Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_207_1_2377_d5YSfK.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 30.31 T-atoms per nm^3
Material density = 3.024 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6305 Angstrom
T1  -- O1  = 1.5398 Angstrom
T1  -- O2  = 1.6114 Angstrom
T1  -- O3  = 1.8227 Angstrom
T1  -- O3  = 1.8227 Angstrom
      mean = 1.6854 Angstrom

        T-O SUMMARY
          Range  = 1.5398 A <--> 1.8227 A
          Mean   = 1.6854 A
          StdDev = 0.1166 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  85.721 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  = 100.024 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  =  68.506 deg; O1  -- O3  = 2 A
O1  -- T1  -- O3  = 128.367 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  =  97.315 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  = 130.759 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  =  70.321 deg; O1  -- O3  = 2 A
O2  -- T1  -- O3  = 127.193 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  = 127.193 deg; O2  -- O3  = 3 A
O3  -- T1  -- O3  =  93.262 deg; O3  -- O3  = 3 A
       68.506 deg <-- 102.866 deg --> 130.759 deg

        O-T-O SUMMARY
          Range  = 68.5056 deg <--> 130.7586 deg
          Mean   = 100.5690 deg
          StdDev = 23.3052 deg

        O--O SUMMARY
          Range  = 1.9501 A <--> 3.1097 A
          Mean   = 2.5269 A
          StdDev = 0.4565 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  60.000 deg; T1  -- T1  = 2.4405 A
T1  - O1  - T1  - O2  - T1  = 135.000 deg; T1  -- T1  = 5.2311 A
T1  - O1  - T1  - O3  - T1  = 135.000 deg; T1  -- T1  = 4.6453 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 3.5566 A
T1  - O1  - T1  - O2  - T1  = 135.000 deg; T1  -- T1  = 5.2311 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 3.5566 A
T1  - O1  - T1  - O3  - T1  = 135.000 deg; T1  -- T1  = 4.6453 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.1248 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.1248 A
T1  - O3  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 3.6588 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 135.0000 deg
          Mean   = 107.6471 deg
          StdDev = 27.4060 deg

        T--T SUMMARY
          Range  = 2.4405 A <--> 5.2311 A
          Mean   = 4.1483 A
          StdDev = 0.8817 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 100.634 deg ; T1  -- T1   2.4405 A

T1  -- O2  -- T1  = 170.891 deg ; T1  -- T1   3.2125 A

T1  -- O3  -- T1  =  84.055 deg ; T1  -- T1   2.4405 A
T1  -- O3  -- T1  = 154.666 deg ; T1  -- T1   3.5566 A
T1  -- O3  -- T1  =  90.424 deg ; T1  -- T1   2.5872 A
T1  -- O3  -- T1  =  90.424 deg ; T1  -- T1   2.5872 A
T1  -- O3  -- T1  = 154.666 deg ; T1  -- T1   3.5566 A
T1  -- O3  -- T1  =  84.055 deg ; T1  -- T1   2.4405 A


        T-O-T SUMMARY
          Range  = 84.0551° <--> 170.8911 deg
          Mean   = 116.2268 deg
          StdDev = 34.7100 deg

        T--T SUMMARY
          Range  = 2.4405 A <--> 3.5566 A
          Mean   = 2.8527 A
          StdDev = 0.4718 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O1  = 2.1575 A
O1  -- O1  = 2.1575 A
O1  -- O3  = 1.9501 A

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 oxygen-bridged T-atoms within 3.50 A
  T1  -- T1  = 2.4405 Angstrom
  T1  -- T1  = 2.4405 Angstrom
  T1  -- T1  = 3.2125 Angstrom
  T1  -- T1  = 2.5872 Angstrom
  T1  -- T1  = 2.5872 Angstrom