Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_20_2_21439_78xNtG.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 22.81 T-atoms per nm^3
Material density = 2.276 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6156 Angstrom
T1  -- O2  = 1.6212 Angstrom
T1  -- O4  = 1.6252 Angstrom
T1  -- O3  = 1.6124 Angstrom
      mean = 1.6186 Angstrom
        t1 = 0.008483  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005432  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6226 Angstrom
T2  -- O4  = 1.6263 Angstrom
T2  -- O5  = 1.6160 Angstrom
T2  -- O3  = 1.6137 Angstrom
      mean = 1.6196 Angstrom
        t1 = 0.008936  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004336  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6124 A <--> 1.6263 A
          Mean   = 1.6191 A
          StdDev = 0.0051 A

       t1 Range  = 0.0085 <-- 0.0087 --> 0.0089
       t2 Range  = 0.0043 <-- 0.0049 --> 0.0054

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.285 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 110.176 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 107.702 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.652 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.664 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.331 deg; O4  -- O3  = 3 A
       107.702 deg <-- 109.468 deg --> 110.285 deg

O2  -- T2  -- O4  = 109.652 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.783 deg; O2  -- O5  = 3 A
O2  -- T2  -- O3  = 108.593 deg; O2  -- O3  = 3 A
O4  -- T2  -- O5  = 110.650 deg; O4  -- O5  = 3 A
O4  -- T2  -- O3  = 109.981 deg; O4  -- O3  = 3 A
O5  -- T2  -- O3  = 108.142 deg; O5  -- O3  = 3 A
       108.142 deg <-- 109.467 deg --> 110.650 deg

        O-T-O SUMMARY
          Range  = 107.7017 deg <--> 110.6496 deg
          Mean   = 109.4675 deg
          StdDev = 0.8557 deg

        O--O SUMMARY
          Range  = 2.6065 A <--> 2.6665 A
          Mean   = 2.6439 A
          StdDev = 0.0176 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  = 109.937 deg; T2  -- T2  = 4.9213 A
T2  - O1  - T1  - O4  - T1  = 110.912 deg; T2  -- T1  = 5.0726 A
T2  - O1  - T1  - O3  - T2  = 109.347 deg; T2  -- T2  = 4.9213 A
T2  - O2  - T1  - O4  - T1  = 110.398 deg; T2  -- T1  = 5.0962 A
T2  - O2  - T1  - O3  - T2  = 105.874 deg; T2  -- T2  = 4.8520 A
T1  - O4  - T1  - O3  - T2  = 110.246 deg; T1  -- T2  = 5.1092 A

T1  - O2  - T2  - O4  - T1  = 109.937 deg; T1  -- T1  = 4.9213 A
T1  - O2  - T2  - O5  - T2  = 110.337 deg; T1  -- T2  = 5.0818 A
T1  - O2  - T2  - O3  - T1  = 109.347 deg; T1  -- T1  = 4.9213 A
T1  - O4  - T2  - O5  - T2  = 119.816 deg; T1  -- T2  = 5.3977 A
T1  - O4  - T2  - O3  - T1  = 105.874 deg; T1  -- T1  = 4.8520 A
T2  - O5  - T2  - O3  - T1  = 100.684 deg; T2  -- T1  = 4.8199 A

        T-T-T SUMMARY
          Range  = 100.6842 deg <--> 119.8159 deg
          Mean   = 109.3926 deg
          StdDev = 4.2528 deg

        T--T SUMMARY
          Range  = 4.8199 A <--> 5.3977 A
          Mean   = 4.9972 A
          StdDev = 0.1569 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 158.815 deg ; T1  -- T1   3.1761 A

T1  -- O2  -- T2  = 133.535 deg ; T1  -- T2   2.9807 A

T1  -- O3  -- T2  = 142.083 deg ; T1  -- T2   3.0511 A

T1  -- O4  -- T2  = 137.391 deg ; T1  -- T2   3.0293 A

T2  -- O5  -- T2  = 166.127 deg ; T2  -- T2   3.2083 A


        T-O-T SUMMARY
          Range  = 133.5349° <--> 166.1267 deg
          Mean   = 147.5902 deg
          StdDev = 12.8221 deg

        T--T SUMMARY
          Range  = 2.9807 A <--> 3.2083 A
          Mean   = 3.0891 A
          StdDev = 0.0889 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 25 44 67 96 130 170 214 264 319 380 445 516 592 674
TD10 = 1027
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 24 42 66 96 130 170 214 264 318 378 444 516 592 674
TD10 = 1023
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29

<TD10> = 1025.000
Average ring size = 6.0000