Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_222-2_1_109_je6tdb.cif"

There are 48 T-atoms per unit cell
There are 96 O-atoms per unit cell

Framework density = 29.07 T-atoms per nm^3
Material density = 2.900 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.9276 Angstrom
T1  -- O1  = 1.9276 Angstrom
T1  -- O2  = 1.5609 Angstrom
T1  -- O3  = 1.5813 Angstrom
T1  -- O3  = 1.6283 Angstrom
      mean = 1.7251 Angstrom

        T-O SUMMARY
          Range  = 1.5609 A <--> 1.9276 A
          Mean   = 1.7251 A
          StdDev = 0.1671 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  76.975 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  = 118.593 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  88.312 deg; O1  -- O3  = 2 A
O1  -- T1  -- O3  = 178.611 deg; O1  -- O3  = 4 A
O1  -- T1  -- O2  = 118.593 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 136.122 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  = 104.161 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 104.824 deg; O2  -- O3  = 2 A
O2  -- T1  -- O3  =  60.198 deg; O2  -- O3  = 2 A
O3  -- T1  -- O3  =  91.368 deg; O3  -- O3  = 2 A
       60.198 deg <-- 107.776 deg --> 178.611 deg

        O-T-O SUMMARY
          Range  = 60.1980 deg <--> 178.6107 deg
          Mean   = 108.3148 deg
          StdDev = 33.1953 deg

        O--O SUMMARY
          Range  = 1.6004 A <--> 3.5556 A
          Mean   = 2.6674 A
          StdDev = 0.5600 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 173.729 deg ; T1  -- T1   3.8493 A
T1  -- O1  -- T1  = 138.400 deg ; T1  -- T1   3.6039 A
T1  -- O1  -- T1  =  41.081 deg ; T1  -- T1   1.3527 A
T1  -- O1  -- T1  =  41.081 deg ; T1  -- T1   1.3527 A
T1  -- O1  -- T1  = 138.400 deg ; T1  -- T1   3.6039 A
T1  -- O1  -- T1  = 173.729 deg ; T1  -- T1   3.8493 A

T1  -- O2  -- T1  =  51.353 deg ; T1  -- T1   1.3527 A

T1  -- O3  -- T1  = 121.620 deg ; T1  -- T1   2.8021 A


        T-O-T SUMMARY
          Range  = 41.0815° <--> 173.7290 deg
          Mean   = 109.9241 deg
          StdDev = 53.4666 deg

        T--T SUMMARY
          Range  = 1.3527 A <--> 3.8493 A
          Mean   = 2.7208 A
          StdDev = 1.1042 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O3  = 1.6004 A
O2  -- O3  = 1.6004 A
O3  -- O3  = 2.2967 A
O3  -- O3  = 2.2967 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has only 3 neighboring T-atoms within 3.50 A, but 5 bridging O-atoms
  T1  -- T1  = 1.3527 Angstrom
  T1  -- T1  = 2.8021 Angstrom
  T1  -- T1  = 2.8021 Angstrom