Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_225_5_1987p_a08jDV.cif"

There are 960 T-atoms per unit cell
There are 1920 O-atoms per unit cell

Framework density = 21.51 T-atoms per nm^3
Material density = 2.146 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6673 Angstrom
T1  -- O2  = 1.6498 Angstrom
T1  -- O3  = 1.6555 Angstrom
T1  -- O4  = 1.6749 Angstrom
      mean = 1.6619 Angstrom
        t1 = 0.035538  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010427  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6404 Angstrom
T2  -- O5  = 1.4835 Angstrom
T2  -- O6  = 1.5904 Angstrom
T2  -- O7  = 1.6442 Angstrom
      mean = 1.5896 Angstrom
        t1 = 0.074822  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.048950  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.5908 Angstrom
T3  -- O8  = 1.6507 Angstrom
T3  -- O9  = 1.6371 Angstrom
T3  -- O10 = 1.5695 Angstrom
      mean = 1.6120 Angstrom
        t1 = 0.059981  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037987  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O10 = 1.5787 Angstrom
T4  -- O11 = 1.6973 Angstrom
T4  -- O12 = 1.5731 Angstrom
T4  -- O13 = 1.6471 Angstrom
      mean = 1.6241 Angstrom
        t1 = 0.069265  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.060032  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O13 = 1.6826 Angstrom
T5  -- O14 = 1.6204 Angstrom
T5  -- O15 = 1.6592 Angstrom
T5  -- O16 = 1.6742 Angstrom
      mean = 1.6591 Angstrom
        t1 = 0.040402  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018343  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4835 A <--> 1.6973 A
          Mean   = 1.6293 A
          StdDev = 0.0499 A

       t1 Range  = 0.0355 <-- 0.0560 --> 0.0748
       t2 Range  = 0.0104 <-- 0.0351 --> 0.0600

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.052 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.645 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 112.373 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.401 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.795 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 105.555 deg; O3  -- O4  = 3 A
       105.555 deg <-- 109.470 deg --> 112.373 deg

O4  -- T2  -- O5  =  96.993 deg; O4  -- O5  = 2 A
O4  -- T2  -- O6  = 109.698 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 127.175 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 107.453 deg; O5  -- O6  = 2 A
O5  -- T2  -- O7  = 103.520 deg; O5  -- O7  = 2 A
O6  -- T2  -- O7  = 109.482 deg; O6  -- O7  = 3 A
       96.993 deg <-- 109.053 deg --> 127.175 deg

O7  -- T3  -- O8  = 118.753 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 108.753 deg; O7  -- O9  = 3 A
O7  -- T3  -- O10 =  93.481 deg; O7  -- O10 = 2 A
O8  -- T3  -- O9  = 112.471 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 107.730 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 114.445 deg; O9  -- O10 = 3 A
       93.481 deg <-- 109.272 deg --> 118.753 deg

O10 -- T4  -- O11 = 116.809 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 103.110 deg; O10 -- O12 = 2 A
O10 -- T4  -- O13 =  97.821 deg; O10 -- O13 = 2 A
O11 -- T4  -- O12 = 105.537 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 124.153 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 107.425 deg; O12 -- O13 = 3 A
       97.821 deg <-- 109.143 deg --> 124.153 deg

O13 -- T5  -- O14 = 104.635 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 110.098 deg; O13 -- O15 = 3 A
O13 -- T5  -- O16 = 114.385 deg; O13 -- O16 = 3 A
O14 -- T5  -- O15 = 107.136 deg; O14 -- O15 = 3 A
O14 -- T5  -- O16 = 108.492 deg; O14 -- O16 = 3 A
O15 -- T5  -- O16 = 111.601 deg; O15 -- O16 = 3 A
       104.635 deg <-- 109.391 deg --> 114.385 deg

        O-T-O SUMMARY
          Range  = 93.4809 deg <--> 127.1747 deg
          Mean   = 109.3170 deg
          StdDev = 7.4598 deg

        O--O SUMMARY
          Range  = 2.3015 A <--> 2.9551 A
          Mean   = 2.6518 A
          StdDev = 0.1599 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 156.759 deg ; T1  -- T1   3.2663 A

