Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_10079866_zh3Rl7.cif"

There are 252 T-atoms per unit cell
There are 504 O-atoms per unit cell

Framework density = 1.91 T-atoms per nm^3
Material density = 0.191 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5015 Angstrom
T1  -- O2  = 1.6159 Angstrom
T1  -- O3  = 1.6433 Angstrom
T1  -- O4  = 1.6632 Angstrom
      mean = 1.6060 Angstrom
        t1 = 0.144362  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.125016  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6455 Angstrom
T2  -- O5  = 1.6444 Angstrom
T2  -- O6  = 1.6600 Angstrom
T2  -- O2  = 1.6455 Angstrom
      mean = 1.6489 Angstrom
        t1 = 0.036930  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.026017  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O3  = 1.6561 Angstrom
T3  -- O6  = 1.6991 Angstrom
T3  -- O7  = 1.6154 Angstrom
T3  -- O3  = 1.6561 Angstrom
      mean = 1.6567 Angstrom
        t1 = 0.029830  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007640  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O4  = 1.6594 Angstrom
T4  -- O8  = 1.6220 Angstrom
T4  -- O9  = 1.6457 Angstrom
T4  -- O4  = 1.6594 Angstrom
      mean = 1.6466 Angstrom
        t1 = 0.032251  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.017192  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O9  = 1.6267 Angstrom
T5  -- O9  = 1.6267 Angstrom
T5  -- O9  = 1.6267 Angstrom
T5  -- O9  = 1.6267 Angstrom
      mean = 1.6267 Angstrom
        t1 = 0.011146  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003185  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5015 A <--> 1.6991 A
          Mean   = 1.6325 A
          StdDev = 0.0468 A

       t1 Range  = 0.0111 <-- 0.0509 --> 0.1444
       t2 Range  = 0.0032 <-- 0.0358 --> 0.1250

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  =  89.981 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  =  85.858 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  =  82.030 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 112.833 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 119.896 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 125.648 deg; O3  -- O4  = 3 A
       82.030 deg <-- 102.708 deg --> 125.648 deg

O2  -- T2  -- O5  = 109.081 deg; O2  -- O5  = 3 A
O2  -- T2  -- O6  = 104.251 deg; O2  -- O6  = 3 A
O2  -- T2  -- O2  = 112.571 deg; O2  -- O2  = 3 A
O5  -- T2  -- O6  = 117.590 deg; O5  -- O6  = 3 A
O5  -- T2  -- O2  = 109.081 deg; O5  -- O2  = 3 A
O6  -- T2  -- O2  = 104.251 deg; O6  -- O2  = 3 A
       104.251 deg <-- 109.471 deg --> 117.590 deg

O3  -- T3  -- O6  = 107.823 deg; O3  -- O6  = 3 A
O3  -- T3  -- O7  = 109.931 deg; O3  -- O7  = 3 A
O3  -- T3  -- O3  = 110.616 deg; O3  -- O3  = 3 A
O6  -- T3  -- O7  = 110.675 deg; O6  -- O7  = 3 A
O6  -- T3  -- O3  = 107.823 deg; O6  -- O3  = 3 A
O7  -- T3  -- O3  = 109.931 deg; O7  -- O3  = 3 A
       107.823 deg <-- 109.467 deg --> 110.675 deg

O4  -- T4  -- O8  = 106.948 deg; O4  -- O8  = 3 A
O4  -- T4  -- O9  = 111.114 deg; O4  -- O9  = 3 A
O4  -- T4  -- O4  = 114.066 deg; O4  -- O4  = 3 A
O8  -- T4  -- O9  = 106.157 deg; O8  -- O9  = 3 A
O8  -- T4  -- O4  = 106.948 deg; O8  -- O4  = 3 A
O9  -- T4  -- O4  = 111.114 deg; O9  -- O4  = 3 A
       106.157 deg <-- 109.391 deg --> 114.066 deg

