Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_225_5_1992p_JlCDxi.cif"

There are 960 T-atoms per unit cell
There are 1920 O-atoms per unit cell

Framework density = 18.48 T-atoms per nm^3
Material density = 1.844 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6637 Angstrom
T1  -- O2  = 1.6687 Angstrom
T1  -- O3  = 1.6683 Angstrom
T1  -- O4  = 1.6555 Angstrom
      mean = 1.6640 Angstrom
        t1 = 0.036026  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.012367  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6444 Angstrom
T2  -- O5  = 1.5455 Angstrom
T2  -- O6  = 1.5618 Angstrom
T2  -- O7  = 1.6608 Angstrom
      mean = 1.6031 Angstrom
        t1 = 0.064325  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.040749  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.6069 Angstrom
T3  -- O8  = 1.6866 Angstrom
T3  -- O9  = 1.6538 Angstrom
T3  -- O10 = 1.6045 Angstrom
      mean = 1.6380 Angstrom
        t1 = 0.070549  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.043569  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O10 = 1.5811 Angstrom
T4  -- O11 = 1.6417 Angstrom
T4  -- O12 = 1.6279 Angstrom
T4  -- O13 = 1.5943 Angstrom
      mean = 1.6113 Angstrom
        t1 = 0.063087  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.044775  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O13 = 1.6164 Angstrom
T5  -- O14 = 1.5967 Angstrom
T5  -- O15 = 1.6151 Angstrom
T5  -- O16 = 1.6300 Angstrom
      mean = 1.6146 Angstrom
        t1 = 0.027902  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.027864  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5455 A <--> 1.6866 A
          Mean   = 1.6262 A
          StdDev = 0.0372 A

       t1 Range  = 0.0279 <-- 0.0524 --> 0.0705
       t2 Range  = 0.0124 <-- 0.0339 --> 0.0448

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.586 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 111.656 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 106.712 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.868 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 112.164 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 107.847 deg; O3  -- O4  = 3 A
       106.712 deg <-- 109.472 deg --> 112.164 deg

O4  -- T2  -- O5  = 104.804 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 108.048 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 125.969 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 100.540 deg; O5  -- O6  = 2 A
O5  -- T2  -- O7  = 106.925 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 107.667 deg; O6  -- O7  = 3 A
       100.540 deg <-- 108.992 deg --> 125.969 deg

O7  -- T3  -- O8  = 117.814 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 108.290 deg; O7  -- O9  = 3 A
O7  -- T3  -- O10 =  90.236 deg; O7  -- O10 = 2 A
O8  -- T3  -- O9  = 113.424 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 111.827 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 113.231 deg; O9  -- O10 = 3 A
       90.236 deg <-- 109.137 deg --> 117.814 deg

O10 -- T4  -- O11 = 118.779 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 114.601 deg; O10 -- O12 = 3 A
O10 -- T4  -- O13 =  91.282 deg; O10 -- O13 = 2 A
O11 -- T4  -- O12 = 112.404 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 110.261 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 106.735 deg; O12 -- O13 = 3 A
       91.282 deg <-- 109.010 deg --> 118.779 deg

O13 -- T5  -- O14 = 107.853 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 103.851 deg; O13 -- O15 = 3 A
O13 -- T5  -- O16 = 117.974 deg; O13 -- O16 = 3 A
O14 -- T5  -- O15 = 108.729 deg; O14 -- O15 = 3 A
O14 -- T5  -- O16 = 109.067 deg; O14 -- O16 = 3 A
O15 -- T5  -- O16 = 108.994 deg; O15 -- O16 = 3 A
       103.851 deg <-- 109.411 deg --> 117.974 deg

        O-T-O SUMMARY
          Range  = 90.2362 deg <--> 125.9689 deg
          Mean   = 109.1962 deg
          StdDev = 7.3989 deg

        O--O SUMMARY
          Range  = 2.2703 A <--> 2.9446 A
          Mean   = 2.6446 A
          StdDev = 0.1483 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 120.000 deg; T1  -- T1  = 5.6180 A
T1  - O1  - T1  - O3  - T2  = 141.634 deg; T1  -- T2  = 5.9082 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.5800 A
T1  - O2  - T1  - O3  - T2  =  86.718 deg; T1  -- T2  = 4.2883 A
T1  - O2  - T1  - O4  - T1  = 135.000 deg; T1  -- T1  = 5.9713 A
T2  - O3  - T1  - O4  - T1  =  87.979 deg; T2  -- T1  = 4.3307 A

T1  - O4  - T2  - O5  - T2  =  93.282 deg; T1  -- T2  = 4.2883 A
T1  - O4  - T2  - O6  - T3  = 126.286 deg; T1  -- T3  = 5.2877 A
T1  - O4  - T2  - O7  - T2  =  92.021 deg; T1  -- T2  = 4.3307 A
T2  - O5  - T2  - O6  - T3  =  92.841 deg; T2  -- T3  = 4.2125 A
T2  - O5  - T2  - O7  - T2  = 135.000 deg; T2  -- T2  = 5.4579 A
T3  - O6  - T2  - O7  - T2  = 118.907 deg; T3  -- T2  = 5.1133 A

T2  - O7  - T3  - O8  - T3  = 150.569 deg; T2  -- T3  = 6.0015 A
T2  - O7  - T3  - O9  - T3  =  87.159 deg; T2  -- T3  = 4.2125 A
T2  - O7  - T3  - O10 - T4  =  87.171 deg; T2  -- T4  = 4.0210 A
T3  - O8  - T3  - O9  - T3  = 120.000 deg; T3  -- T3  = 5.5985 A
T3  - O8  - T3  - O10 - T4  =  82.739 deg; T3  -- T4  = 4.1019 A
T3  - O9  - T3  - O10 - T4  = 131.309 deg; T3  -- T4  = 5.5517 A

