Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_194_6_95047454_clYc46.cif"

There are 144 T-atoms per unit cell
There are 288 O-atoms per unit cell

Framework density = 23.31 T-atoms per nm^3
Material density = 2.325 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6117 Angstrom
T1  -- O2  = 1.5907 Angstrom
T1  -- O3  = 1.5549 Angstrom
T1  -- O4  = 1.4791 Angstrom
      mean = 1.5591 Angstrom
        t1 = 0.212130  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.205020  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.4497 Angstrom
T2  -- O5  = 1.6904 Angstrom
T2  -- O6  = 1.6977 Angstrom
T2  -- O7  = 1.6937 Angstrom
      mean = 1.6329 Angstrom
        t1 = 0.130892  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.083068  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O3  = 1.9490 Angstrom
T3  -- O4  = 1.5241 Angstrom
T3  -- O8  = 1.5981 Angstrom
T3  -- O9  = 1.5695 Angstrom
T3  -- O10 = 1.7226 Angstrom
      mean = 1.6726 Angstrom

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6898 Angstrom
T4  -- O11 = 1.5585 Angstrom
T4  -- O12 = 1.6098 Angstrom
T4  -- O13 = 1.6586 Angstrom
      mean = 1.6292 Angstrom
        t1 = 0.066810  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.042808  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.7045 Angstrom
T5  -- O14 = 1.7512 Angstrom
T5  -- O15 = 1.5667 Angstrom
T5  -- O16 = 1.6390 Angstrom
      mean = 1.6653 Angstrom
        t1 = 0.086457  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.054561  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T6  -- O13 = 1.5667 Angstrom
T6  -- O16 = 1.6544 Angstrom
T6  -- O17 = 1.6599 Angstrom
T6  -- O18 = 1.6994 Angstrom
      mean = 1.6451 Angstrom
        t1 = 0.073405  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.064110  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4497 A <--> 1.9490 A
          Mean   = 1.6356 A
          StdDev = 0.0991 A

       t1 Range  = 0.0668 <-- 0.0949 --> 0.2121
       t2 Range  = 0.0428 <-- 0.0749 --> 0.2050

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.483 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 133.176 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  70.377 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 100.782 deg; O2  -- O3  = 2 A
O2  -- T1  -- O4  = 113.629 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  64.270 deg; O3  -- O4  = 2 A
       64.270 deg <-- 98.286 deg --> 133.176 deg

O3  -- T2  -- O5  =  98.030 deg; O3  -- O5  = 2 A
O3  -- T2  -- O6  = 111.563 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  =  78.789 deg; O3  -- O7  = 2 A
O5  -- T2  -- O6  = 117.272 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 123.687 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 115.809 deg; O6  -- O7  = 3 A
       78.789 deg <-- 107.525 deg --> 123.687 deg

O3  -- T3  -- O4  =  53.751 deg; O3  -- O4  = 2 A
O3  -- T3  -- O8  =  91.853 deg; O3  -- O8  = 3 A
O3  -- T3  -- O9  =  90.071 deg; O3  -- O9  = 3 A
O3  -- T3  -- O10 = 149.769 deg; O3  -- O10 = 4 A
O4  -- T3  -- O8  = 119.703 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 115.212 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 =  96.372 deg; O4  -- O10 = 2 A
O8  -- T3  -- O9  = 111.934 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 101.226 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.541 deg; O9  -- O10 = 3 A
       53.751 deg <-- 103.943 deg --> 149.769 deg

O7  -- T4  -- O11 = 102.097 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 109.366 deg; O7  -- O12 = 3 A
O7  -- T4  -- O13 = 126.262 deg; O7  -- O13 = 3 A
O11 -- T4  -- O12 = 110.953 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 =  97.819 deg; O11 -- O13 = 2 A
O12 -- T4  -- O13 = 108.921 deg; O12 -- O13 = 3 A
       97.819 deg <-- 109.236 deg --> 126.262 deg

O10 -- T5  -- O14 = 124.993 deg; O10 -- O14 = 3 A
O10 -- T5  -- O15 = 105.929 deg; O10 -- O15 = 3 A
O10 -- T5  -- O16 = 102.669 deg; O10 -- O16 = 3 A
O14 -- T5  -- O15 = 100.668 deg; O14 -- O15 = 3 A
O14 -- T5  -- O16 = 118.916 deg; O14 -- O16 = 3 A
O15 -- T5  -- O16 = 100.118 deg; O15 -- O16 = 2 A
       100.118 deg <-- 108.882 deg --> 124.993 deg

