Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_209_1_201_UFCcsV.cif"

There are 96 T-atoms per unit cell
There are 192 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6967 Angstrom
T1  -- O3  = 1.9112 Angstrom
T1  -- O3  = 1.9112 Angstrom
T1  -- O2  = 1.7244 Angstrom
      mean = 1.8109 Angstrom
        t1 = 0.206514  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.206353  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6967 A <--> 1.9112 A
          Mean   = 1.8109 A
          StdDev = 0.1010 A

       t1 Range  = 0.2065 <-- 0.2065 --> 0.2065
       t2 Range  = 0.2064 <-- 0.2064 --> 0.2064

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O3  = 114.765 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  =  60.625 deg; O2  -- O3  = 2 A
O2  -- T1  -- O2  =  82.620 deg; O2  -- O2  = 2 A
O3  -- T1  -- O3  =  87.240 deg; O3  -- O3  = 3 A
O3  -- T1  -- O2  =  60.196 deg; O3  -- O2  = 2 A
O3  -- T1  -- O2  = 114.528 deg; O3  -- O2  = 3 A
       60.196 deg <-- 86.662 deg --> 114.765 deg

        O-T-O SUMMARY
          Range  = 60.1958 deg <--> 114.7654 deg
          Mean   = 86.6099 deg
          StdDev = 23.2255 deg

        O--O SUMMARY
          Range  = 1.8304 A <--> 3.0599 A
          Mean   = 2.4252 A
          StdDev = 0.5297 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O2  - T1  - O3  - T1  =  60.000 deg; T1  -- T1  = 1.9773 A
T1  - O2  - T1  - O3  - T1  = 135.000 deg; T1  -- T1  = 4.7011 A
T1  - O2  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 3.6687 A
T1  - O3  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 3.6687 A
T1  - O3  - T1  - O2  - T1  = 135.000 deg; T1  -- T1  = 4.7011 A
T1  - O3  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.3703 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 135.0000 deg
          Mean   = 100.9091 deg
          StdDev = 27.9727 deg

        T--T SUMMARY
          Range  = 1.9773 A <--> 4.7011 A
          Mean   = 3.8641 A
          StdDev = 0.9802 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O2  -- T1  = 129.186 deg ; T1  -- T1   3.0902 A

T1  -- O3  -- T1  =  62.299 deg ; T1  -- T1   1.9773 A
T1  -- O3  -- T1  = 147.381 deg ; T1  -- T1   3.6687 A
T1  -- O3  -- T1  = 107.886 deg ; T1  -- T1   3.0902 A
T1  -- O3  -- T1  = 107.886 deg ; T1  -- T1   3.0902 A
T1  -- O3  -- T1  = 147.381 deg ; T1  -- T1   3.6687 A
T1  -- O3  -- T1  =  62.299 deg ; T1  -- T1   1.9773 A


        T-O-T SUMMARY
          Range  = 62.2991° <--> 147.3812 deg
          Mean   = 109.1886 deg
          StdDev = 33.2295 deg

        T--T SUMMARY
          Range  = 1.9773 A <--> 3.6687 A
          Mean   = 2.9375 A
          StdDev = 0.6533 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O2  = 2.2585 A
O2  -- O2  = 2.2585 A
O2  -- O3  = 1.8304 A
T1  -- T1  = 1.9773 Angstrom
T1  -- T1  = 1.9773 Angstrom