T3  - O10 - T4  - O11 - T4  = 168.648 deg; T3  -- T4  = 5.6534 A
T3  - O10 - T4  - O12 - T4  =  97.261 deg; T3  -- T4  = 4.1019 A
T3  - O10 - T4  - O13 - T5  =  80.714 deg; T3  -- T5  = 3.8169 A
T4  - O11 - T4  - O12 - T4  =  90.000 deg; T4  -- T4  = 3.7636 A
T4  - O11 - T4  - O13 - T5  =  90.537 deg; T4  -- T5  = 4.0911 A
T4  - O12 - T4  - O13 - T5  =  90.578 deg; T4  -- T5  = 3.9421 A

T4  - O13 - T5  - O14 - T5  =  89.463 deg; T4  -- T5  = 4.0911 A
T4  - O13 - T5  - O15 - T5  =  89.422 deg; T4  -- T5  = 3.9421 A
T4  - O13 - T5  - O16 - T5  = 135.788 deg; T4  -- T5  = 5.3102 A
T5  - O14 - T5  - O15 - T5  =  90.000 deg; T5  -- T5  = 3.8455 A
T5  - O14 - T5  - O16 - T5  = 120.000 deg; T5  -- T5  = 4.8276 A
T5  - O15 - T5  - O16 - T5  = 120.000 deg; T5  -- T5  = 4.6369 A

        T-T-T SUMMARY
          Range  = 80.7141 deg <--> 168.6475 deg
          Mean   = 107.8600 deg
          StdDev = 24.3334 deg

        T--T SUMMARY
          Range  = 3.7636 A <--> 6.0015 A
          Mean   = 4.6881 A
          StdDev = 0.7281 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 151.734 deg ; T1  -- T1   3.2267 A

T1  -- O2  -- T1  = 153.776 deg ; T1  -- T1   3.2504 A

T1  -- O3  -- T1  = 151.879 deg ; T1  -- T1   3.2367 A

T1  -- O4  -- T2  = 131.146 deg ; T1  -- T2   3.0045 A

T2  -- O5  -- T2  = 154.489 deg ; T2  -- T2   3.0147 A

T2  -- O6  -- T2  = 135.664 deg ; T2  -- T2   2.8926 A

T2  -- O7  -- T3  = 126.832 deg ; T2  -- T3   2.9223 A

T3  -- O8  -- T3  = 153.295 deg ; T3  -- T3   3.2820 A

T3  -- O9  -- T3  = 148.350 deg ; T3  -- T3   3.1823 A

T3  -- O10 -- T4  = 131.979 deg ; T3  -- T4   2.9100 A

T4  -- O11 -- T4  = 115.136 deg ; T4  -- T4   2.7713 A

T4  -- O12 -- T4  = 102.913 deg ; T4  -- T4   2.5465 A

T4  -- O13 -- T5  = 136.646 deg ; T4  -- T5   2.9837 A

T5  -- O14 -- T5  = 124.580 deg ; T5  -- T5   2.8272 A

T5  -- O15 -- T5  = 107.599 deg ; T5  -- T5   2.6066 A

T5  -- O16 -- T5  = 114.838 deg ; T5  -- T5   2.7470 A


        T-O-T SUMMARY
          Range  = 102.9129° <--> 154.4892 deg
          Mean   = 133.8036 deg
          StdDev = 16.9055 deg

        T--T SUMMARY
          Range  = 2.5465 A <--> 3.2820 A
          Mean   = 2.9628 A
          StdDev = 0.2227 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O7  -- O10 = 2.2754 A
O10 -- O13 = 2.2703 A
O13 -- O13 = 1.3930 A
T4  -- T4  = 2.7713 Angstrom
T4  -- T4  = 2.5465 Angstrom
T5  -- T5  = 2.6066 Angstrom
T5  -- T5  = 2.7470 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 192
Coordination Sequence =
    1 4 9 17 30 49 73 102 134 167 204 245 290 340 396 458 522
TD10 = 790
Circuit symbol = 4.4.4.6.6.6
Weight = 11
Vertex symbol  = 4.4.4.6.8.8
Weight = 21

T2 (Si): multiplicity = 192
Coordination Sequence =
    1 4 9 19 34 51 73 98 125 158 194 233 278 332 395 465 538
TD10 = 766
Circuit symbol = 4.4.4.8_{2}.6.6
Weight = 13
Vertex symbol  = 4.4.4.8.8.8
Weight = 23

T3 (Si): multiplicity = 192
Coordination Sequence =
    1 4 10 19 31 48 69 94 122 154 194 241 295 349 398 446 502
TD10 = 746
Circuit symbol = 4.4.6.8_{2}.6.8_{2}
Weight = 23
Vertex symbol  = 4.4.6.8.6.8
Weight = 23

T4 (Si): multiplicity = 192
Coordination Sequence =
    1 4 8 15 26 38 53 74 104 141 179 219 262 310 361 410 462
TD10 = 643
Circuit symbol = 4.4.4.6.4.6_{2}
Weight = 12
Vertex symbol  = 4.4.4.6.4.8
Weight = 17

T5 (Si): multiplicity = 192
Coordination Sequence =
    1 4 9 15 21 28 38 54 78 112 155 203 252 297 340 382 424
TD10 = 515
Circuit symbol = 4.6.4.6.4.6
Weight = 17
Vertex symbol  = 4.6.4.6.4.6
Weight = 17

<TD10> = 692.000
Average ring size = 5.0704