Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_214_1_2103_4AX1Ys.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 20.29 T-atoms per nm^3
Material density = 2.024 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6397 Angstrom
T1  -- O1  = 1.6397 Angstrom
T1  -- O2  = 1.6900 Angstrom
T1  -- O2  = 1.6900 Angstrom
      mean = 1.6649 Angstrom
        t1 = 0.140425  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.085299  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6397 A <--> 1.6900 A
          Mean   = 1.6649 A
          StdDev = 0.0253 A

       t1 Range  = 0.1404 <-- 0.1404 --> 0.1404
       t2 Range  = 0.0853 <-- 0.0853 --> 0.0853

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 138.447 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 108.104 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  =  85.071 deg; O1  -- O2  = 2 A
O1  -- T1  -- O2  =  85.071 deg; O1  -- O2  = 2 A
O1  -- T1  -- O2  = 108.104 deg; O1  -- O2  = 3 A
O2  -- T1  -- O2  = 143.047 deg; O2  -- O2  = 3 A
       85.071 deg <-- 111.308 deg --> 143.047 deg

        O-T-O SUMMARY
          Range  = 85.0714 deg <--> 143.0471 deg
          Mean   = 111.3076 deg
          StdDev = 22.9604 deg

        O--O SUMMARY
          Range  = 2.2514 A <--> 3.2058 A
          Mean   = 2.6944 A
          StdDev = 0.3647 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  71.728 deg; T1  -- T1  = 3.5754 A
T1  - O1  - T1  - O2  - T1  = 137.243 deg; T1  -- T1  = 6.2681 A
T1  - O1  - T1  - O2  - T1  = 105.077 deg; T1  -- T1  = 4.8008 A
T1  - O1  - T1  - O2  - T1  = 105.077 deg; T1  -- T1  = 4.8008 A
T1  - O1  - T1  - O2  - T1  = 171.598 deg; T1  -- T1  = 5.3022 A
T1  - O2  - T1  - O2  - T1  =  71.728 deg; T1  -- T1  = 3.5754 A

        T-T-T SUMMARY
          Range  = 71.7282 deg <--> 171.5980 deg
          Mean   = 110.4085 deg
          StdDev = 35.5105 deg

        T--T SUMMARY
          Range  = 3.5754 A <--> 6.2681 A
          Mean   = 4.7205 A
          StdDev = 0.9492 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 108.304 deg ; T1  -- T1   2.6582 A

T1  -- O2  -- T1  = 169.428 deg ; T1  -- T1   3.3656 A


        T-O-T SUMMARY
          Range  = 108.3044° <--> 169.4280 deg
          Mean   = 138.8662 deg
          StdDev = 30.8852 deg

        T--T SUMMARY
          Range  = 2.6582 A <--> 3.3656 A
          Mean   = 3.0119 A
          StdDev = 0.3574 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 2.2514 A
O1  -- O2  = 2.2514 A
T1  -- T1  = 2.6582 Angstrom
T1  -- T1  = 2.6582 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 20 40 76 116 158 220 280 342 436 516 598 724 824 926
TD10 = 1267
Circuit symbol = 4.4.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 9
Vertex symbol  = 4.4.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 9

<TD10> = 1267.000
Average ring size = 5.4545