O9  -- T5  -- O9  = 108.533 deg; O9  -- O9  = 3 A
O9  -- T5  -- O9  = 109.942 deg; O9  -- O9  = 3 A
O9  -- T5  -- O9  = 109.942 deg; O9  -- O9  = 3 A
O9  -- T5  -- O9  = 109.942 deg; O9  -- O9  = 3 A
O9  -- T5  -- O9  = 109.942 deg; O9  -- O9  = 3 A
O9  -- T5  -- O9  = 108.533 deg; O9  -- O9  = 3 A
       108.533 deg <-- 109.473 deg --> 109.942 deg

        O-T-O SUMMARY
          Range  = 82.0305 deg <--> 125.6480 deg
          Mean   = 107.7421 deg
          StdDev = 9.1781 deg

        O--O SUMMARY
          Range  = 2.0804 A <--> 2.9415 A
          Mean   = 2.6394 A
          StdDev = 0.1957 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T3  =  61.916 deg; T2  -- T3  = 2.8229 A
T2  - O1  - T1  - O3  - T4  =  95.420 deg; T2  -- T4  = 4.1280 A
T2  - O1  - T1  - O4  - T1  =  57.168 deg; T2  -- T1  = 2.7582 A
T3  - O2  - T1  - O3  - T4  = 112.573 deg; T3  -- T4  = 4.6177 A
T3  - O2  - T1  - O4  - T1  =  56.772 deg; T3  -- T1  = 2.7291 A
T4  - O3  - T1  - O4  - T1  =  57.996 deg; T4  -- T1  = 2.8218 A

T1  - O2  - T2  - O5  - T2  = 116.150 deg; T1  -- T2  = 4.6017 A
T1  - O2  - T2  - O6  - T3  =  58.535 deg; T1  -- T3  = 2.7291 A
T1  - O2  - T2  - O2  - T1  =  65.665 deg; T1  -- T1  = 2.9909 A
T2  - O5  - T2  - O6  - T3  = 173.230 deg; T2  -- T3  = 5.4766 A
T2  - O5  - T2  - O2  - T1  = 116.150 deg; T2  -- T1  = 4.6017 A
T3  - O6  - T2  - O2  - T1  =  58.535 deg; T3  -- T1  = 2.7291 A

T1  - O3  - T3  - O6  - T2  =  59.549 deg; T1  -- T2  = 2.7582 A
T1  - O3  - T3  - O7  - T3  = 146.760 deg; T1  -- T3  = 5.6088 A
T1  - O3  - T3  - O3  - T1  =  66.456 deg; T1  -- T1  = 2.9909 A
T2  - O6  - T3  - O7  - T3  = 128.230 deg; T2  -- T3  = 5.3510 A
T2  - O6  - T3  - O3  - T1  =  59.549 deg; T2  -- T1  = 2.7582 A
T3  - O7  - T3  - O3  - T1  = 146.760 deg; T3  -- T1  = 5.6088 A

T1  - O4  - T4  - O8  - T4  = 111.795 deg; T1  -- T4  = 4.8209 A
T1  - O4  - T4  - O9  - T5  = 147.758 deg; T1  -- T5  = 5.5827 A
T1  - O4  - T4  - O4  - T1  =  64.007 deg; T1  -- T1  = 2.9909 A
T4  - O8  - T4  - O9  - T5  =  59.891 deg; T4  -- T5  = 2.9892 A
T4  - O8  - T4  - O4  - T1  = 111.795 deg; T4  -- T1  = 4.8209 A
T5  - O9  - T4  - O4  - T1  = 147.758 deg; T5  -- T1  = 5.5827 A

T4  - O9  - T5  - O9  - T4  =  60.218 deg; T4  -- T4  = 2.9991 A
T4  - O9  - T5  - O9  - T4  = 138.448 deg; T4  -- T4  = 5.5897 A
T4  - O9  - T5  - O9  - T4  = 138.448 deg; T4  -- T4  = 5.5897 A
T4  - O9  - T5  - O9  - T4  = 138.448 deg; T4  -- T4  = 5.5897 A
T4  - O9  - T5  - O9  - T4  = 138.448 deg; T4  -- T4  = 5.5897 A
T4  - O9  - T5  - O9  - T4  =  60.218 deg; T4  -- T4  = 2.9991 A

