Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_225_5_1992_6doggd.cif"

There are 960 T-atoms per unit cell
There are 1920 O-atoms per unit cell

Framework density = 18.33 T-atoms per nm^3
Material density = 1.829 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6766 Angstrom
T1  -- O2  = 1.6844 Angstrom
T1  -- O3  = 1.6843 Angstrom
T1  -- O4  = 1.7266 Angstrom
      mean = 1.6930 Angstrom
        t1 = 0.053720  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.011695  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.7115 Angstrom
T2  -- O5  = 1.5578 Angstrom
T2  -- O6  = 1.6047 Angstrom
T2  -- O7  = 1.7141 Angstrom
      mean = 1.6470 Angstrom
        t1 = 0.063292  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.036954  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.5959 Angstrom
T3  -- O8  = 1.6998 Angstrom
T3  -- O9  = 1.6850 Angstrom
T3  -- O10 = 1.6540 Angstrom
      mean = 1.6587 Angstrom
        t1 = 0.082439  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.057954  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O10 = 1.5502 Angstrom
T4  -- O11 = 1.6554 Angstrom
T4  -- O12 = 1.6022 Angstrom
T4  -- O13 = 1.5747 Angstrom
      mean = 1.5956 Angstrom
        t1 = 0.057349  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.051533  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O13 = 1.5408 Angstrom
T5  -- O14 = 1.5850 Angstrom
T5  -- O15 = 1.5415 Angstrom
T5  -- O16 = 1.5631 Angstrom
      mean = 1.5576 Angstrom
        t1 = 0.039681  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.015316  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5408 A <--> 1.7266 A
          Mean   = 1.6304 A
          StdDev = 0.0632 A

       t1 Range  = 0.0397 <-- 0.0593 --> 0.0824
       t2 Range  = 0.0117 <-- 0.0347 --> 0.0580

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.613 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 112.465 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.230 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.727 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 112.204 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 105.641 deg; O3  -- O4  = 3 A
       105.641 deg <-- 109.480 deg --> 112.465 deg

O4  -- T2  -- O5  = 105.016 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 107.747 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 123.260 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 106.476 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 104.836 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.354 deg; O6  -- O7  = 3 A
       104.836 deg <-- 109.281 deg --> 123.260 deg

O7  -- T3  -- O8  = 119.046 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 102.505 deg; O7  -- O9  = 3 A
O7  -- T3  -- O10 =  90.112 deg; O7  -- O10 = 2 A
O8  -- T3  -- O9  = 113.781 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.472 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 120.120 deg; O9  -- O10 = 3 A
       90.112 deg <-- 109.173 deg --> 120.120 deg

O10 -- T4  -- O11 = 122.658 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 101.952 deg; O10 -- O12 = 2 A
O10 -- T4  -- O13 =  98.852 deg; O10 -- O13 = 2 A
O11 -- T4  -- O12 = 108.966 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 108.508 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 116.086 deg; O12 -- O13 = 3 A
       98.852 deg <-- 109.504 deg --> 122.658 deg

O13 -- T5  -- O14 = 110.400 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 109.709 deg; O13 -- O15 = 3 A
O13 -- T5  -- O16 = 110.758 deg; O13 -- O16 = 3 A
O14 -- T5  -- O15 = 107.351 deg; O14 -- O15 = 3 A
O14 -- T5  -- O16 = 114.066 deg; O14 -- O16 = 3 A
O15 -- T5  -- O16 = 104.272 deg; O15 -- O16 = 2 A
       104.272 deg <-- 109.426 deg --> 114.066 deg

        O-T-O SUMMARY
          Range  = 90.1124 deg <--> 123.2601 deg
          Mean   = 109.3460 deg
          StdDev = 7.2091 deg

        O--O SUMMARY
          Range  = 2.3007 A <--> 3.0142 A
          Mean   = 2.6574 A
          StdDev = 0.1626 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 120.000 deg; T1  -- T1  = 5.6854 A
T1  - O1  - T1  - O3  - T2  = 143.016 deg; T1  -- T2  = 6.0489 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.6511 A
T1  - O2  - T1  - O3  - T2  =  85.320 deg; T1  -- T2  = 4.2817 A
T1  - O2  - T1  - O4  - T1  = 135.000 deg; T1  -- T1  = 6.0191 A
T2  - O3  - T1  - O4  - T1  =  88.601 deg; T2  -- T1  = 4.4218 A

T1  - O4  - T2  - O5  - T2  =  94.680 deg; T1  -- T2  = 4.2817 A
T1  - O4  - T2  - O6  - T3  = 123.156 deg; T1  -- T3  = 5.2584 A
T1  - O4  - T2  - O7  - T2  =  91.399 deg; T1  -- T2  = 4.4218 A
T2  - O5  - T2  - O6  - T3  =  93.690 deg; T2  -- T3  = 4.1347 A
T2  - O5  - T2  - O7  - T2  = 135.000 deg; T2  -- T2  = 5.4207 A
T3  - O6  - T2  - O7  - T2  = 119.456 deg; T3  -- T2  = 5.2076 A

T2  - O7  - T3  - O8  - T3  = 150.406 deg; T2  -- T3  = 5.9803 A
T2  - O7  - T3  - O9  - T3  =  86.310 deg; T2  -- T3  = 4.1347 A
T2  - O7  - T3  - O10 - T4  =  85.107 deg; T2  -- T4  = 3.9746 A
T3  - O8  - T3  - O9  - T3  = 120.000 deg; T3  -- T3  = 5.5401 A
T3  - O8  - T3  - O10 - T4  =  89.355 deg; T3  -- T4  = 4.3878 A
T3  - O9  - T3  - O10 - T4  = 125.086 deg; T3  -- T4  = 5.4035 A

