Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_19_2_1779_QRKr_3.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 22.41 T-atoms per nm^3
Material density = 2.236 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6212 Angstrom
T1  -- O3  = 1.6212 Angstrom
T1  -- O4  = 1.6211 Angstrom
T1  -- O2  = 1.6211 Angstrom
      mean = 1.6211 Angstrom
        t1 = 0.006926  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000095  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O1  = 1.6212 Angstrom
T2  -- O2  = 1.6211 Angstrom
T2  -- O4  = 1.6211 Angstrom
T2  -- O3  = 1.6212 Angstrom
      mean = 1.6211 Angstrom
        t1 = 0.006919  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000096  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6211 A <--> 1.6212 A
          Mean   = 1.6211 A
          StdDev = 0.0001 A

       t1 Range  = 0.0069 <-- 0.0069 --> 0.0069
       t2 Range  = 0.0001 <-- 0.0001 --> 0.0001

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 109.471 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.469 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 109.472 deg; O1  -- O2  = 3 A
O3  -- T1  -- O4  = 109.511 deg; O3  -- O4  = 3 A
O3  -- T1  -- O2  = 109.473 deg; O3  -- O2  = 3 A
O4  -- T1  -- O2  = 109.432 deg; O4  -- O2  = 3 A
       109.432 deg <-- 109.471 deg --> 109.511 deg

O1  -- T2  -- O2  = 109.472 deg; O1  -- O2  = 3 A
O1  -- T2  -- O4  = 109.459 deg; O1  -- O4  = 3 A
O1  -- T2  -- O3  = 109.472 deg; O1  -- O3  = 3 A
O2  -- T2  -- O4  = 109.519 deg; O2  -- O4  = 3 A
O2  -- T2  -- O3  = 109.457 deg; O2  -- O3  = 3 A
O4  -- T2  -- O3  = 109.448 deg; O4  -- O3  = 3 A
       109.448 deg <-- 109.471 deg --> 109.519 deg

        O-T-O SUMMARY
          Range  = 109.4320 deg <--> 109.5192 deg
          Mean   = 109.4712 deg
          StdDev = 0.0232 deg

        O--O SUMMARY
          Range  = 2.6466 A <--> 2.6480 A
          Mean   = 2.6473 A
          StdDev = 0.0004 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O3  - T2  = 106.631 deg; T2  -- T2  = 4.8550 A
T2  - O1  - T1  - O4  - T2  =  90.002 deg; T2  -- T2  = 4.2784 A
T2  - O1  - T1  - O2  - T2  = 111.123 deg; T2  -- T2  = 4.9913 A
T2  - O3  - T1  - O4  - T2  = 109.827 deg; T2  -- T2  = 4.9526 A
T2  - O3  - T1  - O2  - T2  = 137.116 deg; T2  -- T2  = 5.6349 A
T2  - O4  - T1  - O2  - T2  =  90.005 deg; T2  -- T2  = 4.2784 A

T1  - O1  - T2  - O2  - T1  = 117.552 deg; T1  -- T1  = 5.1771 A
T1  - O1  - T2  - O4  - T1  =  89.995 deg; T1  -- T1  = 4.2782 A
T1  - O1  - T2  - O3  - T1  = 111.123 deg; T1  -- T1  = 4.9913 A
T1  - O2  - T2  - O4  - T1  = 149.852 deg; T1  -- T1  = 5.8441 A
T1  - O2  - T2  - O3  - T1  =  90.920 deg; T1  -- T1  = 4.3150 A
T1  - O4  - T2  - O3  - T1  =  89.998 deg; T1  -- T1  = 4.2782 A

        T-T-T SUMMARY
          Range  = 89.9948 deg <--> 149.8519 deg
          Mean   = 107.8454 deg
          StdDev = 19.1361 deg

        T--T SUMMARY
          Range  = 4.2782 A <--> 5.8441 A
          Mean   = 4.8229 A
          StdDev = 0.5337 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T2  = 137.907 deg ; T1  -- T2   3.0261 A

T1  -- O2  -- T2  = 137.911 deg ; T1  -- T2   3.0259 A

T1  -- O3  -- T2  = 137.740 deg ; T1  -- T2   3.0244 A

T1  -- O4  -- T2  = 138.112 deg ; T1  -- T2   3.0280 A


        T-O-T SUMMARY
          Range  = 137.7401° <--> 138.1120 deg
          Mean   = 137.9176 deg
          StdDev = 0.1361 deg

        T--T SUMMARY
          Range  = 3.0244 A <--> 3.0280 A
          Mean   = 3.0261 A
          StdDev = 0.0013 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 10 21 36 54 78 106 136 173 214 256 306 360 414 477 544
TD10 = 833
Circuit symbol = 4.6.4.6.6_{2}.8_{6}
Weight = 25
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 23

<TD10> = 833.000
Average ring size = 5.6000