Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_194_6_94882103_ydXga9.cif"

There are 144 T-atoms per unit cell
There are 288 O-atoms per unit cell

Framework density = 21.80 T-atoms per nm^3
Material density = 2.175 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5407 Angstrom
T1  -- O2  = 1.6535 Angstrom
T1  -- O3  = 1.6675 Angstrom
T1  -- O4  = 1.5114 Angstrom
      mean = 1.5933 Angstrom
        t1 = 0.072448  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.046418  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6628 Angstrom
T2  -- O5  = 1.6867 Angstrom
T2  -- O6  = 1.6303 Angstrom
T2  -- O7  = 1.6790 Angstrom
      mean = 1.6647 Angstrom
        t1 = 0.064245  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.061286  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.5789 Angstrom
T3  -- O8  = 1.7396 Angstrom
T3  -- O9  = 1.5034 Angstrom
T3  -- O6  = 1.6662 Angstrom
      mean = 1.6220 Angstrom
        t1 = 0.086706  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.107630  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O11 = 1.4981 Angstrom
T4  -- O12 = 1.5531 Angstrom
T4  -- O7  = 1.6873 Angstrom
T4  -- O10 = 1.7145 Angstrom
T4  -- O12 = 1.7435 Angstrom
      mean = 1.6393 Angstrom

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O8  = 1.6294 Angstrom
T5  -- O11 = 1.4115 Angstrom
T5  -- O12 = 1.6959 Angstrom
T5  -- O13 = 1.6346 Angstrom
      mean = 1.5928 Angstrom
        t1 = 0.129725  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.130311  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T6  -- O9  = 1.5690 Angstrom
T6  -- O14 = 1.6073 Angstrom
T6  -- O15 = 1.6128 Angstrom
T6  -- O16 = 1.6069 Angstrom
      mean = 1.5990 Angstrom
        t1 = 0.013754  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008613  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4115 A <--> 1.7435 A
          Mean   = 1.6194 A
          StdDev = 0.0810 A

       t1 Range  = 0.0138 <-- 0.0611 --> 0.1297
       t2 Range  = 0.0086 <-- 0.0590 --> 0.1303

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.283 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.917 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  94.957 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 120.931 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 112.412 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.214 deg; O3  -- O4  = 3 A
       94.957 deg <-- 108.952 deg --> 120.931 deg

O3  -- T2  -- O5  = 104.436 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  =  98.476 deg; O3  -- O6  = 2 A
O3  -- T2  -- O7  = 120.664 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 118.236 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 112.353 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 102.717 deg; O6  -- O7  = 3 A
       98.476 deg <-- 109.480 deg --> 120.664 deg

O4  -- T3  -- O8  = 105.289 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  =  93.704 deg; O4  -- O9  = 2 A
O4  -- T3  -- O6  = 116.208 deg; O4  -- O6  = 3 A
O8  -- T3  -- O9  = 112.932 deg; O8  -- O9  = 3 A
O8  -- T3  -- O6  = 122.169 deg; O8  -- O6  = 3 A
O9  -- T3  -- O6  = 102.995 deg; O9  -- O6  = 2 A
       93.704 deg <-- 108.883 deg --> 122.169 deg

O11 -- T4  -- O12 =  99.239 deg; O11 -- O12 = 2 A
O11 -- T4  -- O7  =  69.720 deg; O11 -- O7  = 2 A
O11 -- T4  -- O10 =  97.783 deg; O11 -- O10 = 2 A
O11 -- T4  -- O12 = 129.934 deg; O11 -- O12 = 3 A
O12 -- T4  -- O7  = 130.419 deg; O12 -- O7  = 3 A
O12 -- T4  -- O10 = 120.994 deg; O12 -- O10 = 3 A
O12 -- T4  -- O12 = 100.248 deg; O12 -- O12 = 3 A
O7  -- T4  -- O10 = 108.496 deg; O7  -- O10 = 3 A
O7  -- T4  -- O12 =  62.515 deg; O7  -- O12 = 2 A
O10 -- T4  -- O12 = 110.365 deg; O10 -- O12 = 3 A
       62.515 deg <-- 102.971 deg --> 130.419 deg

