Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_224-2_2_1769_Gaamze.cif"

There are 60 T-atoms per unit cell
There are 120 O-atoms per unit cell

Framework density = 19.69 T-atoms per nm^3
Material density = 1.965 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6109 Angstrom
T1  -- O2  = 1.6211 Angstrom
T1  -- O3  = 1.6225 Angstrom
T1  -- O4  = 1.5835 Angstrom
      mean = 1.6095 Angstrom
        t1 = 0.007388  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005933  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6169 Angstrom
T2  -- O4  = 1.6169 Angstrom
T2  -- O4  = 1.6169 Angstrom
T2  -- O4  = 1.6169 Angstrom
      mean = 1.6169 Angstrom
        t1 = 0.017938  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013162  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5835 A <--> 1.6225 A
          Mean   = 1.6110 A
          StdDev = 0.0144 A

       t1 Range  = 0.0074 <-- 0.0127 --> 0.0179
       t2 Range  = 0.0059 <-- 0.0095 --> 0.0132

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.403 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.683 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.516 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.721 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.792 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.706 deg; O3  -- O4  = 3 A
       108.516 deg <-- 109.470 deg --> 109.792 deg

O4  -- T2  -- O4  = 105.560 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 111.321 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 111.602 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 111.602 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 111.321 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 105.560 deg; O4  -- O4  = 3 A
       105.560 deg <-- 109.494 deg --> 111.602 deg

        O-T-O SUMMARY
          Range  = 105.5595 deg <--> 111.6025 deg
          Mean   = 109.4651 deg
          StdDev = 2.1326 deg

        O--O SUMMARY
          Range  = 2.5751 A <--> 2.6746 A
          Mean   = 2.6326 A
          StdDev = 0.0379 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 120.000 deg; T1  -- T1  = 5.4703 A
T1  - O1  - T1  - O3  - T1  = 120.000 deg; T1  -- T1  = 5.4101 A
T1  - O1  - T1  - O4  - T2  = 108.123 deg; T1  -- T2  = 5.1129 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.4038 A
T1  - O2  - T1  - O4  - T2  = 108.307 deg; T1  -- T2  = 5.1033 A
T1  - O3  - T1  - O4  - T2  = 108.977 deg; T1  -- T2  = 5.0681 A

T1  - O4  - T2  - O4  - T1  = 126.248 deg; T1  -- T1  = 5.6143 A
T1  - O4  - T2  - O4  - T1  = 102.611 deg; T1  -- T1  = 4.9125 A
T1  - O4  - T2  - O4  - T1  = 100.975 deg; T1  -- T1  = 4.8559 A
T1  - O4  - T2  - O4  - T1  = 100.975 deg; T1  -- T1  = 4.8559 A
T1  - O4  - T2  - O4  - T1  = 102.611 deg; T1  -- T1  = 4.9125 A
T1  - O4  - T2  - O4  - T1  = 126.248 deg; T1  -- T1  = 5.6143 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 126.2484 deg
          Mean   = 109.5311 deg
          StdDev = 10.2699 deg

        T--T SUMMARY
          Range  = 4.4038 A <--> 5.6143 A
          Mean   = 5.1135 A
          StdDev = 0.3206 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 159.024 deg ; T1  -- T1   3.1679 A

T1  -- O2  -- T1  = 152.401 deg ; T1  -- T1   3.1486 A

T1  -- O3  -- T1  = 143.171 deg ; T1  -- T1   3.0789 A

T1  -- O4  -- T2  = 159.065 deg ; T1  -- T2   3.1471 A


        T-O-T SUMMARY
          Range  = 143.1714° <--> 159.0647 deg
          Mean   = 153.4153 deg
          StdDev = 6.5234 deg

        T--T SUMMARY
          Range  = 3.0789 A <--> 3.1679 A
          Mean   = 3.1356 A
          StdDev = 0.0338 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 48
Coordination Sequence =
    1 4 11 23 40 62 88 119 155 196 242 292 347 407 472 542 616
TD10 = 941
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 24

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 12 24 38 60 88 120 158 196 238 292 348 408 474 540 614
TD10 = 939
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 21
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 21

<TD10> = 940.600
Average ring size = 5.7600