Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_21_2_67162_BmWFxm.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 18.00 T-atoms per nm^3
Material density = 1.796 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6194 Angstrom
T1  -- O2  = 1.6155 Angstrom
T1  -- O3  = 1.6182 Angstrom
T1  -- O4  = 1.6186 Angstrom
      mean = 1.6179 Angstrom
        t1 = 0.005216  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001368  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6172 Angstrom
T2  -- O5  = 1.6155 Angstrom
T2  -- O6  = 1.6155 Angstrom
T2  -- O3  = 1.6175 Angstrom
      mean = 1.6164 Angstrom
        t1 = 0.004778  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001691  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6155 A <--> 1.6194 A
          Mean   = 1.6172 A
          StdDev = 0.0015 A

       t1 Range  = 0.0048 <-- 0.0050 --> 0.0052
       t2 Range  = 0.0014 <-- 0.0015 --> 0.0017

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.592 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.592 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.592 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.182 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.182 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.686 deg; O3  -- O4  = 3 A
       109.182 deg <-- 109.471 deg --> 109.686 deg

O4  -- T2  -- O5  = 109.268 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.395 deg; O4  -- O6  = 3 A
O4  -- T2  -- O3  = 110.302 deg; O4  -- O3  = 3 A
O5  -- T2  -- O6  = 109.188 deg; O5  -- O6  = 3 A
O5  -- T2  -- O3  = 109.271 deg; O5  -- O3  = 3 A
O6  -- T2  -- O3  = 109.398 deg; O6  -- O3  = 3 A
       109.188 deg <-- 109.470 deg --> 110.302 deg

        O-T-O SUMMARY
          Range  = 109.1815 deg <--> 110.3025 deg
          Mean   = 109.4780 deg
          StdDev = 0.3142 deg

        O--O SUMMARY
          Range  = 2.6335 A <--> 2.6546 A
          Mean   = 2.6410 A
          StdDev = 0.0061 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 127.633 deg; T1  -- T2  = 5.6663 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.4659 A
T1  - O1  - T1  - O4  - T2  = 127.633 deg; T1  -- T2  = 5.6663 A
T2  - O2  - T1  - O3  - T1  = 113.998 deg; T2  -- T1  = 5.1739 A
T2  - O2  - T1  - O4  - T2  =  85.613 deg; T2  -- T2  = 4.1921 A
T1  - O3  - T1  - O4  - T2  = 113.998 deg; T1  -- T2  = 5.1739 A

T1  - O4  - T2  - O5  - T2  = 118.914 deg; T1  -- T2  = 5.4398 A
T1  - O4  - T2  - O6  - T2  = 113.998 deg; T1  -- T2  = 5.2950 A
T1  - O4  - T2  - O3  - T1  =  75.267 deg; T1  -- T1  = 3.7669 A
T2  - O5  - T2  - O6  - T2  = 111.471 deg; T2  -- T2  = 5.3384 A
T2  - O5  - T2  - O3  - T1  = 118.914 deg; T2  -- T1  = 5.4398 A
T2  - O6  - T2  - O3  - T1  = 113.998 deg; T2  -- T1  = 5.2950 A

        T-T-T SUMMARY
          Range  = 75.2665 deg <--> 127.6333 deg
          Mean   = 108.3532 deg
          StdDev = 16.2216 deg

        T--T SUMMARY
          Range  = 3.7669 A <--> 5.6663 A
          Mean   = 5.0374 A
          StdDev = 0.5902 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 144.509 deg ; T1  -- T1   3.0847 A

T1  -- O2  -- T1  = 176.307 deg ; T1  -- T1   3.2293 A

T1  -- O3  -- T2  = 144.834 deg ; T1  -- T2   3.0846 A

T1  -- O4  -- T2  = 144.828 deg ; T1  -- T2   3.0846 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2311 A

T2  -- O6  -- T2  = 175.434 deg ; T2  -- T2   3.2284 A


        T-O-T SUMMARY
          Range  = 144.5090° <--> 180.0000 deg
          Mean   = 160.9852 deg
          StdDev = 16.4949 deg

        T--T SUMMARY
          Range  = 3.0846 A <--> 3.2311 A
          Mean   = 3.1571 A
          StdDev = 0.0733 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 21 38 59 83 112 144 181 227 276 327 382 440 504 576
TD10 = 880
Circuit symbol = 4.4.6_{3}.8_{6}.6_{3}.8_{6}
Weight = 28
Vertex symbol  = 4.4.6_{3}.8_{3}.6_{3}.8_{3}
Weight = 28

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 11 22 37 58 82 112 147 184 227 272 324 382 443 510 577
TD10 = 885
Circuit symbol = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 18
Vertex symbol  = 4.6_{2}.6.6_{2}.6.6_{2}
Weight = 18

<TD10> = 882.500
Average ring size = 6.0000