Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_225_5_20368_tz7SEJ.cif"

There are 448 T-atoms per unit cell
There are 896 O-atoms per unit cell

Framework density = 14.17 T-atoms per nm^3
Material density = 1.414 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6735 Angstrom
T1  -- O2  = 1.7054 Angstrom
T1  -- O3  = 1.6134 Angstrom
T1  -- O4  = 1.6878 Angstrom
      mean = 1.6700 Angstrom
        t1 = 0.064302  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.065858  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.5837 Angstrom
T2  -- O5  = 1.5837 Angstrom
T2  -- O5  = 1.5837 Angstrom
T2  -- O6  = 1.4761 Angstrom
      mean = 1.5568 Angstrom
        t1 = 0.045823  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.029181  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.5095 Angstrom
T3  -- O7  = 1.5733 Angstrom
T3  -- O7  = 1.5733 Angstrom
T3  -- O7  = 1.5733 Angstrom
      mean = 1.5574 Angstrom
        t1 = 0.034669  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007747  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O3  = 1.5999 Angstrom
T4  -- O3  = 1.5999 Angstrom
T4  -- O7  = 1.4447 Angstrom
T4  -- O8  = 1.6240 Angstrom
      mean = 1.5671 Angstrom
        t1 = 0.062417  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.060451  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O4  = 1.6426 Angstrom
T5  -- O4  = 1.6426 Angstrom
T5  -- O9  = 1.6209 Angstrom
T5  -- O10 = 1.5853 Angstrom
      mean = 1.6228 Angstrom
        t1 = 0.027182  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.016417  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4447 A <--> 1.7054 A
          Mean   = 1.6217 A
          StdDev = 0.0646 A

       t1 Range  = 0.0272 <-- 0.0469 --> 0.0643
       t2 Range  = 0.0077 <-- 0.0359 --> 0.0659

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 116.323 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  97.668 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 111.119 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 114.859 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 112.635 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 102.549 deg; O3  -- O4  = 3 A
       97.668 deg <-- 109.192 deg --> 116.323 deg

O5  -- T2  -- O5  = 111.920 deg; O5  -- O5  = 3 A
O5  -- T2  -- O5  = 111.920 deg; O5  -- O5  = 3 A
O5  -- T2  -- O6  = 106.895 deg; O5  -- O6  = 2 A
O5  -- T2  -- O5  = 111.920 deg; O5  -- O5  = 3 A
O5  -- T2  -- O6  = 106.895 deg; O5  -- O6  = 2 A
O5  -- T2  -- O6  = 106.895 deg; O5  -- O6  = 2 A
       106.895 deg <-- 109.408 deg --> 111.920 deg

O6  -- T3  -- O7  = 112.444 deg; O6  -- O7  = 3 A
O6  -- T3  -- O7  = 112.444 deg; O6  -- O7  = 3 A
O6  -- T3  -- O7  = 112.444 deg; O6  -- O7  = 3 A
O7  -- T3  -- O7  = 106.342 deg; O7  -- O7  = 3 A
O7  -- T3  -- O7  = 106.342 deg; O7  -- O7  = 3 A
O7  -- T3  -- O7  = 106.342 deg; O7  -- O7  = 3 A
       106.342 deg <-- 109.393 deg --> 112.444 deg

O3  -- T4  -- O3  = 117.843 deg; O3  -- O3  = 3 A
O3  -- T4  -- O7  = 101.612 deg; O3  -- O7  = 2 A
O3  -- T4  -- O8  = 107.132 deg; O3  -- O8  = 3 A
O3  -- T4  -- O7  = 101.612 deg; O3  -- O7  = 2 A
O3  -- T4  -- O8  = 107.132 deg; O3  -- O8  = 3 A
O7  -- T4  -- O8  = 122.255 deg; O7  -- O8  = 3 A
       101.612 deg <-- 109.598 deg --> 122.255 deg

O4  -- T5  -- O4  = 116.511 deg; O4  -- O4  = 3 A
O4  -- T5  -- O9  = 108.573 deg; O4  -- O9  = 3 A
O4  -- T5  -- O10 = 107.496 deg; O4  -- O10 = 3 A
O4  -- T5  -- O9  = 108.573 deg; O4  -- O9  = 3 A
O4  -- T5  -- O10 = 107.496 deg; O4  -- O10 = 3 A
O9  -- T5  -- O10 = 107.896 deg; O9  -- O10 = 3 A
       107.496 deg <-- 109.424 deg --> 116.511 deg

        O-T-O SUMMARY
          Range  = 97.6677 deg <--> 122.2546 deg
          Mean   = 108.9813 deg
          StdDev = 5.5142 deg

        O--O SUMMARY
          Range  = 2.3616 A <--> 2.8705 A
          Mean   = 2.6148 A
          StdDev = 0.1343 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T4  = 101.944 deg; T1  -- T4  = 4.9898 A
T1  - O1  - T1  - O3  - T5  = 130.911 deg; T1  -- T5  = 5.8867 A
T1  - O1  - T1  - O4  - T1  = 135.000 deg; T1  -- T1  = 5.6894 A
T4  - O2  - T1  - O3  - T5  =  75.518 deg; T4  -- T5  = 3.7431 A
T4  - O2  - T1  - O4  - T1  =  81.670 deg; T4  -- T1  = 3.7946 A
T5  - O3  - T1  - O4  - T1  =  93.729 deg; T5  -- T1  = 4.2734 A

T2  - O5  - T2  - O5  - T3  = 125.264 deg; T2  -- T3  = 5.3210 A
T2  - O5  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.2511 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.2511 A
T3  - O5  - T2  - O5  - T2  = 125.264 deg; T3  -- T2  = 5.3210 A
T3  - O5  - T2  - O6  - T2  = 125.264 deg; T3  -- T2  = 5.3210 A
T2  - O5  - T2  - O6  - T2  =  90.000 deg; T2  -- T2  = 4.2511 A

