Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_200_1_7_ezIcNp.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 23.30 T-atoms per nm^3
Material density = 2.325 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.7068 Angstrom
T1  -- O1  = 1.7068 Angstrom
T1  -- O1  = 1.0625 Angstrom
T1  -- O2  = 1.7276 Angstrom
T1  -- O3  = 1.7236 Angstrom
      mean = 1.5854 Angstrom

        T-O SUMMARY
          Range  = 1.0625 A <--> 1.7276 A
          Mean   = 1.5854 A
          StdDev = 0.2627 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  23.732 deg; O1  -- O1  = 1 A
O1  -- T1  -- O1  =  11.867 deg; O1  -- O1  = 1 A
O1  -- T1  -- O2  = 125.811 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 118.789 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  =  11.867 deg; O1  -- O1  = 1 A
O1  -- T1  -- O2  = 111.215 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 118.791 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 119.070 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  = 119.308 deg; O1  -- O3  = 2 A
O2  -- T1  -- O3  = 111.070 deg; O2  -- O3  = 3 A
       11.867 deg <-- 87.152 deg --> 125.811 deg

        O-T-O SUMMARY
          Range  = 11.8675 deg <--> 125.8114 deg
          Mean   = 85.8933 deg
          StdDev = 47.9612 deg

        O--O SUMMARY
          Range  = 0.7019 A <--> 3.0575 A
          Mean   = 2.1243 A
          StdDev = 0.9895 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  60.000 deg; T1  -- T1  = 2.5421 A
T1  - O1  - T1  - O1  - T1  = 135.000 deg; T1  -- T1  = 5.2407 A
T1  - O1  - T1  - O2  - T1  = 135.000 deg; T1  -- T1  = 5.4789 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.2278 A
T1  - O1  - T1  - O1  - T1  = 135.000 deg; T1  -- T1  = 5.2407 A
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.2278 A
T1  - O1  - T1  - O3  - T1  = 135.000 deg; T1  -- T1  = 5.4789 A
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.6021 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.6021 A
T1  - O2  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.7774 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 135.0000 deg
          Mean   = 105.7895 deg
          StdDev = 26.4790 deg

        T--T SUMMARY
          Range  = 2.5421 A <--> 5.4789 A
          Mean   = 4.6347 A
          StdDev = 0.8530 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 131.861 deg ; T1  -- T1   2.5421 A
T1  -- O1  -- T1  =  96.266 deg ; T1  -- T1   2.5421 A
T1  -- O1  -- T1  = 131.861 deg ; T1  -- T1   2.5421 A

T1  -- O2  -- T1  = 155.750 deg ; T1  -- T1   3.3781 A

T1  -- O3  -- T1  = 130.088 deg ; T1  -- T1   3.1253 A


        T-O-T SUMMARY
          Range  = 96.2655° <--> 155.7504 deg
          Mean   = 129.1651 deg
          StdDev = 19.0773 deg

        T--T SUMMARY
          Range  = 2.5421 A <--> 3.3781 A
          Mean   = 2.8259 A
          StdDev = 0.3582 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O1  = 0.7019 A
O1  -- O1  = 0.7019 A

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 oxygen-bridged T-atoms within 3.50 A
  T1  -- T1  = 2.5421 Angstrom
  T1  -- T1  = 2.5421 Angstrom
  T1  -- T1  = 3.1253 Angstrom
  T1  -- T1  = 3.3781 Angstrom
  T1  -- T1  = 3.3781 Angstrom