Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_210_1_325_D8YXEv.cif"

There are 96 T-atoms per unit cell
There are 192 O-atoms per unit cell

Framework density = 22.89 T-atoms per nm^3
Material density = 2.284 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.5811 Angstrom
T1  -- O2  = 1.6604 Angstrom
T1  -- O1  = 1.7781 Angstrom
T1  -- O1  = 1.8541 Angstrom
T1  -- O3  = 1.6871 Angstrom
      mean = 1.7121 Angstrom

        T-O SUMMARY
          Range  = 1.5811 A <--> 1.8541 A
          Mean   = 1.7121 A
          StdDev = 0.0949 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O2  =  89.873 deg; O2  -- O2  = 2 A
O2  -- T1  -- O1  =  74.598 deg; O2  -- O1  = 2 A
O2  -- T1  -- O1  = 131.239 deg; O2  -- O1  = 3 A
O2  -- T1  -- O3  = 132.010 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 131.131 deg; O2  -- O1  = 3 A
O2  -- T1  -- O1  =  70.785 deg; O2  -- O1  = 2 A
O2  -- T1  -- O3  =  91.521 deg; O2  -- O3  = 2 A
O1  -- T1  -- O1  =  85.243 deg; O1  -- O1  = 2 A
O1  -- T1  -- O3  = 133.177 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  =  93.937 deg; O1  -- O3  = 3 A
       70.785 deg <-- 103.351 deg --> 133.177 deg

        O-T-O SUMMARY
          Range  = 70.7847 deg <--> 133.1765 deg
          Mean   = 103.2158 deg
          StdDev = 24.8266 deg

        O--O SUMMARY
          Range  = 2.0416 A <--> 3.1801 A
          Mean   = 2.6041 A
          StdDev = 0.4410 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  82.826 deg ; T1  -- T1   2.4033 A
T1  -- O1  -- T1  = 172.855 deg ; T1  -- T1   3.5492 A
T1  -- O1  -- T1  =  97.052 deg ; T1  -- T1   2.7219 A
T1  -- O1  -- T1  =  97.052 deg ; T1  -- T1   2.7219 A
T1  -- O1  -- T1  = 178.056 deg ; T1  -- T1   3.7076 A
T1  -- O1  -- T1  =  82.826 deg ; T1  -- T1   2.4033 A

T1  -- O2  -- T1  =  95.671 deg ; T1  -- T1   2.4033 A

T1  -- O3  -- T1  = 176.615 deg ; T1  -- T1   3.3727 A


        T-O-T SUMMARY
          Range  = 82.8258° <--> 178.0563 deg
          Mean   = 122.8692 deg
          StdDev = 41.4283 deg

        T--T SUMMARY
          Range  = 2.4033 A <--> 3.7076 A
          Mean   = 2.9104 A
          StdDev = 0.5127 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 2.0416 A
O1  -- O2  = 2.0416 A
O2  -- O2  = 2.2902 A
O2  -- O2  = 2.2902 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 2.4033 Angstrom
  T1  -- T1  = 2.4033 Angstrom
  T1  -- T1  = 2.7219 Angstrom
  T1  -- T1  = 2.7219 Angstrom
  T1  -- T1  = 3.2810 Angstrom
  T1  -- T1  = 3.3727 Angstrom