Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_217_2_217p_WbkcPX.cif"

There are 96 T-atoms per unit cell
There are 192 O-atoms per unit cell

Framework density = 23.28 T-atoms per nm^3
Material density = 2.322 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6415 Angstrom
T1  -- O2  = 1.6588 Angstrom
T1  -- O3  = 1.6386 Angstrom
T1  -- O4  = 1.6162 Angstrom
      mean = 1.6388 Angstrom
        t1 = 0.040623  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.024653  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6559 Angstrom
T2  -- O4  = 1.6374 Angstrom
T2  -- O5  = 1.6101 Angstrom
T2  -- O6  = 1.6327 Angstrom
      mean = 1.6340 Angstrom
        t1 = 0.024250  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.013802  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6101 A <--> 1.6588 A
          Mean   = 1.6364 A
          StdDev = 0.0159 A

       t1 Range  = 0.0242 <-- 0.0324 --> 0.0406
       t2 Range  = 0.0138 <-- 0.0192 --> 0.0247

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.567 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 106.938 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 115.365 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 118.641 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 106.458 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 102.231 deg; O3  -- O4  = 3 A
       102.231 deg <-- 109.533 deg --> 118.641 deg

O3  -- T2  -- O4  = 112.816 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 107.810 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 112.387 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 107.638 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 108.181 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 107.790 deg; O5  -- O6  = 3 A
       107.638 deg <-- 109.437 deg --> 112.816 deg

        O-T-O SUMMARY
          Range  = 102.2312 deg <--> 118.6411 deg
          Mean   = 109.6494 deg
          StdDev = 4.4467 deg

        O--O SUMMARY
          Range  = 2.5336 A <--> 2.8359 A
          Mean   = 2.6735 A
          StdDev = 0.0802 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 3.9645 A
T1  - O1  - T1  - O3  - T2  =  90.678 deg; T1  -- T2  = 4.0103 A
T1  - O1  - T1  - O4  - T2  = 178.823 deg; T1  -- T2  = 5.5620 A
T1  - O2  - T1  - O3  - T2  = 178.757 deg; T1  -- T2  = 5.7216 A
T1  - O2  - T1  - O4  - T2  =  90.471 deg; T1  -- T2  = 4.0096 A
T2  - O3  - T1  - O4  - T2  =  88.871 deg; T2  -- T2  = 3.9757 A

T1  - O3  - T2  - O4  - T2  =  89.322 deg; T1  -- T2  = 4.0103 A
T1  - O3  - T2  - O5  - T2  = 119.534 deg; T1  -- T2  = 4.9834 A
T1  - O3  - T2  - O6  - T1  = 120.626 deg; T1  -- T1  = 4.9330 A
T2  - O4  - T2  - O5  - T2  = 120.000 deg; T2  -- T2  = 4.9538 A
T2  - O4  - T2  - O6  - T1  = 121.153 deg; T2  -- T1  = 4.9041 A
T2  - O5  - T2  - O6  - T1  =  89.529 deg; T2  -- T1  = 4.0096 A

        T-T-T SUMMARY
          Range  = 88.8714 deg <--> 178.8227 deg
          Mean   = 117.0909 deg
          StdDev = 32.1913 deg

        T--T SUMMARY
          Range  = 3.9645 A <--> 5.7216 A
          Mean   = 4.6410 A
          StdDev = 0.6367 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 114.471 deg ; T1  -- T1   2.7606 A

T1  -- O2  -- T1  = 118.111 deg ; T1  -- T1   2.8454 A

T1  -- O3  -- T2  = 121.645 deg ; T1  -- T2   2.8765 A

T1  -- O4  -- T2  = 118.879 deg ; T1  -- T2   2.8017 A

T2  -- O5  -- T2  = 122.894 deg ; T2  -- T2   2.8286 A

T2  -- O6  -- T2  = 124.622 deg ; T2  -- T2   2.8915 A


        T-O-T SUMMARY
          Range  = 114.4708° <--> 124.6215 deg
          Mean   = 120.1036 deg
          StdDev = 3.3667 deg

        T--T SUMMARY
          Range  = 2.7606 A <--> 2.8915 A
          Mean   = 2.8340 A
          StdDev = 0.0442 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7606 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 48
Coordination Sequence =
    1 4 9 19 35 53 73 101 139 179 222 278 344 410 472 538 621
TD10 = 835
Circuit symbol = 4.4.4.6.6.6
Weight = 11
Vertex symbol  = 4.4.4.6.10_{2}.10_{2}
Weight = 28

T2 (Si): multiplicity = 48
Coordination Sequence =
    1 4 10 19 33 54 80 110 144 185 233 284 340 408 489 573 652
TD10 = 873
Circuit symbol = 4.4.6.6.6.8_{3}
Weight = 19
Vertex symbol  = 4.4.6.6.6.8
Weight = 19

<TD10> = 854.000
Average ring size = 5.7338