T2  - O6  - T3  - O7  - T4  =  86.487 deg; T2  -- T4  = 3.8908 A
T2  - O6  - T3  - O7  - T4  =  86.487 deg; T2  -- T4  = 3.8908 A
T2  - O6  - T3  - O7  - T4  =  86.487 deg; T2  -- T4  = 3.8908 A
T4  - O7  - T3  - O7  - T4  = 119.628 deg; T4  -- T4  = 4.6411 A
T4  - O7  - T3  - O7  - T4  = 119.628 deg; T4  -- T4  = 4.6411 A
T4  - O7  - T3  - O7  - T4  = 119.628 deg; T4  -- T4  = 4.6411 A

T1  - O3  - T4  - O3  - T1  = 105.558 deg; T1  -- T1  = 4.8249 A
T1  - O3  - T4  - O7  - T3  = 100.711 deg; T1  -- T3  = 4.4055 A
T1  - O3  - T4  - O8  - T4  =  98.330 deg; T1  -- T4  = 3.7946 A
T1  - O3  - T4  - O7  - T3  = 100.711 deg; T1  -- T3  = 4.4055 A
T1  - O3  - T4  - O8  - T4  =  98.330 deg; T1  -- T4  = 3.7946 A
T3  - O7  - T4  - O8  - T4  = 148.249 deg; T3  -- T4  = 4.4034 A

T1  - O4  - T5  - O4  - T1  = 102.987 deg; T1  -- T1  = 4.8249 A
T1  - O4  - T5  - O9  - T5  = 128.258 deg; T1  -- T5  = 5.5021 A
T1  - O4  - T5  - O10 - T5  =  86.271 deg; T1  -- T5  = 4.2734 A
T1  - O4  - T5  - O9  - T5  = 128.258 deg; T1  -- T5  = 5.5021 A
T1  - O4  - T5  - O10 - T5  =  86.271 deg; T1  -- T5  = 4.2734 A
T5  - O9  - T5  - O10 - T5  =  90.000 deg; T5  -- T5  = 4.3842 A

        T-T-T SUMMARY
          Range  = 75.5182 deg <--> 148.2486 deg
          Mean   = 104.6135 deg
          StdDev = 18.7977 deg

        T--T SUMMARY
          Range  = 3.7431 A <--> 5.8867 A
          Mean   = 4.5666 A
          StdDev = 0.6575 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 111.441 deg ; T1  -- T1   2.7657 A

T1  -- O2  -- T1  = 166.520 deg ; T1  -- T1   3.3871 A

T1  -- O3  -- T4  = 141.058 deg ; T1  -- T4   3.0295 A

T1  -- O4  -- T5  = 135.538 deg ; T1  -- T5   3.0829 A

T2  -- O5  -- T2  = 143.262 deg ; T2  -- T2   3.0060 A

T2  -- O6  -- T3  = 180.000 deg ; T2  -- T3   2.9856 A

T3  -- O7  -- T4  = 125.575 deg ; T3  -- T4   2.6846 A

T4  -- O8  -- T4  =  71.075 deg ; T4  -- T4   1.8878 A

T5  -- O9  -- T5  = 138.549 deg ; T5  -- T5   3.0321 A

T5  -- O10 -- T5  = 174.341 deg ; T5  -- T5   3.1666 A


        T-O-T SUMMARY
          Range  = 71.0753° <--> 180.0000 deg
          Mean   = 136.2954 deg
          StdDev = 27.5169 deg

        T--T SUMMARY
          Range  = 1.8878 A <--> 3.3871 A
          Mean   = 2.9446 A
          StdDev = 0.3720 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O3  = 1.3319 A
O5  -- O8  = 2.0299 A
T1  -- T1  = 2.7657 Angstrom
T3  -- T4  = 2.6846 Angstrom
T3  -- T4  = 2.6846 Angstrom
T3  -- T4  = 2.6846 Angstrom
T4  -- T3  = 2.6846 Angstrom
T4  -- T4  = 1.8878 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 192
Coordination Sequence =
    1 4 9 16 26 38 56 81 104 127 160 200 242 287 324 369 429
TD10 = 622
Circuit symbol = 4.5.4.7.4.7
Weight = 10
Vertex symbol  = 4.5.4.8.4.9
Weight = 20

T2 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 19 31 33 30 39 69 123 183 219 237 261 282 300 339
TD10 = 541
Circuit symbol = 4.6.4.6.4.6
Weight = 17
Vertex symbol  = 4.6.4.6.4.6
Weight = 17

T3 (Si): multiplicity = 32
Coordination Sequence =
    1 4 12 15 22 37 42 57 84 126 168 210 234 261 294 312 381
TD10 = 568
Circuit symbol = 5.6.5.6.5.6
Weight = 20
Vertex symbol  = 5.6.5.6.5.6
Weight = 20

T4 (Si): multiplicity = 96
Coordination Sequence =
    1 4 9 17 24 31 48 71 96 129 167 201 235 268 302 339 390
TD10 = 597
Circuit symbol = 4.5.4.5.4.6
Weight = 15
Vertex symbol  = 4.5.4.5.4.6
Weight = 15

T5 (Si): multiplicity = 96
Coordination Sequence =
    1 4 8 15 28 45 60 77 100 135 178 209 237 281 342 395 434
TD10 = 651
Circuit symbol = 4.4.4.6.4.6
Weight = 9
Vertex symbol  = 4.4.4.12.4.12
Weight = 27

<TD10> = 613.214
Average ring size = 4.9655