Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_229_4_224924_BEAzFX.cif"

There are 216 T-atoms per unit cell
There are 432 O-atoms per unit cell

Framework density = 2.18 T-atoms per nm^3
Material density = 0.217 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6016 Angstrom
T1  -- O2  = 1.6552 Angstrom
T1  -- O3  = 1.6250 Angstrom
T1  -- O4  = 1.6697 Angstrom
      mean = 1.6379 Angstrom
        t1 = 0.030456  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.029907  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6348 Angstrom
T2  -- O5  = 1.6348 Angstrom
T2  -- O6  = 1.6617 Angstrom
T2  -- O6  = 1.6617 Angstrom
      mean = 1.6482 Angstrom
        t1 = 0.037408  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021865  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6373 Angstrom
T3  -- O5  = 1.5960 Angstrom
T3  -- O7  = 1.5817 Angstrom
T3  -- O4  = 1.6373 Angstrom
      mean = 1.6131 Angstrom
        t1 = 0.053404  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037877  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O6  = 1.6498 Angstrom
T4  -- O8  = 1.5226 Angstrom
T4  -- O9  = 1.6679 Angstrom
T4  -- O9  = 1.6679 Angstrom
      mean = 1.6270 Angstrom
        t1 = 0.143124  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.131178  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5226 A <--> 1.6697 A
          Mean   = 1.6311 A
          StdDev = 0.0376 A

       t1 Range  = 0.0305 <-- 0.0661 --> 0.1431
       t2 Range  = 0.0219 <-- 0.0552 --> 0.1312

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.145 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 105.360 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.519 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 115.386 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 107.784 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 111.453 deg; O3  -- O4  = 3 A
       105.360 deg <-- 109.441 deg --> 115.386 deg

O5  -- T2  -- O5  = 115.239 deg; O5  -- O5  = 3 A
O5  -- T2  -- O6  = 106.309 deg; O5  -- O6  = 3 A
O5  -- T2  -- O6  = 106.309 deg; O5  -- O6  = 3 A
O5  -- T2  -- O6  = 106.309 deg; O5  -- O6  = 3 A
O5  -- T2  -- O6  = 106.309 deg; O5  -- O6  = 3 A
O6  -- T2  -- O6  = 116.747 deg; O6  -- O6  = 3 A
       106.309 deg <-- 109.537 deg --> 116.747 deg

O4  -- T3  -- O5  = 120.335 deg; O4  -- O5  = 3 A
O4  -- T3  -- O7  = 104.807 deg; O4  -- O7  = 3 A
O4  -- T3  -- O4  = 104.862 deg; O4  -- O4  = 3 A
O5  -- T3  -- O7  =  99.290 deg; O5  -- O7  = 2 A
O5  -- T3  -- O4  = 120.335 deg; O5  -- O4  = 3 A
O7  -- T3  -- O4  = 104.807 deg; O7  -- O4  = 3 A
       99.290 deg <-- 109.073 deg --> 120.335 deg

O6  -- T4  -- O8  =  75.094 deg; O6  -- O8  = 2 A
O6  -- T4  -- O9  = 122.874 deg; O6  -- O9  = 3 A
O6  -- T4  -- O9  = 122.874 deg; O6  -- O9  = 3 A
O8  -- T4  -- O9  =  93.608 deg; O8  -- O9  = 2 A
O8  -- T4  -- O9  =  93.608 deg; O8  -- O9  = 2 A
O9  -- T4  -- O9  = 113.463 deg; O9  -- O9  = 3 A
       75.094 deg <-- 103.587 deg --> 122.874 deg

        O-T-O SUMMARY
          Range  = 75.0944 deg <--> 122.8740 deg
          Mean   = 108.5541 deg
          StdDev = 9.5811 deg

        O--O SUMMARY
          Range  = 1.9359 A <--> 2.9139 A
          Mean   = 2.6409 A
          StdDev = 0.1896 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.2510 A
T1  - O1  - T1  - O3  - T3  =  87.879 deg; T1  -- T3  = 4.1820 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3053 A
T1  - O2  - T1  - O3  - T3  = 165.709 deg; T1  -- T3  = 5.4212 A
T1  - O2  - T1  - O4  - T1  = 135.000 deg; T1  -- T1  = 5.1119 A
T3  - O3  - T1  - O4  - T1  =  59.159 deg; T3  -- T1  = 2.7392 A

