 0.0134 <-- 0.0387 --> 0.0716

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 105.897 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 106.171 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 106.705 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 111.662 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 118.757 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 106.878 deg; O3  -- O4  = 3 A
       105.897 deg <-- 109.345 deg --> 118.757 deg

O3  -- T2  -- O5  = 103.364 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 113.315 deg; O3  -- O6  = 3 A
O3  -- T2  -- O3  = 108.730 deg; O3  -- O3  = 3 A
O5  -- T2  -- O6  = 113.835 deg; O5  -- O6  = 3 A
O5  -- T2  -- O3  = 103.364 deg; O5  -- O3  = 3 A
O6  -- T2  -- O3  = 113.315 deg; O6  -- O3  = 3 A
       103.364 deg <-- 109.321 deg --> 113.835 deg

O6  -- T3  -- O7  = 100.151 deg; O6  -- O7  = 2 A
O6  -- T3  -- O8  = 119.121 deg; O6  -- O8  = 3 A
O6  -- T3  -- O8  = 119.121 deg; O6  -- O8  = 3 A
O7  -- T3  -- O8  =  98.848 deg; O7  -- O8  = 2 A
O7  -- T3  -- O8  =  98.848 deg; O7  -- O8  = 2 A
O8  -- T3  -- O8  = 114.070 deg; O8  -- O8  = 3 A
       98.848 deg <-- 108.360 deg --> 119.121 deg

O4  -- T4  -- O4  = 122.359 deg; O4  -- O4  = 3 A
O4  -- T4  -- O9  = 109.690 deg; O4  -- O9  = 3 A
O4  -- T4  -- O10 = 100.235 deg; O4  -- O10 = 2 A
O4  -- T4  -- O9  = 109.690 deg; O4  -- O9  = 3 A
O4  -- T4  -- O10 = 100.235 deg; O4  -- O10 = 2 A
O9  -- T4  -- O10 = 114.029 deg; O9  -- O10 = 3 A
       100.235 deg <-- 109.373 deg --> 122.359 deg

O10 -- T5  -- O11 = 108.458 deg; O10 -- O11 = 2 A
O10 -- T5  -- O12 = 108.589 deg; O10 -- O12 = 3 A
O10 -- T5  -- O12 = 108.589 deg; O10 -- O12 = 3 A
O11 -- T5  -- O12 = 110.536 deg; O11 -- O12 = 3 A
O11 -- T5  -- O12 = 110.536 deg; O11 -- O12 = 3 A
O12 -- T5  -- O12 = 110.071 deg; O12 -- O12 = 3 A
       108.458 deg <-- 109.463 deg --> 110.536 deg

        O-T-O SUMMARY
          Range  = 98.8479 deg <--> 122.3587 deg
          Mean   = 109.1032 deg
          StdDev = 6.1248 deg

        O--O SUMMARY
          Range  = 2.4402 A <--> 2.9181 A
          Mean   = 2.6546 A
          StdDev = 0.1415 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  91.682 deg; T1  -- T2  = 4.2397 A
T1  - O1  - T1  - O3  - T4  = 131.217 deg; T1  -- T4  = 5.4615 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2634 A
T2  - O2  - T1  - O3  - T4  = 130.244 deg; T2  -- T4  = 5.2916 A
T2  - O2  - T1  - O4  - T1  =  58.590 deg; T2  -- T1  = 2.8718 A
T4  - O3  - T1  - O4  - T1  =  92.760 deg; T4  -- T1  = 4.3105 A

T1  - O3  - T2  - O5  - T2  =  88.318 deg; T1  -- T2  = 4.2397 A
T1  - O3  - T2  - O6  - T3  = 148.263 deg; T1  -- T3  = 5.6518 A
T1  - O3  - T2  - O3  - T1  =  62.821 deg; T1  -- T1  = 2.9934 A
T2  - O5  - T2  - O6  - T3  =  87.178 deg; T2  -- T3  = 4.2829 A
T2  - O5  - T2  - O3  - T1  =  88.318 deg; T2  -- T1  = 4.2397 A
T3  - O6  - T2  - O3  - T1  = 148.263 deg; T3  -- T1  = 5.6518 A

T2  - O6  - T3  - O7  - T3  =  92.822 deg; T2  -- T3  = 4.2829 A
T2  - O6  - T3  - O8  - T3  = 133.212 deg; T2  -- T3  = 5.2685 A
T2  - O6  - T3  - O8  - T3  = 133.212 deg; T2  -- T3  = 5.2685 A
T3  - O7  - T3  - O8  - T3  =  57.883 deg; T3  -- T3  = 2.7355 A
T3  - O7  - T3  - O8  - T3  =  57.883 deg; T3  -- T3  = 2.7355 A
T3  - O8  - T3  - O8  - T3  =  64.234 deg; T3  -- T3  = 2.9086 A

