Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_225_5_6188_xNLbNj.cif"

There are 864 T-atoms per unit cell
There are 1728 O-atoms per unit cell

Framework density = 18.00 T-atoms per nm^3
Material density = 1.796 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6278 Angstrom
T1  -- O2  = 1.6009 Angstrom
T1  -- O3  = 1.6103 Angstrom
T1  -- O4  = 1.6580 Angstrom
      mean = 1.6242 Angstrom
        t1 = 0.022249  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.016053  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6036 Angstrom
T2  -- O5  = 1.5128 Angstrom
T2  -- O6  = 1.6142 Angstrom
T2  -- O7  = 1.5670 Angstrom
      mean = 1.5744 Angstrom
        t1 = 0.061274  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.046816  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.5224 Angstrom
T3  -- O8  = 1.7233 Angstrom
T3  -- O9  = 1.6083 Angstrom
T3  -- O10 = 1.8020 Angstrom
      mean = 1.6640 Angstrom
        t1 = 0.096729  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.082851  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.6422 Angstrom
T4  -- O11 = 1.6240 Angstrom
T4  -- O12 = 1.6170 Angstrom
T4  -- O13 = 1.6227 Angstrom
      mean = 1.6265 Angstrom
        t1 = 0.011489  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003330  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6917 Angstrom
T5  -- O14 = 1.6522 Angstrom
T5  -- O15 = 1.6975 Angstrom
T5  -- O10 = 1.6917 Angstrom
      mean = 1.6833 Angstrom
        t1 = 0.053223  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019406  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5128 A <--> 1.8020 A
          Mean   = 1.6291 A
          StdDev = 0.0657 A

       t1 Range  = 0.0115 <-- 0.0490 --> 0.0967
       t2 Range  = 0.0033 <-- 0.0337 --> 0.0829

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.413 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 107.506 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 114.090 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 107.408 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 107.706 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.525 deg; O3  -- O4  = 3 A
       107.408 deg <-- 109.442 deg --> 114.090 deg

O4  -- T2  -- O5  =  98.317 deg; O4  -- O5  = 2 A
O4  -- T2  -- O6  = 112.995 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 119.229 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 112.952 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 100.535 deg; O5  -- O7  = 2 A
O6  -- T2  -- O7  = 111.287 deg; O6  -- O7  = 3 A
       98.317 deg <-- 109.219 deg --> 119.229 deg

O7  -- T3  -- O8  = 101.276 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 102.701 deg; O7  -- O9  = 2 A
O7  -- T3  -- O10 = 100.100 deg; O7  -- O10 = 3 A
O8  -- T3  -- O9  = 109.649 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 128.232 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 110.687 deg; O9  -- O10 = 3 A
       100.100 deg <-- 108.774 deg --> 128.232 deg

O9  -- T4  -- O11 = 110.077 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 = 109.013 deg; O9  -- O12 = 3 A
O9  -- T4  -- O13 = 109.627 deg; O9  -- O13 = 3 A
O11 -- T4  -- O12 = 109.023 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 109.911 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 109.168 deg; O12 -- O13 = 3 A
       109.013 deg <-- 109.470 deg --> 110.077 deg

O10 -- T5  -- O14 = 106.525 deg; O10 -- O14 = 3 A
O10 -- T5  -- O15 = 110.106 deg; O10 -- O15 = 3 A
O10 -- T5  -- O10 = 117.109 deg; O10 -- O10 = 3 A
O14 -- T5  -- O15 = 105.741 deg; O14 -- O15 = 3 A
O14 -- T5  -- O10 = 106.525 deg; O14 -- O10 = 3 A
O15 -- T5  -- O10 = 110.106 deg; O15 -- O10 = 3 A
       105.741 deg <-- 109.352 deg --> 117.109 deg

        O-T-O SUMMARY
          Range  = 98.3168 deg <--> 128.2320 deg
          Mean   = 109.3220 deg
          StdDev = 6.1847 deg

        O--O SUMMARY
          Range  = 2.3584 A <--> 3.1718 A
          Mean   = 2.6685 A
          StdDev = 0.1582 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 120.000 deg; T1  -- T1  = 4.8864 A
T1  - O1  - T1  - O3  - T2  = 145.648 deg; T1  -- T2  = 5.2494 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.3266 A
T1  - O2  - T1  - O3  - T2  =  85.821 deg; T1  -- T2  = 3.6753 A
T1  - O2  - T1  - O4  - T1  = 135.000 deg; T1  -- T1  = 5.5549 A
T2  - O3  - T1  - O4  - T1  =  85.041 deg; T2  -- T1  = 3.9872 A

T1  - O4  - T2  - O5  - T2  =  94.179 deg; T1  -- T2  = 3.6753 A
T1  - O4  - T2  - O6  - T3  = 122.354 deg; T1  -- T3  = 4.5402 A
T1  - O4  - T2  - O7  - T2  =  94.959 deg; T1  -- T2  = 3.9872 A
T2  - O5  - T2  - O6  - T3  =  96.959 deg; T2  -- T3  = 3.7061 A
T2  - O5  - T2  - O7  - T2  = 135.000 deg; T2  -- T2  = 4.7821 A
T3  - O6  - T2  - O7  - T2  = 114.456 deg; T3  -- T2  = 4.4935 A

T2  - O7  - T3  - O8  - T3  =  83.041 deg; T2  -- T3  = 3.7061 A
T2  - O7  - T3  - O9  - T4  = 107.779 deg; T2  -- T4  = 4.3622 A
T2  - O7  - T3  - O10 - T5  =  84.221 deg; T2  -- T5  = 4.0251 A
T3  - O8  - T3  - O9  - T4  =  89.709 deg; T3  -- T4  = 4.1257 A
T3  - O8  - T3  - O10 - T5  = 165.044 deg; T3  -- T5  = 6.3312 A
T4  - O9  - T3  - O10 - T5  = 101.645 deg; T4  -- T5  = 4.8285 A

