Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_225_5_15903_qnnxn7.cif"

There are 520 T-atoms per unit cell
There are 1040 O-atoms per unit cell

Framework density = 18.79 T-atoms per nm^3
Material density = 1.875 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6071 Angstrom
T1  -- O2  = 1.5890 Angstrom
T1  -- O3  = 1.5773 Angstrom
T1  -- O4  = 1.5311 Angstrom
      mean = 1.5761 Angstrom
        t1 = 0.026561  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.012612  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.5256 Angstrom
T2  -- O5  = 1.6965 Angstrom
T2  -- O6  = 1.7112 Angstrom
T2  -- O7  = 1.7260 Angstrom
      mean = 1.6648 Angstrom
        t1 = 0.080584  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.067647  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O8  = 1.6161 Angstrom
T3  -- O8  = 1.6161 Angstrom
T3  -- O8  = 1.6161 Angstrom
T3  -- O9  = 1.6890 Angstrom
      mean = 1.6344 Angstrom
        t1 = 0.042031  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.035069  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6570 Angstrom
T4  -- O7  = 1.6570 Angstrom
T4  -- O8  = 1.5795 Angstrom
T4  -- O10 = 1.5991 Angstrom
      mean = 1.6231 Angstrom
        t1 = 0.043078  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.026830  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O9  = 1.6309 Angstrom
T5  -- O9  = 1.6309 Angstrom
T5  -- O9  = 1.6309 Angstrom
T5  -- O9  = 1.6309 Angstrom
      mean = 1.6309 Angstrom
        t1 = 0.012979  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000000  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5256 A <--> 1.7260 A
          Mean   = 1.6220 A
          StdDev = 0.0668 A

       t1 Range  = 0.0130 <-- 0.0410 --> 0.0806
       t2 Range  = 0.0000 <-- 0.0284 --> 0.0676

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 111.908 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.617 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.780 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 108.079 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 107.297 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 110.117 deg; O3  -- O4  = 3 A
       107.297 deg <-- 109.466 deg --> 111.908 deg

O4  -- T2  -- O5  = 101.549 deg; O4  -- O5  = 2 A
O4  -- T2  -- O6  = 100.701 deg; O4  -- O6  = 2 A
O4  -- T2  -- O7  = 103.120 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 119.489 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 111.652 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 116.694 deg; O6  -- O7  = 3 A
       100.701 deg <-- 108.868 deg --> 119.489 deg

O8  -- T3  -- O8  = 104.782 deg; O8  -- O8  = 3 A
O8  -- T3  -- O8  = 104.782 deg; O8  -- O8  = 3 A
O8  -- T3  -- O9  = 113.830 deg; O8  -- O9  = 3 A
O8  -- T3  -- O8  = 104.782 deg; O8  -- O8  = 3 A
O8  -- T3  -- O9  = 113.830 deg; O8  -- O9  = 3 A
O8  -- T3  -- O9  = 113.830 deg; O8  -- O9  = 3 A
       104.782 deg <-- 109.306 deg --> 113.830 deg

O7  -- T4  -- O7  = 120.256 deg; O7  -- O7  = 3 A
O7  -- T4  -- O8  = 109.281 deg; O7  -- O8  = 3 A
O7  -- T4  -- O10 = 106.430 deg; O7  -- O10 = 3 A
O7  -- T4  -- O8  = 109.281 deg; O7  -- O8  = 3 A
O7  -- T4  -- O10 = 106.430 deg; O7  -- O10 = 3 A
O8  -- T4  -- O10 = 103.870 deg; O8  -- O10 = 3 A
       103.870 deg <-- 109.258 deg --> 120.256 deg

O9  -- T5  -- O9  = 109.471 deg; O9  -- O9  = 3 A
O9  -- T5  -- O9  = 109.471 deg; O9  -- O9  = 3 A
O9  -- T5  -- O9  = 109.471 deg; O9  -- O9  = 3 A
O9  -- T5  -- O9  = 109.471 deg; O9  -- O9  = 3 A
O9  -- T5  -- O9  = 109.471 deg; O9  -- O9  = 3 A
O9  -- T5  -- O9  = 109.471 deg; O9  -- O9  = 3 A
       109.471 deg <-- 109.471 deg --> 109.471 deg

        O-T-O SUMMARY
          Range  = 100.7011 deg <--> 120.2558 deg
          Mean   = 109.0492 deg
          StdDev = 5.0890 deg

        O--O SUMMARY
          Range  = 2.4950 A <--> 2.9435 A
          Mean   = 2.6455 A
          StdDev = 0.1336 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 120.000 deg; T1  -- T1  = 4.6311 A
T1  - O1  - T1  - O3  - T2  = 124.106 deg; T1  -- T2  = 4.8615 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 3.6550 A
T1  - O2  - T1  - O3  - T2  =  94.023 deg; T1  -- T2  = 4.1212 A
T1  - O2  - T1  - O4  - T1  = 135.000 deg; T1  -- T1  = 4.8968 A
T2  - O3  - T1  - O4  - T1  =  94.966 deg; T2  -- T1  = 4.0262 A

T1  - O4  - T2  - O5  - T2  =  85.977 deg; T1  -- T2  = 4.1212 A
T1  - O4  - T2  - O6  - T4  =  77.042 deg; T1  -- T4  = 3.8809 A
T1  - O4  - T2  - O7  - T2  =  85.034 deg; T1  -- T2  = 4.0262 A
T2  - O5  - T2  - O6  - T4  = 108.930 deg; T2  -- T4  = 5.2582 A
T2  - O5  - T2  - O7  - T2  = 135.000 deg; T2  -- T2  = 5.7342 A
T4  - O6  - T2  - O7  - T2  = 111.728 deg; T4  -- T2  = 5.2804 A