T1  - O4  - T4  - O4  - T1  = 170.731 deg; T1  -- T1  = 5.9024 A
T1  - O4  - T4  - O9  - T5  =  93.582 deg; T1  -- T5  = 4.1871 A
T1  - O4  - T4  - O10 - T4  =  87.240 deg; T1  -- T4  = 4.3105 A
T1  - O4  - T4  - O9  - T5  =  93.582 deg; T1  -- T5  = 4.1871 A
T1  - O4  - T4  - O10 - T4  =  87.240 deg; T1  -- T4  = 4.3105 A
T5  - O9  - T4  - O10 - T4  =  87.220 deg; T5  -- T4  = 4.1953 A

T4  - O10 - T5  - O11 - T5  = 134.933 deg; T4  -- T5  = 5.3489 A
T4  - O10 - T5  - O12 - T5  = 134.933 deg; T4  -- T5  = 5.3489 A
T4  - O10 - T5  - O12 - T5  =  92.780 deg; T4  -- T5  = 4.1953 A
T5  - O11 - T5  - O12 - T5  =  90.000 deg; T5  -- T5  = 4.2551 A
T5  - O11 - T5  - O12 - T5  =  90.000 deg; T5  -- T5  = 4.2551 A
T5  - O12 - T5  - O12 - T5  =  90.000 deg; T5  -- T5  = 4.2551 A

        T-T-T SUMMARY
          Range  = 57.8832 deg <--> 170.7306 deg
          Mean   = 101.7846 deg
          StdDev = 30.2259 deg

        T--T SUMMARY
          Range  = 2.7355 A <--> 5.9024 A
          Mean   = 4.4294 A
          StdDev = 0.8803 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 135.465 deg ; T1  -- T1   2.9934 A

T1  -- O2  -- T1  = 129.232 deg ; T1  -- T1   3.0358 A

T1  -- O3  -- T2  = 122.320 deg ; T1  -- T2   2.8718 A

T1  -- O4  -- T4  = 124.009 deg ; T1  -- T4   2.9609 A

T2  -- O5  -- T2  = 179.552 deg ; T2  -- T2   3.2044 A

T2  -- O6  -- T3  = 125.519 deg ; T2  -- T3   3.0038 A

T3  -- O7  -- T3  = 139.459 deg ; T3  -- T3   2.9086 A

T3  -- O8  -- T3  = 110.858 deg ; T3  -- T3   2.7355 A

T4  -- O9  -- T4  = 175.288 deg ; T4  -- T4   3.2786 A

T4  -- O10 -- T5  = 130.509 deg ; T4  -- T5   2.7814 A

T5  -- O11 -- T5  = 161.280 deg ; T5  -- T5   3.0088 A

T5  -- O12 -- T5  = 138.774 deg ; T5  -- T5   3.0088 A


        T-O-T SUMMARY
          Range  = 110.8582° <--> 179.5521 deg
          Mean   = 136.4556 deg
          StdDev = 18.7571 deg

        T--T SUMMARY
          Range  = 2.7355 A <--> 3.2786 A
          Mean   = 2.9783 A
          StdDev = 0.1316 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T3  -- T3  = 2.7355 Angstrom
T3  -- T3  = 2.7355 Angstrom
T4  -- T5  = 2.7814 Angstrom
T5  -- T4  = 2.7814 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 11 12 14 13 17 21 22 32 28 36 36 42 54 54
TD10 = 154
Circuit symbol = 3.6_{2}.4.4.4.5
Weight = 11
Vertex symbol  = 3.6.4.4.4.*
Weight = 11

T2 (Si): multiplicity = 48
Coordination Sequence =
    1 4 7 8 13 13 17 18 16 21 20 32 32 44 50 44 58
TD10 = 138
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.*.4.*
Weight = 8

T3 (Si): multiplicity = 48
Coordination Sequence =
    1 4 5 8 10 17 19 17 18 14 21 24 40 46 46 54 46
TD10 = 134
Circuit symbol = 3.4.3.5.3.5
Weight = 6
Vertex symbol  = 3.4.3.*.3.*
Weight = 6

T4 (Si): multiplicity = 48
Coordination Sequence =
    1 4 9 11 12 11 14 14 20 28 24 36 32 36 40 48 68
TD10 = 148
Circuit symbol = 4.6.4.6_{2}.4.6_{2}
Weight = 14
Vertex symbol  = 4.6.4.6.4.*
Weight = 14

T5 (Si): multiplicity = 48
Coordination Sequence =
    1 4 8 12 13 12 10 12 16 24 36 36 36 32 32 40 56
TD10 = 148
Circuit symbol = 4.4.4.6_{2}.4.6_{2}
Weight = 15
Vertex symbol  = 4.4.4.6.4.6
Weight = 15

<TD10> = 146.000
Average ring size = 4.0000