Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_5_10075254_Gr66eD.cif"

There are 288 T-atoms per unit cell
There are 576 O-atoms per unit cell

Framework density = 1.88 T-atoms per nm^3
Material density = 0.187 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.7213 Angstrom
T1  -- O2  = 1.5545 Angstrom
T1  -- O3  = 1.6845 Angstrom
T1  -- O4  = 1.6182 Angstrom
      mean = 1.6446 Angstrom
        t1 = 0.189420  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.220031  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.5864 Angstrom
T2  -- O5  = 1.6056 Angstrom
T2  -- O6  = 1.4698 Angstrom
T2  -- O2  = 1.5864 Angstrom
      mean = 1.5620 Angstrom
        t1 = 0.051105  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.040038  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O3  = 1.6588 Angstrom
T3  -- O6  = 1.6034 Angstrom
T3  -- O7  = 1.6771 Angstrom
T3  -- O3  = 1.6588 Angstrom
      mean = 1.6495 Angstrom
        t1 = 0.048985  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.038881  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O4  = 1.6112 Angstrom
T4  -- O8  = 1.5832 Angstrom
T4  -- O9  = 1.7113 Angstrom
T4  -- O4  = 1.6112 Angstrom
      mean = 1.6292 Angstrom
        t1 = 0.045614  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.038622  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O9  = 1.6722 Angstrom
T5  -- O10 = 1.5489 Angstrom
T5  -- O11 = 1.6611 Angstrom
T5  -- O11 = 1.6611 Angstrom
      mean = 1.6358 Angstrom
        t1 = 0.077424  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.073106  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4698 A <--> 1.7213 A
          Mean   = 1.6276 A
          StdDev = 0.0608 A

       t1 Range  = 0.0456 <-- 0.0825 --> 0.1894
       t2 Range  = 0.0386 <-- 0.0821 --> 0.2200

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  =  76.111 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  = 141.829 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 107.926 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  =  66.341 deg; O2  -- O3  = 2 A
O2  -- T1  -- O4  = 121.435 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  97.555 deg; O3  -- O4  = 2 A
       66.341 deg <-- 101.866 deg --> 141.829 deg

O2  -- T2  -- O5  = 114.294 deg; O2  -- O5  = 3 A
O2  -- T2  -- O6  = 105.031 deg; O2  -- O6  = 2 A
O2  -- T2  -- O2  = 103.980 deg; O2  -- O2  = 2 A
O5  -- T2  -- O6  = 113.171 deg; O5  -- O6  = 3 A
O5  -- T2  -- O2  = 114.294 deg; O5  -- O2  = 3 A
O6  -- T2  -- O2  = 105.031 deg; O6  -- O2  = 2 A
       103.980 deg <-- 109.300 deg --> 114.294 deg

O3  -- T3  -- O6  = 103.885 deg; O3  -- O6  = 3 A
O3  -- T3  -- O7  = 114.399 deg; O3  -- O7  = 3 A
O3  -- T3  -- O3  = 114.898 deg; O3  -- O3  = 3 A
O6  -- T3  -- O7  = 103.360 deg; O6  -- O7  = 3 A
O6  -- T3  -- O3  = 103.885 deg; O6  -- O3  = 3 A
O7  -- T3  -- O3  = 114.399 deg; O7  -- O3  = 3 A
       103.360 deg <-- 109.138 deg --> 114.898 deg

O4  -- T4  -- O8  = 103.332 deg; O4  -- O8  = 3 A
O4  -- T4  -- O9  = 112.990 deg; O4  -- O9  = 3 A
O4  -- T4  -- O4  = 110.027 deg; O4  -- O4  = 3 A
O8  -- T4  -- O9  = 113.350 deg; O8  -- O9  = 3 A
O8  -- T4  -- O4  = 103.332 deg; O8  -- O4  = 3 A
O9  -- T4  -- O4  = 112.990 deg; O9  -- O4  = 3 A
       103.332 deg <-- 109.337 deg --> 113.350 deg

