Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_225_2_11p_Q7BNH6.cif"

There are 40 T-atoms per unit cell
There are 80 O-atoms per unit cell

Framework density = 15.76 T-atoms per nm^3
Material density = 1.572 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6166 Angstrom
T1  -- O1  = 1.6166 Angstrom
T1  -- O1  = 1.6166 Angstrom
T1  -- O2  = 1.6100 Angstrom
      mean = 1.6150 Angstrom
        t1 = 0.005260  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003819  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6098 Angstrom
T2  -- O2  = 1.6098 Angstrom
T2  -- O2  = 1.6098 Angstrom
T2  -- O2  = 1.6098 Angstrom
      mean = 1.6098 Angstrom
        t1 = 0.000149  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000000  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6098 A <--> 1.6166 A
          Mean   = 1.6139 A
          StdDev = 0.0033 A

       t1 Range  = 0.0001 <-- 0.0027 --> 0.0053
       t2 Range  = 0.0000 <-- 0.0019 --> 0.0038

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 109.995 deg; O1  -- O1  = 3 A
O1  -- T1  -- O1  = 109.995 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 108.942 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  = 109.995 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 108.942 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 108.942 deg; O1  -- O2  = 3 A
       108.942 deg <-- 109.469 deg --> 109.995 deg

O2  -- T2  -- O2  = 109.471 deg; O2  -- O2  = 3 A
O2  -- T2  -- O2  = 109.471 deg; O2  -- O2  = 3 A
O2  -- T2  -- O2  = 109.471 deg; O2  -- O2  = 3 A
O2  -- T2  -- O2  = 109.471 deg; O2  -- O2  = 3 A
O2  -- T2  -- O2  = 109.471 deg; O2  -- O2  = 3 A
O2  -- T2  -- O2  = 109.471 deg; O2  -- O2  = 3 A
       109.471 deg <-- 109.471 deg --> 109.471 deg

        O-T-O SUMMARY
          Range  = 108.9422 deg <--> 109.9950 deg
          Mean   = 109.4697 deg
          StdDev = 0.4082 deg

        O--O SUMMARY
          Range  = 2.6259 A <--> 2.6484 A
          Mean   = 2.6338 A
          StdDev = 0.0097 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T2  = 125.264 deg; T1  -- T2  = 5.6152 A
T1  - O1  - T1  - O1  - T1  =  90.000 deg; T1  -- T1  = 4.3882 A
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.3882 A
T2  - O1  - T1  - O1  - T1  = 125.264 deg; T2  -- T1  = 5.6152 A
T2  - O1  - T1  - O2  - T1  = 125.264 deg; T2  -- T1  = 5.6152 A
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.3882 A

T1  - O2  - T2  - O2  - T1  = 109.471 deg; T1  -- T1  = 5.2578 A
T1  - O2  - T2  - O2  - T1  = 109.471 deg; T1  -- T1  = 5.2578 A
T1  - O2  - T2  - O2  - T1  = 109.471 deg; T1  -- T1  = 5.2578 A
T1  - O2  - T2  - O2  - T1  = 109.471 deg; T1  -- T1  = 5.2578 A
T1  - O2  - T2  - O2  - T1  = 109.471 deg; T1  -- T1  = 5.2578 A
T1  - O2  - T2  - O2  - T1  = 109.471 deg; T1  -- T1  = 5.2578 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 125.2644 deg
          Mean   = 108.3678 deg
          StdDev = 13.7018 deg

        T--T SUMMARY
          Range  = 4.3882 A <--> 5.6152 A
          Mean   = 5.1042 A
          StdDev = 0.4920 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 147.356 deg ; T1  -- T1   3.1029 A

T1  -- O2  -- T2  = 180.000 deg ; T1  -- T2   3.2198 A


        T-O-T SUMMARY
          Range  = 147.3557° <--> 180.0000 deg
          Mean   = 163.6778 deg
          StdDev = 16.4512 deg

        T--T SUMMARY
          Range  = 3.1029 A <--> 3.2198 A
          Mean   = 3.1613 A
          StdDev = 0.0589 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 32
Coordination Sequence =
    1 4 9 19 34 48 66 96 127 151 183 232 281 316 357 427 499
TD10 = 738
Circuit symbol = 4.6.4.6.4.6
Weight = 17
Vertex symbol  = 4.6.4.6.4.6
Weight = 17

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 18 28 52 78 88 112 162 204 220 254 328 396 414 448
TD10 = 759
Circuit symbol = 6.6.6.6.6.6
Weight = 23
Vertex symbol  = 6.6.6.6.6.6
Weight = 23

<TD10> = 742.200
Average ring size = 5.0000