        T-T-T SUMMARY
          Range  = 56.7721 deg <--> 173.2299 deg
          Mean   = 95.5630 deg
          StdDev = 37.0891 deg

        T--T SUMMARY
          Range  = 2.7291 A <--> 5.6088 A
          Mean   = 4.0055 A
          StdDev = 1.1971 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 169.754 deg ; T1  -- T1   2.9909 A

T1  -- O2  -- T2  = 115.497 deg ; T1  -- T2   2.7582 A

T1  -- O3  -- T3  = 111.618 deg ; T1  -- T3   2.7291 A

T1  -- O4  -- T4  = 116.266 deg ; T1  -- T4   2.8218 A

T2  -- O5  -- T2  = 108.154 deg ; T2  -- T2   2.6633 A

T2  -- O6  -- T3  = 114.347 deg ; T2  -- T3   2.8229 A

T3  -- O7  -- T3  = 150.318 deg ; T3  -- T3   3.1231 A

T4  -- O8  -- T4  = 135.189 deg ; T4  -- T4   2.9991 A

T4  -- O9  -- T5  = 131.982 deg ; T4  -- T5   2.9892 A


        T-O-T SUMMARY
          Range  = 108.1537° <--> 169.7541 deg
          Mean   = 128.1738 deg
          StdDev = 21.0610 deg

        T--T SUMMARY
          Range  = 2.6633 A <--> 3.1231 A
          Mean   = 2.8614 A
          StdDev = 0.1353 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 2.2054 A
O1  -- O3  = 2.1444 A
O1  -- O4  = 2.0804 A
O1  -- O2  = 2.2054 A
O1  -- O3  = 2.1444 A
O1  -- O4  = 2.0804 A
T1  -- T2  = 2.7582 Angstrom
T1  -- T3  = 2.7291 Angstrom
T2  -- T1  = 2.7582 Angstrom
T2  -- T2  = 2.6633 Angstrom
T2  -- T1  = 2.7582 Angstrom
T3  -- T1  = 2.7291 Angstrom
T3  -- T1  = 2.7291 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 4 8 7 12 7 18 13 20 18 24 30 17 44 32 53
TD10 = 112
Circuit symbol = 3.3.3.4.3.4
Weight = 5
Vertex symbol  = 3.3.3.6_{2}.3.*
Weight = 9

T2 (Si): multiplicity = 48
Coordination Sequence =
    1 4 5 6 7 11 12 12 18 12 20 20 32 28 31 42 37
TD10 = 108
Circuit symbol = 3.6_{2}.3.6_{2}.3.7_{4}
Weight = 9
Vertex symbol  = 3.6_{2}.3.6_{2}.3.16
Weight = 22

T3 (Si): multiplicity = 48
Coordination Sequence =
    1 4 5 7 8 10 13 13 15 16 22 22 28 34 29 35 46
TD10 = 114
Circuit symbol = 3.16.3.17.3.17
Weight = 18
Vertex symbol  = 3.16.3.*.3.*
Weight = 18

T4 (Si): multiplicity = 48
Coordination Sequence =
    1 4 6 7 8 7 13 12 20 18 22 20 19 32 30 50 42
TD10 = 118
Circuit symbol = 3.3.6_{2}.7_{2}.6_{2}.7_{2}
Weight = 9
Vertex symbol  = 3.3.6_{2}.*.6_{2}.*
Weight = 9

T5 (Si): multiplicity = 12
Coordination Sequence =
    1 4 8 8 4 12 8 20 12 28 20 10 28 24 48 28 68
TD10 = 125
Circuit symbol = *.*.*.*.3.3
Weight = 5
Vertex symbol  = 3.3.*.*.*.*
Weight = 5

<TD10> = 113.381
Average ring size = 4.0000