T1  -- O2  -- T1  = 146.838 deg ; T1  -- T1   3.1624 A

T1  -- O3  -- T1  = 137.296 deg ; T1  -- T1   3.0837 A

T1  -- O4  -- T2  = 120.909 deg ; T1  -- T2   2.8842 A

T2  -- O5  -- T2  = 144.954 deg ; T2  -- T2   2.8293 A

T2  -- O6  -- T2  = 101.749 deg ; T2  -- T2   2.4676 A

T2  -- O7  -- T3  = 129.048 deg ; T2  -- T3   2.9205 A

T3  -- O8  -- T3  = 118.036 deg ; T3  -- T3   2.8303 A

T3  -- O9  -- T3  = 125.942 deg ; T3  -- T3   2.9166 A

T3  -- O10 -- T4  = 166.945 deg ; T3  -- T4   3.1278 A

T4  -- O11 -- T4  = 131.291 deg ; T4  -- T4   3.0925 A

T4  -- O12 -- T4  = 142.236 deg ; T4  -- T4   2.9768 A

T4  -- O13 -- T5  = 124.151 deg ; T4  -- T5   2.9421 A

T5  -- O14 -- T5  = 122.359 deg ; T5  -- T5   2.8394 A

T5  -- O15 -- T5  = 146.484 deg ; T5  -- T5   3.1775 A

T5  -- O16 -- T5  = 147.938 deg ; T5  -- T5   3.2181 A


        T-O-T SUMMARY
          Range  = 101.7493° <--> 166.9451 deg
          Mean   = 135.1835 deg
          StdDev = 15.9913 deg

        T--T SUMMARY
          Range  = 2.4676 A <--> 3.2663 A
          Mean   = 2.9834 A
          StdDev = 0.1939 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O13 -- O13 = 2.1411 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 2.8842 Angstrom
  T2  -- T2  = 2.4676 Angstrom
  T2  -- T3  = 2.9205 Angstrom
  T2  -- T4  = 3.4117 Angstrom
  T2  -- T2  = 2.8293 Angstrom
T4  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T2  = 3.4117 Angstrom
  T4  -- T3  = 3.1278 Angstrom
  T4  -- T4  = 2.9768 Angstrom
  T4  -- T5  = 2.9421 Angstrom
  T4  -- T4  = 3.0925 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 192
Coordination Sequence =
    1 4 9 17 30 49 73 102 136 176 225 282 345 410 474 538 603
TD10 = 822
Circuit symbol = 4.4.4.6.6.6
Weight = 11
Vertex symbol  = 4.4.4.6.8.10
Weight = 23

T2 (Si): multiplicity = 192
Coordination Sequence =
    1 4 9 18 31 48 72 100 133 174 218 264 314 372 441 521 607
TD10 = 808
Circuit symbol = 4.4.4.6.6.6
Weight = 11
Vertex symbol  = 4.4.4.6.8.10
Weight = 22

T3 (Si): multiplicity = 192
Coordination Sequence =
    1 4 10 19 32 52 78 108 138 169 207 254 312 377 446 516 587
TD10 = 818
Circuit symbol = 4.4.6.6.6.8_{5}
Weight = 20
Vertex symbol  = 4.4.6.6.6.8_{2}
Weight = 20

T4 (Si): multiplicity = 192
Coordination Sequence =
    1 4 9 18 32 51 76 105 140 182 227 278 334 392 459 538 622
TD10 = 845
Circuit symbol = 4.6.4.6_{2}.4.6_{2}
Weight = 14
Vertex symbol  = 4.6.4.6.4.8
Weight = 19

T5 (Si): multiplicity = 192
Coordination Sequence =
    1 4 10 20 34 53 77 108 147 193 246 302 362 426 493 563 632
TD10 = 893
Circuit symbol = 4.6.4.6.6.6
Weight = 16
Vertex symbol  = 4.6.4.6.6.8
Weight = 21

<TD10> = 837.200
Average ring size = 5.2841