O9  -- T5  -- O10 =  99.892 deg; O9  -- O10 = 2 A
O9  -- T5  -- O11 = 119.220 deg; O9  -- O11 = 3 A
O9  -- T5  -- O11 = 119.220 deg; O9  -- O11 = 3 A
O10 -- T5  -- O11 =  98.632 deg; O10 -- O11 = 2 A
O10 -- T5  -- O11 =  98.632 deg; O10 -- O11 = 2 A
O11 -- T5  -- O11 = 114.243 deg; O11 -- O11 = 3 A
       98.632 deg <-- 108.306 deg --> 119.220 deg

        O-T-O SUMMARY
          Range  = 66.3414 deg <--> 141.8295 deg
          Mean   = 107.3658 deg
          StdDev = 13.8003 deg

        O--O SUMMARY
          Range  = 1.7755 A <--> 3.2187 A
          Mean   = 2.6004 A
          StdDev = 0.2712 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T3  =  43.255 deg; T2  -- T3  = 2.2916 A
T2  - O1  - T1  - O3  - T4  =  95.079 deg; T2  -- T4  = 4.5302 A
T2  - O1  - T1  - O4  - T1  =  81.691 deg; T2  -- T1  = 4.2285 A
T3  - O2  - T1  - O3  - T4  =  87.640 deg; T3  -- T4  = 4.2965 A
T3  - O2  - T1  - O4  - T1  = 123.970 deg; T3  -- T1  = 5.7571 A
T4  - O3  - T1  - O4  - T1  =  87.997 deg; T4  -- T1  = 4.4828 A

T1  - O2  - T2  - O5  - T2  =  98.309 deg; T1  -- T2  = 4.2285 A
T1  - O2  - T2  - O6  - T3  =  69.864 deg; T1  -- T3  = 3.1398 A
T1  - O2  - T2  - O2  - T1  =  83.812 deg; T1  -- T1  = 4.1085 A
T2  - O5  - T2  - O6  - T3  = 163.644 deg; T2  -- T3  = 4.7342 A
T2  - O5  - T2  - O2  - T1  =  98.309 deg; T2  -- T1  = 4.2285 A
T3  - O6  - T2  - O2  - T1  =  69.864 deg; T3  -- T1  = 3.1398 A

T1  - O3  - T3  - O6  - T2  =  66.882 deg; T1  -- T2  = 3.0756 A
T1  - O3  - T3  - O7  - T3  = 139.066 deg; T1  -- T3  = 5.8053 A
T1  - O3  - T3  - O3  - T1  =  81.728 deg; T1  -- T1  = 4.1085 A
T2  - O6  - T3  - O7  - T3  = 118.644 deg; T2  -- T3  = 4.6162 A
T2  - O6  - T3  - O3  - T1  =  66.882 deg; T2  -- T1  = 3.0756 A
T3  - O7  - T3  - O3  - T1  = 139.066 deg; T3  -- T1  = 5.8053 A

T1  - O4  - T4  - O8  - T4  =  92.003 deg; T1  -- T4  = 4.4828 A
T1  - O4  - T4  - O9  - T5  = 137.915 deg; T1  -- T5  = 5.6725 A
T1  - O4  - T4  - O4  - T1  =  84.169 deg; T1  -- T1  = 4.1085 A
T4  - O8  - T4  - O9  - T5  =  87.586 deg; T4  -- T5  = 4.2775 A
T4  - O8  - T4  - O4  - T1  =  92.003 deg; T4  -- T1  = 4.4828 A
T5  - O9  - T4  - O4  - T1  = 137.915 deg; T5  -- T1  = 5.6725 A

T4  - O9  - T5  - O10 - T5  =  92.414 deg; T4  -- T5  = 4.2775 A
T4  - O9  - T5  - O11 - T5  = 132.831 deg; T4  -- T5  = 5.2685 A
T4  - O9  - T5  - O11 - T5  = 132.831 deg; T4  -- T5  = 5.2685 A
T5  - O10 - T5  - O11 - T5  =  57.828 deg; T5  -- T5  = 2.7346 A
T5  - O10 - T5  - O11 - T5  =  57.828 deg; T5  -- T5  = 2.7346 A
T5  - O11 - T5  - O11 - T5  =  64.345 deg; T5  -- T5  = 2.9121 A

