Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_199_1_80__CGGM0.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 21.59 T-atoms per nm^3
Material density = 2.154 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6413 Angstrom
T1  -- O2  = 1.6576 Angstrom
T1  -- O3  = 1.7198 Angstrom
T1  -- O3  = 1.6493 Angstrom
      mean = 1.6670 Angstrom
        t1 = 0.143949  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.088912  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6413 A <--> 1.7198 A
          Mean   = 1.6670 A
          StdDev = 0.0312 A

       t1 Range  = 0.1439 <-- 0.1439 --> 0.1439
       t2 Range  = 0.0889 <-- 0.0889 --> 0.0889

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 132.637 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 103.213 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  = 103.243 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 111.515 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  =  73.108 deg; O2  -- O3  = 2 A
O3  -- T1  -- O3  = 135.709 deg; O3  -- O3  = 3 A
       73.108 deg <-- 109.904 deg --> 135.709 deg

        O-T-O SUMMARY
          Range  = 73.1084 deg <--> 135.7089 deg
          Mean   = 107.8378 deg
          StdDev = 20.7337 deg

        O--O SUMMARY
          Range  = 1.9695 A <--> 3.1206 A
          Mean   = 2.6559 A
          StdDev = 0.3777 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 113.979 deg; T1  -- T1  = 5.2620 A
T1  - O1  - T1  - O3  - T1  = 160.178 deg; T1  -- T1  = 5.2426 A
T1  - O1  - T1  - O3  - T1  =  70.030 deg; T1  -- T1  = 3.6110 A
T1  - O2  - T1  - O3  - T1  =  76.638 deg; T1  -- T1  = 3.6110 A
T1  - O2  - T1  - O3  - T1  = 135.564 deg; T1  -- T1  = 6.1542 A
T1  - O3  - T1  - O3  - T1  =  90.605 deg; T1  -- T1  = 4.1055 A

        T-T-T SUMMARY
          Range  = 70.0295 deg <--> 160.1782 deg
          Mean   = 107.2736 deg
          StdDev = 33.7713 deg

        T--T SUMMARY
          Range  = 3.6110 A <--> 6.1542 A
          Mean   = 4.6101 A
          StdDev = 0.9805 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 127.670 deg ; T1  -- T1   2.9463 A

T1  -- O2  -- T1  =  91.508 deg ; T1  -- T1   2.3748 A

T1  -- O3  -- T1  = 161.215 deg ; T1  -- T1   3.3239 A


        T-O-T SUMMARY
          Range  = 91.5078° <--> 161.2152 deg
          Mean   = 126.7975 deg
          StdDev = 28.6644 deg

        T--T SUMMARY
          Range  = 2.3748 A <--> 3.3239 A
          Mean   = 2.8817 A
          StdDev = 0.3929 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O3  = 1.9695 A
O2  -- O3  = 1.9695 A
T1  -- T1  = 2.3748 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 20 40 76 116 158 220 280 342 436 516 598 724 824 926
TD10 = 1267
Circuit symbol = 4.4.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 9
Vertex symbol  = 4.4.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 9

<TD10> = 1267.000
Average ring size = 5.4545