Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_211_1_2650_V53Fnv.cif"

There are 48 T-atoms per unit cell
There are 96 O-atoms per unit cell

Framework density = 19.74 T-atoms per nm^3
Material density = 1.970 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6846 Angstrom
T1  -- O2  = 1.6435 Angstrom
T1  -- O1  = 1.6515 Angstrom
T1  -- O2  = 1.6435 Angstrom
T1  -- O3  = 1.6912 Angstrom
      mean = 1.6628 Angstrom

        T-O SUMMARY
          Range  = 1.6435 A <--> 1.6912 A
          Mean   = 1.6628 A
          StdDev = 0.0208 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  =  66.795 deg; O1  -- O2  = 2 A
O1  -- T1  -- O1  =  90.689 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  = 128.205 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 138.251 deg; O1  -- O3  = 3 A
O2  -- T1  -- O1  = 128.770 deg; O2  -- O1  = 3 A
O2  -- T1  -- O2  =  90.478 deg; O2  -- O2  = 2 A
O2  -- T1  -- O3  = 136.009 deg; O2  -- O3  = 3 A
O1  -- T1  -- O2  =  67.570 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  =  91.754 deg; O1  -- O3  = 2 A
O2  -- T1  -- O3  =  90.727 deg; O2  -- O3  = 2 A
       66.795 deg <-- 102.925 deg --> 138.251 deg

        O-T-O SUMMARY
          Range  = 66.7945 deg <--> 138.2507 deg
          Mean   = 102.4282 deg
          StdDev = 26.7820 deg

        O--O SUMMARY
          Range  = 1.8322 A <--> 3.1542 A
          Mean   = 2.5242 A
          StdDev = 0.4861 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 106.979 deg ; T1  -- T1   2.6814 A

T1  -- O2  -- T1  = 109.330 deg ; T1  -- T1   2.6814 A
T1  -- O2  -- T1  =  66.298 deg ; T1  -- T1   1.7974 A
T1  -- O2  -- T1  = 158.283 deg ; T1  -- T1   3.2281 A
T1  -- O2  -- T1  = 158.283 deg ; T1  -- T1   3.2281 A
T1  -- O2  -- T1  =  66.298 deg ; T1  -- T1   1.7974 A
T1  -- O2  -- T1  = 109.330 deg ; T1  -- T1   2.6814 A

T1  -- O3  -- T1  = 141.696 deg ; T1  -- T1   3.1951 A


        T-O-T SUMMARY
          Range  = 66.2979° <--> 158.2832 deg
          Mean   = 114.5621 deg
          StdDev = 34.1958 deg

        T--T SUMMARY
          Range  = 1.7974 A <--> 3.2281 A
          Mean   = 2.6613 A
          StdDev = 0.5509 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 1.8322 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 7 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 1.7974 Angstrom
  T1  -- T1  = 3.2281 Angstrom
  T1  -- T1  = 2.6814 Angstrom
  T1  -- T1  = 3.1951 Angstrom
  T1  -- T1  = 2.6814 Angstrom
  T1  -- T1  = 3.2281 Angstrom
  T1  -- T1  = 3.1951 Angstrom