Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_217_2_217_QW_duU.cif"

There are 96 T-atoms per unit cell
There are 192 O-atoms per unit cell

Framework density = 24.07 T-atoms per nm^3
Material density = 2.401 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6519 Angstrom
T1  -- O2  = 1.6347 Angstrom
T1  -- O3  = 1.6166 Angstrom
T1  -- O4  = 1.6394 Angstrom
      mean = 1.6357 Angstrom
        t1 = 0.033688  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019601  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6432 Angstrom
T2  -- O4  = 1.6529 Angstrom
T2  -- O5  = 1.6314 Angstrom
T2  -- O6  = 1.6140 Angstrom
      mean = 1.6354 Angstrom
        t1 = 0.022459  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010594  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6140 A <--> 1.6529 A
          Mean   = 1.6355 A
          StdDev = 0.0136 A

       t1 Range  = 0.0225 <-- 0.0281 --> 0.0337
       t2 Range  = 0.0106 <-- 0.0151 --> 0.0196

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.352 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.000 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 117.151 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 113.165 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 107.135 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 103.146 deg; O3  -- O4  = 3 A
       103.146 deg <-- 109.491 deg --> 117.151 deg

O3  -- T2  -- O4  = 112.427 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 108.433 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 107.987 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 111.589 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 108.298 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 107.951 deg; O5  -- O6  = 3 A
       107.951 deg <-- 109.447 deg --> 112.427 deg

        O-T-O SUMMARY
          Range  = 103.1456 deg <--> 117.1514 deg
          Mean   = 109.5893 deg
          StdDev = 3.5680 deg

        O--O SUMMARY
          Range  = 2.5508 A <--> 2.8086 A
          Mean   = 2.6720 A
          StdDev = 0.0655 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 3.8910 A
T1  - O1  - T1  - O3  - T2  =  90.908 deg; T1  -- T2  = 3.9331 A
T1  - O1  - T1  - O4  - T2  = 179.333 deg; T1  -- T2  = 5.6222 A
T1  - O2  - T1  - O3  - T2  = 177.836 deg; T1  -- T2  = 5.5182 A
T1  - O2  - T1  - O4  - T2  =  90.624 deg; T1  -- T2  = 3.9984 A
T2  - O3  - T1  - O4  - T2  =  88.460 deg; T2  -- T2  = 3.9340 A

T1  - O3  - T2  - O4  - T2  =  89.092 deg; T1  -- T2  = 3.9331 A
T1  - O3  - T2  - O5  - T2  = 122.127 deg; T1  -- T2  = 4.8849 A
T1  - O3  - T2  - O6  - T1  = 119.095 deg; T1  -- T1  = 4.8612 A
T2  - O4  - T2  - O5  - T2  = 120.000 deg; T2  -- T2  = 4.8956 A
T2  - O4  - T2  - O6  - T1  = 120.551 deg; T2  -- T1  = 4.9587 A
T2  - O5  - T2  - O6  - T1  =  89.376 deg; T2  -- T1  = 3.9984 A

        T-T-T SUMMARY
          Range  = 88.4602 deg <--> 179.3331 deg
          Mean   = 117.0649 deg
          StdDev = 32.1589 deg

        T--T SUMMARY
          Range  = 3.8910 A <--> 5.6222 A
          Mean   = 4.5895 A
          StdDev = 0.6316 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 112.754 deg ; T1  -- T1   2.7511 A

T1  -- O2  -- T1  = 114.622 deg ; T1  -- T1   2.7516 A

T1  -- O3  -- T2  = 116.202 deg ; T1  -- T2   2.7676 A

T1  -- O4  -- T2  = 121.402 deg ; T1  -- T2   2.8712 A

T2  -- O5  -- T2  = 120.934 deg ; T2  -- T2   2.8388 A

T2  -- O6  -- T2  = 121.337 deg ; T2  -- T2   2.8141 A


        T-O-T SUMMARY
          Range  = 112.7541° <--> 121.4024 deg
          Mean   = 117.8752 deg
          StdDev = 3.5036 deg

        T--T SUMMARY
          Range  = 2.7511 A <--> 2.8712 A
          Mean   = 2.7991 A
          StdDev = 0.0458 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7511 Angstrom
T1  -- T1  = 2.7516 Angstrom
T1  -- T2  = 2.7676 Angstrom
T2  -- T1  = 2.7676 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 48
Coordination Sequence =
    1 4 9 19 35 53 73 101 139 179 222 278 344 410 472 538 621
TD10 = 835
Circuit symbol = 4.4.4.6.6.6
Weight = 11
Vertex symbol  = 4.4.4.6.10_{2}.10_{2}
Weight = 28

T2 (Si): multiplicity = 48
Coordination Sequence =
    1 4 10 19 33 54 80 110 144 185 233 284 340 408 489 573 652
TD10 = 873
Circuit symbol = 4.4.6.6.6.8_{3}
Weight = 19
Vertex symbol  = 4.4.6.6.6.8
Weight = 19

<TD10> = 854.000
Average ring size = 5.7338