Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_214_1_532_IlGGqr.cif"

There are 48 T-atoms per unit cell
There are 96 O-atoms per unit cell

Framework density = 9.26 T-atoms per nm^3
Material density = 0.924 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.8416 Angstrom
T1  -- O2  = 1.8416 Angstrom
T1  -- O2  = 1.7332 Angstrom
T1  -- O3  = 1.8534 Angstrom
T1  -- O1  = 1.7022 Angstrom
T1  -- O3  = 1.8534 Angstrom
      mean = 1.8042 Angstrom

        T-O SUMMARY
          Range  = 1.7022 A <--> 1.8534 A
          Mean   = 1.8042 A
          StdDev = 0.0621 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O2  = 103.474 deg; O2  -- O2  = 3 A
O2  -- T1  -- O2  =  85.279 deg; O2  -- O2  = 2 A
O2  -- T1  -- O3  = 136.612 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 128.077 deg; O2  -- O1  = 3 A
O2  -- T1  -- O3  =  76.389 deg; O2  -- O3  = 2 A
O2  -- T1  -- O2  =  67.848 deg; O2  -- O2  = 2 A
O2  -- T1  -- O3  =  76.389 deg; O2  -- O3  = 2 A
O2  -- T1  -- O1  = 128.077 deg; O2  -- O1  = 3 A
O2  -- T1  -- O3  = 136.611 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  = 130.834 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 106.677 deg; O2  -- O1  = 3 A
O2  -- T1  -- O3  = 152.112 deg; O2  -- O3  = 3 A
O3  -- T1  -- O1  =  70.538 deg; O3  -- O1  = 2 A
O3  -- T1  -- O3  =  75.559 deg; O3  -- O3  = 2 A
O1  -- T1  -- O3  =  70.538 deg; O1  -- O3  = 2 A
       67.848 deg <-- 103.001 deg --> 152.112 deg

        O-T-O SUMMARY
          Range  = 67.8478 deg <--> 152.1124 deg
          Mean   = 106.4221 deg
          StdDev = 28.5098 deg

        O--O SUMMARY
          Range  = 1.9971 A <--> 3.4811 A
          Mean   = 2.8009 A
          StdDev = 0.5309 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O2  - T1  - O2  - T1  =  60.000 deg; T1  -- T1  = 3.1467 A
T1  - O2  - T1  - O2  - T1  =  23.269 deg; T1  -- T1  = 1.2767 A
T1  - O2  - T1  - O3  - T1  = 100.850 deg; T1  -- T1  = 3.6116 A
T1  - O2  - T1  - O1  - T1  = 166.672 deg; T1  -- T1  = 5.7449 A
T1  - O2  - T1  - O3  - T1  = 163.304 deg; T1  -- T1  = 6.0122 A
T1  - O2  - T1  - O2  - T1  =  77.228 deg; T1  -- T1  = 3.6116 A
T1  - O2  - T1  - O3  - T1  =  53.563 deg; T1  -- T1  = 2.5999 A
T1  - O2  - T1  - O1  - T1  = 133.328 deg; T1  -- T1  = 5.3144 A
T1  - O2  - T1  - O3  - T1  = 111.026 deg; T1  -- T1  = 5.0101 A
T1  - O2  - T1  - O3  - T1  = 103.169 deg; T1  -- T1  = 3.1467 A
T1  - O2  - T1  - O1  - T1  = 146.149 deg; T1  -- T1  = 5.0101 A
T1  - O2  - T1  - O3  - T1  = 147.862 deg; T1  -- T1  = 5.3144 A
T1  - O3  - T1  - O1  - T1  =  90.000 deg; T1  -- T1  = 2.9298 A
T1  - O3  - T1  - O3  - T1  =  64.167 deg; T1  -- T1  = 2.6370 A
T1  - O1  - T1  - O3  - T1  =  25.833 deg; T1  -- T1  = 1.2767 A

        T-T-T SUMMARY
          Range  = 23.2689 deg <--> 166.6715 deg
          Mean   = 101.9570 deg
          StdDev = 45.3074 deg

        T--T SUMMARY
          Range  = 1.2767 A <--> 6.0122 A
          Mean   = 3.9423 A
          StdDev = 1.4640 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 101.533 deg ; T1  -- T1   2.6370 A

T1  -- O2  -- T1  =  40.561 deg ; T1  -- T1   1.2767 A
T1  -- O2  -- T1  =  93.268 deg ; T1  -- T1   2.5999 A
T1  -- O2  -- T1  = 123.313 deg ; T1  -- T1   3.1467 A

T1  -- O3  -- T1  =  40.291 deg ; T1  -- T1   1.2767 A
T1  -- O3  -- T1  =  90.696 deg ; T1  -- T1   2.6370 A
T1  -- O3  -- T1  = 104.441 deg ; T1  -- T1   2.9298 A
T1  -- O3  -- T1  = 104.441 deg ; T1  -- T1   2.9298 A
T1  -- O3  -- T1  =  90.696 deg ; T1  -- T1   2.6370 A
T1  -- O3  -- T1  =  40.291 deg ; T1  -- T1   1.2767 A


        T-O-T SUMMARY
          Range  = 40.2912° <--> 123.3135 deg
          Mean   = 82.9530 deg
          StdDev = 29.2898 deg

        T--T SUMMARY
          Range  = 1.2767 A <--> 3.1467 A
          Mean   = 2.3347 A
          StdDev = 0.7128 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O3  = 2.0568 A
O1  -- O3  = 2.0568 A
O2  -- O2  = 1.9971 A
O2  -- O2  = 1.9971 A
O2  -- O3  = 2.2848 A
O3  -- O3  = 2.2709 A

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 oxygen-bridged T-atoms within 3.50 A
  T1  -- T1  = 3.1467 Angstrom
  T1  -- T1  = 3.1467 Angstrom
  T1  -- T1  = 2.5999 Angstrom
  T1  -- T1  = 1.2767 Angstrom
  T1  -- T1  = 2.6370 Angstrom
  T1  -- T1  = 2.9298 Angstrom