Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_195_1_355_jH6IDv.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 28.45 T-atoms per nm^3
Material density = 2.838 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6982 Angstrom
T1  -- O2  = 1.6969 Angstrom
T1  -- O3  = 1.7103 Angstrom
T1  -- O3  = 1.1331 Angstrom
T1  -- O3  = 1.7120 Angstrom
      mean = 1.5901 Angstrom

        T-O SUMMARY
          Range  = 1.1331 A <--> 1.7120 A
          Mean   = 1.5901 A
          StdDev = 0.2305 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 105.228 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 128.221 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  = 119.118 deg; O1  -- O3  = 2 A
O1  -- T1  -- O3  = 108.987 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 108.721 deg; O2  -- O3  = 3 A
O2  -- T1  -- O3  = 119.029 deg; O2  -- O3  = 2 A
O2  -- T1  -- O3  = 128.057 deg; O2  -- O3  = 3 A
O3  -- T1  -- O3  =  10.814 deg; O3  -- O3  = 1 A
O3  -- T1  -- O3  =  21.354 deg; O3  -- O3  = 1 A
O3  -- T1  -- O3  =  10.658 deg; O3  -- O3  = 1 A
       10.658 deg <-- 86.019 deg --> 128.221 deg

        O-T-O SUMMARY
          Range  = 10.6582 deg <--> 128.2211 deg
          Mean   = 85.0078 deg
          StdDev = 48.8463 deg

        O--O SUMMARY
          Range  = 0.6341 A <--> 3.0664 A
          Mean   = 2.0884 A
          StdDev = 1.0122 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 163.920 deg ; T1  -- T1   3.3630 A

T1  -- O2  -- T1  = 162.489 deg ; T1  -- T1   3.3542 A

T1  -- O3  -- T1  =  98.522 deg ; T1  -- T1   2.5930 A
T1  -- O3  -- T1  = 130.452 deg ; T1  -- T1   2.5930 A
T1  -- O3  -- T1  = 130.297 deg ; T1  -- T1   2.5930 A


        T-O-T SUMMARY
          Range  = 98.5220° <--> 163.9196 deg
          Mean   = 137.1359 deg
          StdDev = 24.4643 deg

        T--T SUMMARY
          Range  = 2.5930 A <--> 3.3630 A
          Mean   = 2.8993 A
          StdDev = 0.3782 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O3  = 0.6341 A
O3  -- O3  = 0.6341 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 2.5930 Angstrom
  T1  -- T1  = 3.3196 Angstrom
  T1  -- T1  = 2.5930 Angstrom
  T1  -- T1  = 3.3196 Angstrom
  T1  -- T1  = 3.3630 Angstrom
  T1  -- T1  = 3.3542 Angstrom