Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_199_1_138_ezeqZW.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 31.41 T-atoms per nm^3
Material density = 3.134 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5018 Angstrom
T1  -- O1  = 1.6721 Angstrom
T1  -- O2  = 2.0148 Angstrom
T1  -- O2  = 1.7253 Angstrom
T1  -- O1  = 1.8054 Angstrom
T1  -- O2  = 1.8062 Angstrom
      mean = 1.7543 Angstrom

        T-O SUMMARY
          Range  = 1.5018 A <--> 2.0148 A
          Mean   = 1.7543 A
          StdDev = 0.1558 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  68.062 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  = 103.823 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  =  42.284 deg; O1  -- O2  = 1 A
O1  -- T1  -- O1  = 158.504 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 130.308 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  =  35.913 deg; O1  -- O2  = 1 A
O1  -- T1  -- O2  = 110.160 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  = 127.341 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 104.516 deg; O1  -- O2  = 3 A
O2  -- T1  -- O2  = 145.285 deg; O2  -- O2  = 4 A
O2  -- T1  -- O1  =  91.994 deg; O2  -- O1  = 3 A
O2  -- T1  -- O2  =  79.132 deg; O2  -- O2  = 2 A
O2  -- T1  -- O1  = 119.058 deg; O2  -- O1  = 3 A
O2  -- T1  -- O2  = 114.926 deg; O2  -- O2  = 3 A
O1  -- T1  -- O2  =  38.223 deg; O1  -- O2  = 1 A
       35.913 deg <-- 97.969 deg --> 158.504 deg

        O-T-O SUMMARY
          Range  = 35.9127 deg <--> 158.5040 deg
          Mean   = 97.9685 deg
          StdDev = 37.0887 deg

        O--O SUMMARY
          Range  = 1.1825 A <--> 3.5709 A
          Mean   = 2.5205 A
          StdDev = 0.7704 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 113.053 deg ; T1  -- T1   2.6491 A
T1  -- O1  -- T1  = 125.082 deg ; T1  -- T1   2.9380 A
T1  -- O1  -- T1  =  25.592 deg ; T1  -- T1   0.7811 A

T1  -- O2  -- T1  =  89.846 deg ; T1  -- T1   2.6491 A
T1  -- O2  -- T1  =  22.757 deg ; T1  -- T1   0.7811 A
T1  -- O2  -- T1  = 112.571 deg ; T1  -- T1   2.9380 A


        T-O-T SUMMARY
          Range  = 22.7570° <--> 125.0819 deg
          Mean   = 81.4836 deg
          StdDev = 41.9921 deg

        T--T SUMMARY
          Range  = 0.7811 A <--> 2.9380 A
          Mean   = 2.1227 A
          StdDev = 0.9593 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O1  = 1.7818 A
O1  -- O1  = 1.7818 A
O1  -- O2  = 1.1825 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 7 neighboring T-atoms within 3.50 A, but only 6 bridging O-atoms
  T1  -- T1  = 2.6491 Angstrom
  T1  -- T1  = 2.6491 Angstrom
  T1  -- T1  = 2.9380 Angstrom
  T1  -- T1  = 3.3916 Angstrom
  T1  -- T1  = 0.7811 Angstrom
  T1  -- T1  = 3.3916 Angstrom
  T1  -- T1  = 2.9380 Angstrom