T3  - O10 - T4  - O11 - T4  = 174.137 deg; T3  -- T4  = 5.5345 A
T3  - O10 - T4  - O12 - T4  =  90.645 deg; T3  -- T4  = 4.3878 A
T3  - O10 - T4  - O13 - T5  =  83.722 deg; T3  -- T5  = 3.8161 A
T4  - O11 - T4  - O12 - T4  =  90.000 deg; T4  -- T4  = 4.1129 A
T4  - O11 - T4  - O13 - T5  =  90.474 deg; T4  -- T5  = 3.7867 A
T4  - O12 - T4  - O13 - T5  =  88.204 deg; T4  -- T5  = 4.1569 A

T4  - O13 - T5  - O14 - T5  =  89.526 deg; T4  -- T5  = 3.7867 A
T4  - O13 - T5  - O15 - T5  =  91.796 deg; T4  -- T5  = 4.1569 A
T4  - O13 - T5  - O16 - T5  = 134.043 deg; T4  -- T5  = 5.0249 A
T5  - O14 - T5  - O15 - T5  =  90.000 deg; T5  -- T5  = 4.0096 A
T5  - O14 - T5  - O16 - T5  = 120.000 deg; T5  -- T5  = 4.6174 A
T5  - O15 - T5  - O16 - T5  = 120.000 deg; T5  -- T5  = 4.9718 A

        T-T-T SUMMARY
          Range  = 83.7220 deg <--> 174.1367 deg
          Mean   = 107.7301 deg
          StdDev = 24.4439 deg

        T--T SUMMARY
          Range  = 3.7867 A <--> 6.0489 A
          Mean   = 4.7025 A
          StdDev = 0.7037 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 153.466 deg ; T1  -- T1   3.2638 A

T1  -- O2  -- T1  = 159.221 deg ; T1  -- T1   3.3136 A

T1  -- O3  -- T1  = 149.654 deg ; T1  -- T1   3.2512 A

T1  -- O4  -- T2  = 126.042 deg ; T1  -- T2   3.0640 A

T2  -- O5  -- T2  = 176.434 deg ; T2  -- T2   3.1142 A

T2  -- O6  -- T2  = 118.022 deg ; T2  -- T2   2.7512 A

T2  -- O7  -- T3  = 123.368 deg ; T2  -- T3   2.9145 A

T3  -- O8  -- T3  = 148.291 deg ; T3  -- T3   3.2703 A

T3  -- O9  -- T3  = 136.161 deg ; T3  -- T3   3.1263 A

T3  -- O10 -- T4  = 135.176 deg ; T3  -- T4   2.9625 A

T4  -- O11 -- T4  = 102.348 deg ; T4  -- T4   2.5793 A

T4  -- O12 -- T4  = 177.544 deg ; T4  -- T4   3.2036 A

T4  -- O13 -- T5  = 124.029 deg ; T4  -- T5   2.7512 A

T5  -- O14 -- T5  = 111.786 deg ; T5  -- T5   2.6248 A

T5  -- O15 -- T5  = 158.951 deg ; T5  -- T5   3.0311 A

T5  -- O16 -- T5  = 119.962 deg ; T5  -- T5   2.7068 A


        T-O-T SUMMARY
          Range  = 102.3485° <--> 177.5437 deg
          Mean   = 138.7783 deg
          StdDev = 21.8664 deg

        T--T SUMMARY
          Range  = 2.5793 A <--> 3.3136 A
          Mean   = 2.9955 A
          StdDev = 0.2393 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T2  -- T2  = 2.7512 Angstrom
T4  -- T4  = 2.5793 Angstrom
T4  -- T5  = 2.7512 Angstrom
T5  -- T4  = 2.7512 Angstrom
T5  -- T5  = 2.6248 Angstrom
T5  -- T5  = 2.7068 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 192
Coordination Sequence =
    1 4 9 17 30 49 73 102 134 167 204 245 290 340 396 458 522
TD10 = 790
Circuit symbol = 4.4.4.6.6.6
Weight = 11
Vertex symbol  = 4.4.4.6.8.8
Weight = 21

T2 (Si): multiplicity = 192
Coordination Sequence =
    1 4 9 19 34 51 73 98 125 158 194 233 278 332 395 465 538
TD10 = 766
Circuit symbol = 4.4.4.8_{2}.6.6
Weight = 13
Vertex symbol  = 4.4.4.8.8.8
Weight = 23

T3 (Si): multiplicity = 192
Coordination Sequence =
    1 4 10 19 31 48 69 94 122 154 194 241 295 349 398 446 502
TD10 = 746
Circuit symbol = 4.4.6.8_{2}.6.8_{2}
Weight = 23
Vertex symbol  = 4.4.6.8.6.8
Weight = 23

T4 (Si): multiplicity = 192
Coordination Sequence =
    1 4 8 15 26 38 53 74 104 141 179 219 262 310 361 410 462
TD10 = 643
Circuit symbol = 4.4.4.6.4.6_{2}
Weight = 12
Vertex symbol  = 4.4.4.6.4.8
Weight = 17

T5 (Si): multiplicity = 192
Coordination Sequence =
    1 4 9 15 21 28 38 54 78 112 155 203 252 297 340 382 424
TD10 = 515
Circuit symbol = 4.6.4.6.4.6
Weight = 17
Vertex symbol  = 4.6.4.6.4.6
Weight = 17

<TD10> = 692.000
Average ring size = 5.0704