Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_227-2_1_2p_gS82iM.cif"

There are 192 T-atoms per unit cell
There are 576 O-atoms per unit cell

Framework density = 13.36 T-atoms per nm^3
Material density = 1.688 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6457 Angstrom
T1  -- O3  = 1.6212 Angstrom
T1  -- O3  = 1.3819 Angstrom
T1  -- O4  = 1.6191 Angstrom
T1  -- O4  = 1.5713 Angstrom
T1  -- O1  = 1.6189 Angstrom
T1  -- O2  = 1.6206 Angstrom
      mean = 1.5827 Angstrom

        T-O SUMMARY
          Range  = 1.3819 A <--> 1.6457 A
          Mean   = 1.5827 A
          StdDev = 0.0845 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O3  =  76.395 deg; O2  -- O3  = 2 A
O2  -- T1  -- O3  = 121.956 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 140.488 deg; O2  -- O4  = 3 A
O2  -- T1  -- O4  = 110.584 deg; O2  -- O4  = 3 A
O2  -- T1  -- O1  = 105.093 deg; O2  -- O1  = 3 A
O2  -- T1  -- O2  =  38.182 deg; O2  -- O2  = 1 A
O3  -- T1  -- O3  = 153.837 deg; O3  -- O3  = 3 A
O3  -- T1  -- O4  = 109.549 deg; O3  -- O4  = 3 A
O3  -- T1  -- O4  =  42.289 deg; O3  -- O4  = 1 A
O3  -- T1  -- O1  = 109.561 deg; O3  -- O1  = 3 A
O3  -- T1  -- O2  = 109.686 deg; O3  -- O2  = 3 A
O3  -- T1  -- O4  =  44.296 deg; O3  -- O4  = 1 A
O3  -- T1  -- O4  = 127.247 deg; O3  -- O4  = 3 A
O3  -- T1  -- O1  =  84.902 deg; O3  -- O1  = 2 A
O3  -- T1  -- O2  =  84.176 deg; O3  -- O2  = 2 A
O4  -- T1  -- O4  =  96.252 deg; O4  -- O4  = 2 A
O4  -- T1  -- O1  = 108.909 deg; O4  -- O1  = 3 A
O4  -- T1  -- O2  = 109.447 deg; O4  -- O2  = 3 A
O4  -- T1  -- O1  =  77.105 deg; O4  -- O1  = 2 A
O4  -- T1  -- O2  = 148.578 deg; O4  -- O2  = 3 A
O1  -- T1  -- O2  = 109.673 deg; O1  -- O2  = 3 A
       38.182 deg <-- 100.391 deg --> 153.837 deg

        O-T-O SUMMARY
          Range  = 38.1816 deg <--> 153.8372 deg
          Mean   = 100.8755 deg
          StdDev = 32.2721 deg

        O--O SUMMARY
          Range  = 1.0686 A <--> 3.0727 A
          Mean   = 2.3482 A
          StdDev = 0.6025 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 100.655 deg ; T1  -- T1   2.4922 A

T1  -- O2  -- T1  =  18.339 deg ; T1  -- T1   0.5211 A

T1  -- O3  -- T1  =  17.789 deg ; T1  -- T1   0.5211 A

T1  -- O4  -- T1  =  18.722 deg ; T1  -- T1   0.5211 A
T1  -- O4  -- T1  = 123.539 deg ; T1  -- T1   2.8110 A
T1  -- O4  -- T1  = 141.974 deg ; T1  -- T1   3.0616 A
T1  -- O4  -- T1  = 104.945 deg ; T1  -- T1   2.4922 A
T1  -- O4  -- T1  = 123.539 deg ; T1  -- T1   2.8110 A
T1  -- O4  -- T1  =  18.722 deg ; T1  -- T1   0.5211 A


        T-O-T SUMMARY
          Range  = 17.7892° <--> 141.9743 deg
          Mean   = 74.2471 deg
          StdDev = 51.1850 deg

        T--T SUMMARY
          Range  = 0.5211 A <--> 3.0616 A
          Mean   = 1.7503 A
          StdDev = 1.1116 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O3  = 2.0330 A
O1  -- O3  = 2.0330 A
O1  -- O4  = 1.9886 A
O2  -- O2  = 1.0686 A
O2  -- O3  = 2.0203 A
O3  -- O3  = 1.5497 A
O3  -- O4  = 1.1525 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has only 5 neighboring T-atoms within 3.50 A, but 7 bridging O-atoms
  T1  -- T1  = 0.5211 Angstrom
  T1  -- T1  = 2.8110 Angstrom
  T1  -- T1  = 2.8110 Angstrom
  T1  -- T1  = 3.0616 Angstrom
  T1  -- T1  = 2.4922 Angstrom