Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_203-2_1_230_Rp8gS3.cif"

There are 96 T-atoms per unit cell
There are 192 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6669 Angstrom
T1  -- O1  = 1.7549 Angstrom
T1  -- O2  = 1.5010 Angstrom
T1  -- O2  = 2.0292 Angstrom
T1  -- O2  = 1.8040 Angstrom
      mean = 1.7512 Angstrom

        T-O SUMMARY
          Range  = 1.5010 A <--> 2.0292 A
          Mean   = 1.7512 A
          StdDev = 0.1733 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  66.762 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  = 160.948 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 100.727 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  =  61.116 deg; O1  -- O2  = 2 A
O1  -- T1  -- O2  =  98.741 deg; O1  -- O2  = 2 A
O1  -- T1  -- O2  = 141.978 deg; O1  -- O2  = 4 A
O1  -- T1  -- O2  = 115.466 deg; O1  -- O2  = 3 A
O2  -- T1  -- O2  =  83.015 deg; O2  -- O2  = 2 A
O2  -- T1  -- O2  = 137.902 deg; O2  -- O2  = 3 A
O2  -- T1  -- O2  =  84.245 deg; O2  -- O2  = 3 A
       61.116 deg <-- 105.090 deg --> 160.948 deg

        O-T-O SUMMARY
          Range  = 61.1161 deg <--> 160.9477 deg
          Mean   = 105.0901 deg
          StdDev = 31.7167 deg

        O--O SUMMARY
          Range  = 1.7686 A <--> 3.5788 A
          Mean   = 2.6733 A
          StdDev = 0.5407 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  = 120.000 deg; T1  -- T1  = 4.5360 A
T1  - O1  - T1  - O2  - T1  = 102.744 deg; T1  -- T1  = 3.7826 A
T1  - O1  - T1  - O2  - T1  = 120.000 deg; T1  -- T1  = 4.5360 A
T1  - O1  - T1  - O2  - T1  = 102.744 deg; T1  -- T1  = 3.7826 A
T1  - O1  - T1  - O2  - T1  =  77.256 deg; T1  -- T1  = 3.7826 A
T1  - O1  - T1  - O2  - T1  =  60.000 deg; T1  -- T1  = 3.2167 A
T1  - O1  - T1  - O2  - T1  = 129.979 deg; T1  -- T1  = 5.4755 A
T1  - O2  - T1  - O2  - T1  = 129.979 deg; T1  -- T1  = 5.4755 A
T1  - O2  - T1  - O2  - T1  = 119.332 deg; T1  -- T1  = 4.8723 A
T1  - O2  - T1  - O2  - T1  =  77.256 deg; T1  -- T1  = 3.7826 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 129.9786 deg
          Mean   = 103.9289 deg
          StdDev = 23.3926 deg

        T--T SUMMARY
          Range  = 3.2167 A <--> 5.4755 A
          Mean   = 4.3243 A
          StdDev = 0.7380 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 140.108 deg ; T1  -- T1   3.2167 A

T1  -- O2  -- T1  =  65.934 deg ; T1  -- T1   1.9714 A
T1  -- O2  -- T1  = 117.010 deg ; T1  -- T1   2.8226 A
T1  -- O2  -- T1  = 161.336 deg ; T1  -- T1   3.7826 A


        T-O-T SUMMARY
          Range  = 65.9338° <--> 161.3355 deg
          Mean   = 121.0970 deg
          StdDev = 35.5437 deg

        T--T SUMMARY
          Range  = 1.9714 A <--> 3.7826 A
          Mean   = 2.9483 A
          StdDev = 0.6601 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O1  = 1.8842 A
O1  -- O1  = 1.8842 A
O1  -- O2  = 1.7686 A

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 oxygen-bridged T-atoms within 3.50 A
  T1  -- T1  = 1.9714 Angstrom
  T1  -- T1  = 3.2167 Angstrom
  T1  -- T1  = 2.8226 Angstrom
  T1  -- T1  = 3.2167 Angstrom
  T1  -- T1  = 2.8226 Angstrom