Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_210_1_224_wuje8o.cif"

There are 96 T-atoms per unit cell
There are 192 O-atoms per unit cell

Framework density = 23.28 T-atoms per nm^3
Material density = 2.323 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6875 Angstrom
T1  -- O1  = 1.8136 Angstrom
T1  -- O2  = 1.6970 Angstrom
T1  -- O2  = 1.5359 Angstrom
T1  -- O3  = 1.6633 Angstrom
      mean = 1.6795 Angstrom

        T-O SUMMARY
          Range  = 1.5359 A <--> 1.8136 A
          Mean   = 1.6795 A
          StdDev = 0.0887 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  88.813 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  =  72.788 deg; O1  -- O2  = 2 A
O1  -- T1  -- O2  = 138.428 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 100.474 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 129.289 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  =  73.143 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  = 131.417 deg; O1  -- O3  = 3 A
O2  -- T1  -- O2  =  89.933 deg; O2  -- O2  = 2 A
O2  -- T1  -- O3  =  98.722 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  = 119.703 deg; O2  -- O3  = 3 A
       72.788 deg <-- 104.271 deg --> 138.428 deg

        O-T-O SUMMARY
          Range  = 72.7875 deg <--> 138.4281 deg
          Mean   = 103.8067 deg
          StdDev = 23.5806 deg

        O--O SUMMARY
          Range  = 2.0082 A <--> 3.1728 A
          Mean   = 2.5772 A
          StdDev = 0.4200 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  83.011 deg ; T1  -- T1   2.3221 A
T1  -- O1  -- T1  = 174.826 deg ; T1  -- T1   3.3716 A
T1  -- O1  -- T1  =  97.136 deg ; T1  -- T1   2.6263 A
T1  -- O1  -- T1  =  97.136 deg ; T1  -- T1   2.6263 A
T1  -- O1  -- T1  = 176.767 deg ; T1  -- T1   3.6258 A
T1  -- O1  -- T1  =  83.011 deg ; T1  -- T1   2.3221 A

T1  -- O2  -- T1  =  91.685 deg ; T1  -- T1   2.3221 A

T1  -- O3  -- T1  = 177.523 deg ; T1  -- T1   3.3258 A


        T-O-T SUMMARY
          Range  = 83.0107° <--> 177.5233 deg
          Mean   = 122.6370 deg
          StdDev = 41.9578 deg

        T--T SUMMARY
          Range  = 2.3221 A <--> 3.6258 A
          Mean   = 2.8178 A
          StdDev = 0.5038 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 2.0082 A
O1  -- O2  = 2.0082 A
O2  -- O2  = 2.2875 A
O2  -- O2  = 2.2875 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 7 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 2.3221 Angstrom
  T1  -- T1  = 2.3221 Angstrom
  T1  -- T1  = 3.3716 Angstrom
  T1  -- T1  = 2.6263 Angstrom
  T1  -- T1  = 2.6263 Angstrom
  T1  -- T1  = 3.3258 Angstrom
  T1  -- T1  = 3.4648 Angstrom