T3  - O9  - T4  - O11 - T4  = 113.894 deg; T3  -- T4  = 4.7606 A
T3  - O9  - T4  - O12 - T4  =  90.291 deg; T3  -- T4  = 4.1257 A
T3  - O9  - T4  - O13 - T4  = 108.282 deg; T3  -- T4  = 4.8328 A
T4  - O11 - T4  - O12 - T4  = 120.000 deg; T4  -- T4  = 5.0433 A
T4  - O11 - T4  - O13 - T4  =  90.000 deg; T4  -- T4  = 4.2221 A
T4  - O12 - T4  - O13 - T4  = 135.000 deg; T4  -- T4  = 5.6383 A

T3  - O10 - T5  - O14 - T5  = 105.983 deg; T3  -- T5  = 5.3168 A
T3  - O10 - T5  - O15 - T5  = 129.058 deg; T3  -- T5  = 6.0746 A
T3  - O10 - T5  - O10 - T3  =  93.113 deg; T3  -- T3  = 4.9021 A
T5  - O14 - T5  - O15 - T5  =  90.000 deg; T5  -- T5  = 4.6916 A
T5  - O14 - T5  - O10 - T3  = 105.983 deg; T5  -- T3  = 5.3168 A
T5  - O15 - T5  - O10 - T3  = 129.058 deg; T5  -- T3  = 6.0746 A

        T-T-T SUMMARY
          Range  = 83.0413 deg <--> 165.0439 deg
          Mean   = 108.6331 deg
          StdDev = 20.6302 deg

        T--T SUMMARY
          Range  = 3.6753 A <--> 6.3312 A
          Mean   = 4.7190 A
          StdDev = 0.7453 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 167.946 deg ; T1  -- T1   3.2376 A

T1  -- O2  -- T1  = 127.379 deg ; T1  -- T1   2.8701 A

T1  -- O3  -- T1  = 118.793 deg ; T1  -- T1   2.7719 A

T1  -- O4  -- T2  = 107.105 deg ; T1  -- T2   2.6238 A

T2  -- O5  -- T2  = 133.886 deg ; T2  -- T2   2.7840 A

T2  -- O6  -- T2  =  95.493 deg ; T2  -- T2   2.3895 A

T2  -- O7  -- T3  = 111.789 deg ; T2  -- T3   2.5582 A

T3  -- O8  -- T3  = 121.654 deg ; T3  -- T3   3.0094 A

T3  -- O9  -- T4  = 121.596 deg ; T3  -- T4   2.8375 A

T3  -- O10 -- T5  = 150.141 deg ; T3  -- T5   3.3759 A

T4  -- O11 -- T4  = 147.987 deg ; T4  -- T4   3.1220 A

T4  -- O12 -- T4  = 123.026 deg ; T4  -- T4   2.8424 A

T4  -- O13 -- T4  = 133.387 deg ; T4  -- T4   2.9806 A

T5  -- O14 -- T5  = 166.619 deg ; T5  -- T5   3.2818 A

T5  -- O15 -- T5  = 161.900 deg ; T5  -- T5   3.3527 A


        T-O-T SUMMARY
          Range  = 95.4932° <--> 167.9461 deg
          Mean   = 130.3173 deg
          StdDev = 20.2548 deg

        T--T SUMMARY
          Range  = 2.3895 A <--> 3.3759 A
          Mean   = 2.9086 A
          StdDev = 0.2770 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7719 Angstrom
T1  -- T2  = 2.6238 Angstrom
T2  -- T1  = 2.6238 Angstrom
T2  -- T2  = 2.3895 Angstrom
T2  -- T3  = 2.5582 Angstrom
T2  -- T2  = 2.7840 Angstrom
T3  -- T2  = 2.5582 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 192
Coordination Sequence =
    1 4 9 17 27 39 54 73 98 130 172 222 282 343 410 490 573
TD10 = 624
Circuit symbol = 4.4.4.6.6.6
Weight = 11
Vertex symbol  = 4.4.4.6.8.8
Weight = 21

T2 (Si): multiplicity = 192
Coordination Sequence =
    1 4 9 16 26 39 58 82 111 149 192 244 296 357 444 526 597
TD10 = 687
Circuit symbol = 4.4.4.5.6.6
Weight = 10
Vertex symbol  = 4.4.4.5.8.8
Weight = 19

T3 (Si): multiplicity = 192
Coordination Sequence =
    1 4 10 19 33 52 74 105 144 184 232 287 347 426 505 572 660
TD10 = 858
Circuit symbol = 4.5.4.5.6_{2}.7_{2}
Weight = 10
Vertex symbol  = 4.5.4.5.12_{2}.12_{3}
Weight = 44

T4 (Si): multiplicity = 192
Coordination Sequence =
    1 4 10 19 31 49 71 101 139 179 227 277 329 388 457 542 634
TD10 = 831
Circuit symbol = 4.4.5.6.6.7
Weight = 14
Vertex symbol  = 4.4.5.6.6.8
Weight = 19

T5 (Si): multiplicity = 96
Coordination Sequence =
    1 4 11 22 36 58 87 118 158 204 255 320 384 448 529 620 712
TD10 = 954
Circuit symbol = 4.5_{2}.6.8_{2}.6.8_{2}
Weight = 22
Vertex symbol  = 4.5_{2}.6.8.6.8
Weight = 22

<TD10> = 772.667
Average ring size = 5.5878