Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_19_2_1795_NVnGHS.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 21.78 T-atoms per nm^3
Material density = 2.173 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6202 Angstrom
T1  -- O2  = 1.6212 Angstrom
T1  -- O3  = 1.6212 Angstrom
T1  -- O4  = 1.6212 Angstrom
      mean = 1.6210 Angstrom
        t1 = 0.006816  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000471  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O1  = 1.6201 Angstrom
T2  -- O3  = 1.6213 Angstrom
T2  -- O4  = 1.6214 Angstrom
T2  -- O2  = 1.6212 Angstrom
      mean = 1.6210 Angstrom
        t1 = 0.006851  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000716  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6201 A <--> 1.6214 A
          Mean   = 1.6210 A
          StdDev = 0.0005 A

       t1 Range  = 0.0068 <-- 0.0068 --> 0.0069
       t2 Range  = 0.0005 <-- 0.0006 --> 0.0007

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.439 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.398 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.600 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.425 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.465 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.499 deg; O3  -- O4  = 3 A
       109.398 deg <-- 109.471 deg --> 109.600 deg

O1  -- T2  -- O3  = 109.603 deg; O1  -- O3  = 3 A
O1  -- T2  -- O4  = 109.335 deg; O1  -- O4  = 3 A
O1  -- T2  -- O2  = 109.464 deg; O1  -- O2  = 3 A
O3  -- T2  -- O4  = 109.488 deg; O3  -- O4  = 3 A
O3  -- T2  -- O2  = 109.467 deg; O3  -- O2  = 3 A
O4  -- T2  -- O2  = 109.470 deg; O4  -- O2  = 3 A
       109.335 deg <-- 109.471 deg --> 109.603 deg

        O-T-O SUMMARY
          Range  = 109.3349 deg <--> 109.6033 deg
          Mean   = 109.4712 deg
          StdDev = 0.0728 deg

        O--O SUMMARY
          Range  = 2.6444 A <--> 2.6488 A
          Mean   = 2.6470 A
          StdDev = 0.0013 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  = 136.272 deg; T2  -- T2  = 5.6533 A
T2  - O1  - T1  - O3  - T2  = 111.752 deg; T2  -- T2  = 5.0421 A
T2  - O1  - T1  - O4  - T2  = 106.491 deg; T2  -- T2  = 4.8804 A
T2  - O2  - T1  - O3  - T2  =  89.995 deg; T2  -- T2  = 4.2812 A
T2  - O2  - T1  - O4  - T2  = 111.127 deg; T2  -- T2  = 4.9942 A
T2  - O3  - T1  - O4  - T2  =  90.000 deg; T2  -- T2  = 4.2812 A

T1  - O1  - T2  - O3  - T1  =  92.264 deg; T1  -- T1  = 4.3917 A
T1  - O1  - T2  - O4  - T1  = 148.021 deg; T1  -- T1  = 5.8550 A
T1  - O1  - T2  - O2  - T1  = 118.576 deg; T1  -- T1  = 5.2370 A
T1  - O3  - T2  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2814 A
T1  - O3  - T2  - O2  - T1  = 111.127 deg; T1  -- T1  = 4.9942 A
T1  - O4  - T2  - O2  - T1  =  90.005 deg; T1  -- T1  = 4.2814 A

        T-T-T SUMMARY
          Range  = 89.9954 deg <--> 148.0212 deg
          Mean   = 107.9692 deg
          StdDev = 18.6624 deg

        T--T SUMMARY
          Range  = 4.2812 A <--> 5.8550 A
          Mean   = 4.8478 A
          StdDev = 0.5370 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T2  = 141.996 deg ; T1  -- T2   3.0637 A

T1  -- O2  -- T2  = 138.048 deg ; T1  -- T2   3.0276 A

T1  -- O3  -- T2  = 138.065 deg ; T1  -- T2   3.0278 A

T1  -- O4  -- T2  = 137.976 deg ; T1  -- T2   3.0270 A


        T-O-T SUMMARY
          Range  = 137.9760° <--> 141.9962 deg
          Mean   = 139.0212 deg
          StdDev = 1.7743 deg

        T--T SUMMARY
          Range  = 3.0270 A <--> 3.0637 A
          Mean   = 3.0365 A
          StdDev = 0.0162 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000