        T-T-T SUMMARY
          Range  = 43.2547 deg <--> 163.6445 deg
          Mean   = 95.3487 deg
          StdDev = 28.4379 deg

        T--T SUMMARY
          Range  = 2.2916 A <--> 5.8053 A
          Mean   = 4.2797 A
          StdDev = 0.9886 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 158.133 deg ; T1  -- T1   3.3802 A

T1  -- O2  -- T2  = 156.594 deg ; T1  -- T2   3.0756 A

T1  -- O3  -- T3  = 139.802 deg ; T1  -- T3   3.1398 A

T1  -- O4  -- T4  = 143.279 deg ; T1  -- T4   3.0650 A

T2  -- O5  -- T2  = 101.749 deg ; T2  -- T2   2.4912 A

T2  -- O6  -- T3  =  96.336 deg ; T2  -- T3   2.2916 A

T3  -- O7  -- T3  = 131.360 deg ; T3  -- T3   3.0566 A

T4  -- O8  -- T4  = 178.062 deg ; T4  -- T4   3.1660 A

T4  -- O9  -- T5  = 125.856 deg ; T4  -- T5   3.0128 A

T5  -- O10 -- T5  = 140.135 deg ; T5  -- T5   2.9121 A

T5  -- O11 -- T5  = 110.798 deg ; T5  -- T5   2.7346 A


        T-O-T SUMMARY
          Range  = 96.3362° <--> 178.0619 deg
          Mean   = 138.6609 deg
          StdDev = 21.8460 deg

        T--T SUMMARY
          Range  = 2.2916 A <--> 3.3802 A
          Mean   = 2.9991 A
          StdDev = 0.2851 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 2.0236 A
O1  -- O2  = 2.0236 A
O2  -- O3  = 1.7755 A
T2  -- T2  = 2.4912 Angstrom
T2  -- T3  = 2.2916 Angstrom
T3  -- T2  = 2.2916 Angstrom
T5  -- T5  = 2.7346 Angstrom
T5  -- T5  = 2.7346 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 6 8 9 11 11 11 16 18 15 18 28 28 26 30 42
TD10 = 110
Circuit symbol = 3.4.4.4.4.5
Weight = 8
Vertex symbol  = 3.4.4.4.4.6_{2}
Weight = 10

T2 (Si): multiplicity = 48
Coordination Sequence =
    1 4 5 6 10 9 11 13 12 16 17 16 26 28 26 34 34
TD10 = 104
Circuit symbol = 3.4.3.4.4_{2}.5_{2}
Weight = 8
Vertex symbol  = 3.4.3.4.4.16_{27}
Weight = 33

T3 (Si): multiplicity = 48
Coordination Sequence =
    1 4 7 7 7 9 13 15 12 13 20 22 20 26 34 34 30
TD10 = 108
Circuit symbol = 3.16_{27}.3.16_{27}.4_{2}.16_{27}
Weight = 33
Vertex symbol  = 3.16_{27}.3.16_{27}.4.16_{27}
Weight = 33

T4 (Si): multiplicity = 48
Coordination Sequence =
    1 4 7 5 8 11 9 13 17 16 18 19 20 28 24 30 44
TD10 = 109
Circuit symbol = 4.4_{2}.4.6.4.6
Weight = 10
Vertex symbol  = 4.4_{2}.4.*.4.*
Weight = 10

T5 (Si): multiplicity = 48
Coordination Sequence =
    1 4 5 8 7 6 13 15 13 17 20 20 19 16 32 38 32
TD10 = 109
Circuit symbol = 3.4.3.5.3.5
Weight = 6
Vertex symbol  = 3.4.3.*.3.*
Weight = 6

<TD10> = 108.333
Average ring size = 9.3184