Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_205_1_76_wdrw5K.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.8764 Angstrom
T1  -- O1  = 1.7366 Angstrom
T1  -- O2  = 1.6636 Angstrom
T1  -- O2  = 1.6551 Angstrom
T1  -- O1  = 1.6998 Angstrom
      mean = 1.7263 Angstrom

        T-O SUMMARY
          Range  = 1.6551 A <--> 1.8764 A
          Mean   = 1.7263 A
          StdDev = 0.0807 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  91.701 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  =  97.801 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 153.291 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  =  92.872 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 122.351 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  =  75.061 deg; O1  -- O2  = 2 A
O1  -- T1  -- O1  = 104.981 deg; O1  -- O1  = 3 A
O2  -- T1  -- O2  =  71.537 deg; O2  -- O2  = 2 A
O2  -- T1  -- O1  = 130.865 deg; O2  -- O1  = 3 A
O2  -- T1  -- O1  = 112.767 deg; O2  -- O1  = 3 A
       71.537 deg <-- 105.323 deg --> 153.291 deg

        O-T-O SUMMARY
          Range  = 71.5374 deg <--> 153.2909 deg
          Mean   = 105.3228 deg
          StdDev = 24.0359 deg

        O--O SUMMARY
          Range  = 1.9398 A <--> 3.4364 A
          Mean   = 2.6861 A
          StdDev = 0.4202 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  86.701 deg ; T1  -- T1   2.4583 A
T1  -- O1  -- T1  =  85.658 deg ; T1  -- T1   2.4583 A
T1  -- O1  -- T1  = 132.151 deg ; T1  -- T1   3.1412 A

T1  -- O2  -- T1  = 172.403 deg ; T1  -- T1   3.3114 A


        T-O-T SUMMARY
          Range  = 85.6582° <--> 172.4031 deg
          Mean   = 119.2283 deg
          StdDev = 36.1735 deg

        T--T SUMMARY
          Range  = 2.4583 A <--> 3.3114 A
          Mean   = 2.8423 A
          StdDev = 0.3907 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 2.0672 A
O2  -- O2  = 1.9398 A
O2  -- O2  = 1.9398 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 3.1412 Angstrom
  T1  -- T1  = 3.3114 Angstrom
  T1  -- T1  = 2.4583 Angstrom
  T1  -- T1  = 2.4583 Angstrom
  T1  -- T1  = 3.3114 Angstrom
  T1  -- T1  = 3.1412 Angstrom