T3  - O5  - T2  - O5  - T3  =  63.672 deg; T3  -- T3  = 3.0603 A
T3  - O5  - T2  - O6  - T4  = 137.023 deg; T3  -- T4  = 5.4216 A
T3  - O5  - T2  - O6  - T4  = 137.023 deg; T3  -- T4  = 5.4216 A
T3  - O5  - T2  - O6  - T4  = 137.023 deg; T3  -- T4  = 5.4216 A
T3  - O5  - T2  - O6  - T4  = 137.023 deg; T3  -- T4  = 5.4216 A
T4  - O6  - T2  - O6  - T4  =  61.100 deg; T4  -- T4  = 2.9742 A

T1  - O4  - T3  - O5  - T2  = 138.442 deg; T1  -- T2  = 5.2735 A
T1  - O4  - T3  - O7  - T3  =  92.121 deg; T1  -- T3  = 4.1820 A
T1  - O4  - T3  - O4  - T1  =  61.681 deg; T1  -- T1  = 2.8085 A
T2  - O5  - T3  - O7  - T3  =  58.164 deg; T2  -- T3  = 2.9009 A
T2  - O5  - T3  - O4  - T1  = 138.442 deg; T2  -- T1  = 5.2735 A
T3  - O7  - T3  - O4  - T1  =  92.121 deg; T3  -- T1  = 4.1820 A

T2  - O6  - T4  - O8  - T4  =  59.450 deg; T2  -- T4  = 2.9257 A
T2  - O6  - T4  - O9  - T4  = 106.970 deg; T2  -- T4  = 4.5877 A
T2  - O6  - T4  - O9  - T4  = 106.970 deg; T2  -- T4  = 4.5877 A
T4  - O8  - T4  - O9  - T4  =  57.681 deg; T4  -- T4  = 2.7816 A
T4  - O8  - T4  - O9  - T4  =  57.681 deg; T4  -- T4  = 2.7816 A
T4  - O9  - T4  - O9  - T4  =  64.638 deg; T4  -- T4  = 2.9742 A

        T-T-T SUMMARY
          Range  = 57.6810 deg <--> 165.7090 deg
          Mean   = 98.1856 deg
          StdDev = 33.6362 deg

        T--T SUMMARY
          Range  = 2.7392 A <--> 5.4216 A
          Mean   = 4.1521 A
          StdDev = 1.0276 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 122.511 deg ; T1  -- T1   2.8085 A

T1  -- O2  -- T1  = 160.590 deg ; T1  -- T1   3.2631 A

T1  -- O3  -- T1  = 113.924 deg ; T1  -- T1   2.7245 A

T1  -- O4  -- T3  = 111.845 deg ; T1  -- T3   2.7392 A

T2  -- O5  -- T3  = 127.757 deg ; T2  -- T3   2.9009 A

T2  -- O6  -- T4  = 124.135 deg ; T2  -- T4   2.9257 A

T3  -- O7  -- T3  = 150.667 deg ; T3  -- T3   3.0603 A

T4  -- O8  -- T4  = 155.207 deg ; T4  -- T4   2.9742 A

T4  -- O9  -- T4  = 112.997 deg ; T4  -- T4   2.7816 A


        T-O-T SUMMARY
          Range  = 111.8448° <--> 160.5900 deg
          Mean   = 129.8848 deg
          StdDev = 18.7246 deg

        T--T SUMMARY
          Range  = 2.7245 A <--> 3.2631 A
          Mean   = 2.9010 A
          StdDev = 0.1841 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O6  -- O8  = 1.9359 A
T1  -- T1  = 2.7245 Angstrom
T1  -- T3  = 2.7392 Angstrom
T3  -- T1  = 2.7392 Angstrom
T3  -- T1  = 2.7392 Angstrom
T4  -- T4  = 2.7816 Angstrom
T4  -- T4  = 2.7816 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 96
Coordination Sequence =
    1 4 7 9 10 8 7 9 11 18 22 24 25 21 21 24 29
TD10 = 106
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.8.4.*
Weight = 13

T2 (Si): multiplicity = 24
Coordination Sequence =
    1 4 6 5 10 10 10 13 10 12 14 14 26 25 30 36 30
TD10 = 95
Circuit symbol = *.*.*.*.3.3
Weight = 5
Vertex symbol  = 3.3.*.*.*.*
Weight = 5

T3 (Si): multiplicity = 48
Coordination Sequence =
    1 4 6 8 9 9 10 8 14 15 16 25 20 26 25 24 37
TD10 = 100
Circuit symbol = 3.3.4.5.4.5
Weight = 7
Vertex symbol  = 3.3.4.*.4.*
Weight = 7

T4 (Si): multiplicity = 48
Coordination Sequence =
    1 4 3 6 8 12 14 12 11 9 10 15 19 30 36 36 36
TD10 = 90
Circuit symbol = 3.3.3.4.3.4
Weight = 5
Vertex symbol  = 3.3.3.*.3.*
Weight = 5

<TD10> = 99.889
Average ring size = 3.6190