O8  -- T5  -- O11 =  83.277 deg; O8  -- O11 = 2 A
O8  -- T5  -- O12 = 125.336 deg; O8  -- O12 = 3 A
O8  -- T5  -- O13 = 117.615 deg; O8  -- O13 = 3 A
O11 -- T5  -- O12 =  96.415 deg; O11 -- O12 = 2 A
O11 -- T5  -- O13 = 101.319 deg; O11 -- O13 = 2 A
O12 -- T5  -- O13 = 115.968 deg; O12 -- O13 = 3 A
       83.277 deg <-- 106.655 deg --> 125.336 deg

O9  -- T6  -- O14 = 107.394 deg; O9  -- O14 = 3 A
O9  -- T6  -- O15 = 111.355 deg; O9  -- O15 = 3 A
O9  -- T6  -- O16 = 108.770 deg; O9  -- O16 = 3 A
O14 -- T6  -- O15 = 110.336 deg; O14 -- O15 = 3 A
O14 -- T6  -- O16 = 110.708 deg; O14 -- O16 = 3 A
O15 -- T6  -- O16 = 108.279 deg; O15 -- O16 = 3 A
       107.394 deg <-- 109.474 deg --> 111.355 deg

        O-T-O SUMMARY
          Range  = 62.5153 deg <--> 130.4194 deg
          Mean   = 107.1599 deg
          StdDev = 14.0356 deg

        O--O SUMMARY
          Range  = 1.7808 A <--> 2.9814 A
          Mean   = 2.5939 A
          StdDev = 0.2888 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 143.120 deg; T1  -- T2  = 5.8115 A
T1  - O1  - T1  - O3  - T3  = 125.412 deg; T1  -- T3  = 5.0361 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2474 A
T2  - O2  - T1  - O3  - T3  =  91.392 deg; T2  -- T3  = 4.2523 A
T2  - O2  - T1  - O4  - T1  =  91.351 deg; T2  -- T1  = 4.4820 A
T3  - O3  - T1  - O4  - T1  =  84.727 deg; T3  -- T1  = 3.9194 A

T1  - O3  - T2  - O5  - T2  =  97.811 deg; T1  -- T2  = 4.7417 A
T1  - O3  - T2  - O6  - T3  =  77.487 deg; T1  -- T3  = 3.9194 A
T1  - O3  - T2  - O7  - T4  = 117.568 deg; T1  -- T4  = 5.5543 A
T2  - O5  - T2  - O6  - T3  = 155.312 deg; T2  -- T3  = 6.0252 A
T2  - O5  - T2  - O7  - T4  = 126.044 deg; T2  -- T4  = 5.7054 A
T3  - O6  - T2  - O7  - T4  =  76.049 deg; T3  -- T4  = 3.9286 A

T1  - O4  - T3  - O8  - T5  = 104.927 deg; T1  -- T5  = 4.5989 A
T1  - O4  - T3  - O9  - T6  =  94.719 deg; T1  -- T6  = 4.0543 A
T1  - O4  - T3  - O6  - T2  = 101.012 deg; T1  -- T2  = 4.4820 A
T5  - O8  - T3  - O9  - T6  = 127.523 deg; T5  -- T6  = 5.2393 A
T5  - O8  - T3  - O6  - T2  =  83.855 deg; T5  -- T2  = 4.0959 A
T6  - O9  - T3  - O6  - T2  = 139.604 deg; T6  -- T2  = 5.4883 A

T4  - O11 - T4  - O12 - T5  =  87.578 deg; T4  -- T5  = 3.6853 A
T4  - O11 - T4  - O7  - T2  = 105.113 deg; T4  -- T2  = 5.1703 A
T4  - O11 - T4  - O10 - T4  = 150.000 deg; T4  -- T4  = 5.1542 A
T4  - O11 - T4  - O12 - T5  = 145.643 deg; T4  -- T5  = 6.1747 A
T5  - O12 - T4  - O7  - T2  =  99.212 deg; T5  -- T2  = 4.0959 A
T5  - O12 - T4  - O10 - T4  = 106.062 deg; T5  -- T4  = 3.2534 A
T5  - O12 - T4  - O12 - T5  = 126.435 deg; T5  -- T5  = 4.6836 A
T2  - O7  - T4  - O10 - T4  =  99.008 deg; T2  -- T4  = 4.1930 A
T2  - O7  - T4  - O12 - T5  =  68.349 deg; T2  -- T5  = 3.6825 A
T4  - O10 - T4  - O12 - T5  =  35.205 deg; T4  -- T5  = 1.9518 A

