Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_199_1_139_Tvi1ed.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 18.79 T-atoms per nm^3
Material density = 1.874 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6246 Angstrom
T1  -- O1  = 1.7146 Angstrom
T1  -- O2  = 1.3331 Angstrom
T1  -- O2  = 1.7057 Angstrom
T1  -- O2  = 1.9619 Angstrom
      mean = 1.6680 Angstrom

        T-O SUMMARY
          Range  = 1.3331 A <--> 1.9619 A
          Mean   = 1.6680 A
          StdDev = 0.2028 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  85.078 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  =  53.281 deg; O1  -- O2  = 1 A
O1  -- T1  -- O2  = 113.259 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 118.570 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 120.409 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  =  46.550 deg; O1  -- O2  = 1 A
O1  -- T1  -- O2  = 149.301 deg; O1  -- O2  = 4 A
O2  -- T1  -- O2  = 108.478 deg; O2  -- O2  = 2 A
O2  -- T1  -- O2  =  90.215 deg; O2  -- O2  = 2 A
O2  -- T1  -- O2  = 125.548 deg; O2  -- O2  = 3 A
       46.550 deg <-- 101.069 deg --> 149.301 deg

        O-T-O SUMMARY
          Range  = 46.5495 deg <--> 149.3013 deg
          Mean   = 101.0690 deg
          StdDev = 30.7872 deg

        O--O SUMMARY
          Range  = 1.3516 A <--> 3.5460 A
          Mean   = 2.5144 A
          StdDev = 0.6968 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 100.932 deg ; T1  -- T1   2.5760 A

T1  -- O2  -- T1  = 115.380 deg ; T1  -- T1   2.5760 A
T1  -- O2  -- T1  =  22.140 deg ; T1  -- T1   0.8838 A
T1  -- O2  -- T1  = 137.067 deg ; T1  -- T1   3.4145 A


        T-O-T SUMMARY
          Range  = 22.1396° <--> 137.0668 deg
          Mean   = 93.8795 deg
          StdDev = 43.5975 deg

        T--T SUMMARY
          Range  = 0.8838 A <--> 3.4145 A
          Mean   = 2.3626 A
          StdDev = 0.9247 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O1  = 2.2586 A
O1  -- O1  = 2.2586 A
O1  -- O2  = 1.3516 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 7 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 2.5760 Angstrom
  T1  -- T1  = 2.5760 Angstrom
  T1  -- T1  = 3.3096 Angstrom
  T1  -- T1  = 3.4145 Angstrom
  T1  -- T1  = 0.8838 Angstrom
  T1  -- T1  = 3.4145 Angstrom
  T1  -- T1  = 3.3096 Angstrom