O13 -- T6  -- O16 =  93.791 deg; O13 -- O16 = 2 A
O13 -- T6  -- O17 = 100.341 deg; O13 -- O17 = 2 A
O13 -- T6  -- O18 = 117.103 deg; O13 -- O18 = 3 A
O16 -- T6  -- O17 = 114.840 deg; O16 -- O17 = 3 A
O16 -- T6  -- O18 = 112.454 deg; O16 -- O18 = 3 A
O17 -- T6  -- O18 = 115.855 deg; O17 -- O18 = 3 A
       93.791 deg <-- 109.064 deg --> 117.103 deg

        O-T-O SUMMARY
          Range  = 53.7512 deg <--> 149.7694 deg
          Mean   = 105.5490 deg
          StdDev = 18.1971 deg

        O--O SUMMARY
          Range  = 1.6151 A <--> 3.5450 A
          Mean   = 2.5831 A
          StdDev = 0.3714 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 129.101 deg ; T1  -- T1   2.9106 A

T1  -- O2  -- T1  = 163.654 deg ; T1  -- T1   3.1490 A

T1  -- O3  -- T2  = 131.611 deg ; T1  -- T2   2.7410 A
T1  -- O3  -- T3  =  94.851 deg ; T1  -- T3   2.5940 A
T2  -- O3  -- T3  = 132.233 deg ; T2  -- T3   3.1142 A

T1  -- O4  -- T3  = 119.472 deg ; T1  -- T3   2.5940 A

T2  -- O5  -- T2  = 164.315 deg ; T2  -- T2   3.3492 A

T2  -- O6  -- T2  = 169.474 deg ; T2  -- T2   3.3810 A

T2  -- O7  -- T4  = 123.440 deg ; T2  -- T4   2.9797 A

T3  -- O8  -- T3  = 165.368 deg ; T3  -- T3   3.1702 A

T3  -- O9  -- T3  = 139.396 deg ; T3  -- T3   2.9439 A

T3  -- O10 -- T5  = 141.324 deg ; T3  -- T5   3.2337 A

T4  -- O11 -- T4  = 140.051 deg ; T4  -- T4   2.9296 A

T4  -- O12 -- T4  = 123.964 deg ; T4  -- T4   2.8422 A

T4  -- O13 -- T6  = 135.741 deg ; T4  -- T6   2.9879 A

T5  -- O14 -- T5  = 140.652 deg ; T5  -- T5   3.2979 A

T5  -- O15 -- T5  = 144.613 deg ; T5  -- T5   2.9852 A

T5  -- O16 -- T6  = 147.419 deg ; T5  -- T6   3.1611 A

T6  -- O17 -- T6  = 173.873 deg ; T6  -- T6   3.3151 A

T6  -- O18 -- T6  = 156.254 deg ; T6  -- T6   3.3262 A


        T-O-T SUMMARY
          Range  = 94.8513° <--> 173.8732 deg
          Mean   = 141.8403 deg
          StdDev = 19.1831 deg

        T--T SUMMARY
          Range  = 2.5940 A <--> 3.3810 A
          Mean   = 3.0503 A
          StdDev = 0.2342 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O4  = 1.7844 A
O1  -- O4  = 1.7844 A
O3  -- O4  = 1.6151 A
O3  -- O7  = 2.0039 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 3.1490 Angstrom
  T1  -- T2  = 2.7410 Angstrom
  T1  -- T3  = 2.5940 Angstrom
  T1  -- T4  = 3.4564 Angstrom
  T1  -- T1  = 2.9106 Angstrom
T2  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 2.7410 Angstrom
  T2  -- T2  = 2.9223 Angstrom
  T2  -- T2  = 3.3492 Angstrom
  T2  -- T2  = 3.3810 Angstrom
  T2  -- T3  = 3.1142 Angstrom
  T2  -- T4  = 2.9797 Angstrom
T3  has 5 oxygen-bridged T-atoms within 3.50 A
  T3  -- T1  = 2.5940 Angstrom
  T3  -- T2  = 3.1142 Angstrom
  T3  -- T3  = 3.1702 Angstrom
  T3  -- T3  = 2.9439 Angstrom
  T3  -- T5  = 3.2337 Angstrom
T4  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T1  = 3.4564 Angstrom
  T4  -- T2  = 2.9797 Angstrom
  T4  -- T4  = 2.9296 Angstrom
  T4  -- T4  = 2.8422 Angstrom
  T4  -- T6  = 2.9879 Angstrom