T4  - O8  - T3  - O8  - T4  = 115.476 deg; T4  -- T4  = 5.2961 A
T4  - O8  - T3  - O8  - T4  = 115.476 deg; T4  -- T4  = 5.2961 A
T4  - O8  - T3  - O9  - T5  = 102.463 deg; T4  -- T5  = 5.0315 A
T4  - O8  - T3  - O8  - T4  = 115.476 deg; T4  -- T4  = 5.2961 A
T4  - O8  - T3  - O9  - T5  = 102.463 deg; T4  -- T5  = 5.0315 A
T4  - O8  - T3  - O9  - T5  = 102.463 deg; T4  -- T5  = 5.0315 A

T2  - O7  - T4  - O7  - T2  = 123.915 deg; T2  -- T2  = 5.8526 A
T2  - O7  - T4  - O8  - T3  = 103.237 deg; T2  -- T3  = 5.0551 A
T2  - O7  - T4  - O10 - T4  = 106.844 deg; T2  -- T4  = 5.0708 A
T2  - O7  - T4  - O8  - T3  = 103.237 deg; T2  -- T3  = 5.0551 A
T2  - O7  - T4  - O10 - T4  = 106.844 deg; T2  -- T4  = 5.0708 A
T3  - O8  - T4  - O10 - T4  = 112.801 deg; T3  -- T4  = 5.1029 A

T3  - O9  - T5  - O9  - T3  = 109.471 deg; T3  -- T3  = 5.4214 A
T3  - O9  - T5  - O9  - T3  = 109.471 deg; T3  -- T3  = 5.4214 A
T3  - O9  - T5  - O9  - T3  = 109.471 deg; T3  -- T3  = 5.4214 A
T3  - O9  - T5  - O9  - T3  = 109.471 deg; T3  -- T3  = 5.4214 A
T3  - O9  - T5  - O9  - T3  = 109.471 deg; T3  -- T3  = 5.4214 A
T3  - O9  - T5  - O9  - T3  = 109.471 deg; T3  -- T3  = 5.4214 A

        T-T-T SUMMARY
          Range  = 77.0420 deg <--> 135.0000 deg
          Mean   = 106.4172 deg
          StdDev = 15.4151 deg

        T--T SUMMARY
          Range  = 3.6550 A <--> 5.8526 A
          Mean   = 4.8526 A
          StdDev = 0.6199 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 105.633 deg ; T1  -- T1   2.5607 A

T1  -- O2  -- T1  = 110.299 deg ; T1  -- T1   2.6081 A

T1  -- O3  -- T1  = 120.508 deg ; T1  -- T1   2.7390 A

T1  -- O4  -- T2  = 142.358 deg ; T1  -- T2   2.8932 A

T2  -- O5  -- T2  = 128.939 deg ; T2  -- T2   3.0616 A

T2  -- O6  -- T2  = 133.531 deg ; T2  -- T2   3.1449 A

T2  -- O7  -- T4  = 157.075 deg ; T2  -- T4   3.3156 A

T3  -- O8  -- T4  = 157.000 deg ; T3  -- T4   3.1315 A

T3  -- O9  -- T5  = 180.000 deg ; T3  -- T5   3.3199 A

T4  -- O10 -- T4  = 138.871 deg ; T4  -- T4   2.9943 A


        T-O-T SUMMARY
          Range  = 105.6329° <--> 180.0000 deg
          Mean   = 131.7892 deg
          StdDev = 18.4085 deg

        T--T SUMMARY
          Range  = 2.5607 A <--> 3.3199 A
          Mean   = 2.9313 A
          StdDev = 0.2567 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.6081 Angstrom
T1  -- T1  = 2.7390 Angstrom
T1  -- T1  = 2.5607 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 192
Coordination Sequence =
    1 4 9 16 25 38 55 77 107 141 183 237 291 356 422 484 578
TD10 = 656
Circuit symbol = 4.4.4.6.5.6
Weight = 13
Vertex symbol  = 4.4.4.6.5.8
Weight = 18

T2 (Si): multiplicity = 192
Coordination Sequence =
    1 4 10 20 34 52 76 105 136 177 225 279 345 408 478 565 644
TD10 = 840
Circuit symbol = 4.5.4.6.5.6
Weight = 13
Vertex symbol  = 4.5.4.6.5.8
Weight = 18

T3 (Si): multiplicity = 32
Coordination Sequence =
    1 4 12 24 39 60 84 111 159 195 249 304 355 441 495 580 673
TD10 = 938
Circuit symbol = 5.5.5.5.5.5
Weight = 17
Vertex symbol  = 5.5.5.5.5.5
Weight = 17

T4 (Si): multiplicity = 96
Coordination Sequence =
    1 4 12 23 36 58 82 108 147 194 241 302 356 422 509 569 667
TD10 = 906
Circuit symbol = 5.5.5.8_{3}.5.8_{3}
Weight = 21
Vertex symbol  = 5.5.5.8_{2}.5.8_{2}
Weight = 21

T5 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 24 48 60 84 126 144 228 264 264 388 442 484 592 672
TD10 = 995
Circuit symbol = 5.5.5.5.5.5
Weight = 17
Vertex symbol  = 5.5.5.5.5.5
Weight = 17

<TD10> = 792.662
Average ring size = 5.1750