T3  - O8  - T5  - O11 - T4  = 100.872 deg; T3  -- T4  = 3.9286 A
T3  - O8  - T5  - O12 - T5  = 103.269 deg; T3  -- T5  = 4.7874 A
T3  - O8  - T5  - O13 - T4  = 106.668 deg; T3  -- T4  = 5.0664 A
T4  - O11 - T5  - O12 - T5  =  92.422 deg; T4  -- T5  = 3.6853 A
T4  - O11 - T5  - O13 - T4  =  38.734 deg; T4  -- T4  = 2.1183 A
T5  - O12 - T5  - O13 - T4  = 126.103 deg; T5  -- T4  = 5.6150 A

T3  - O9  - T6  - O14 - T6  = 115.247 deg; T3  -- T6  = 4.8151 A
T3  - O9  - T6  - O15 - T6  = 126.488 deg; T3  -- T6  = 4.9776 A
T3  - O9  - T6  - O16 - T6  = 107.031 deg; T3  -- T6  = 4.5032 A
T6  - O14 - T6  - O15 - T6  =  90.000 deg; T6  -- T6  = 4.0445 A
T6  - O14 - T6  - O16 - T6  =  90.000 deg; T6  -- T6  = 4.0628 A
T6  - O15 - T6  - O16 - T6  = 120.000 deg; T6  -- T6  = 4.8658 A

        T-T-T SUMMARY
          Range  = 35.2049 deg <--> 155.3116 deg
          Mean   = 103.8366 deg
          StdDev = 26.0722 deg

        T--T SUMMARY
          Range  = 1.9518 A <--> 6.1747 A
          Mean   = 4.4922 A
          StdDev = 0.9091 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 170.962 deg ; T1  -- T1   3.0718 A

T1  -- O2  -- T1  = 124.985 deg ; T1  -- T1   2.9332 A

T1  -- O3  -- T2  = 146.883 deg ; T1  -- T2   3.1922 A

T1  -- O4  -- T3  = 124.320 deg ; T1  -- T3   2.7329 A

T2  -- O5  -- T2  = 133.476 deg ; T2  -- T2   3.0992 A

T2  -- O6  -- T3  = 137.139 deg ; T2  -- T3   3.0686 A

T2  -- O7  -- T4  = 157.577 deg ; T2  -- T4   3.3020 A

T3  -- O8  -- T5  = 130.610 deg ; T3  -- T5   3.0612 A

T3  -- O9  -- T6  = 129.446 deg ; T3  -- T6   2.7783 A

T4  -- O10 -- T4  = 138.803 deg ; T4  -- T4   3.2097 A

T4  -- O11 -- T5  =  84.199 deg ; T4  -- T5   1.9518 A

T4  -- O12 -- T5  =  73.696 deg ; T4  -- T5   1.9518 A
T4  -- O12 -- T4  =  79.740 deg ; T4  -- T4   2.1183 A
T4  -- O12 -- T5  = 142.131 deg ; T4  -- T5   3.2534 A

T5  -- O13 -- T5  = 137.291 deg ; T5  -- T5   3.0447 A

T6  -- O14 -- T6  = 130.757 deg ; T6  -- T6   2.9224 A

T6  -- O15 -- T6  = 120.182 deg ; T6  -- T6   2.7961 A

T6  -- O16 -- T6  = 122.860 deg ; T6  -- T6   2.8225 A


        T-O-T SUMMARY
          Range  = 73.6962° <--> 170.9622 deg
          Mean   = 126.9476 deg
          StdDev = 24.6327 deg

        T--T SUMMARY
          Range  = 1.9518 A <--> 3.3020 A
          Mean   = 2.8506 A
          StdDev = 0.4114 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O4  = 2.2496 A
O1  -- O4  = 2.2496 A
O4  -- O9  = 2.2495 A
O7  -- O12 = 1.7808 A
O7  -- O11 = 1.8273 A
O8  -- O11 = 2.0270 A
T1  -- T3  = 2.7329 Angstrom
T3  -- T1  = 2.7329 Angstrom
T3  -- T6  = 2.7783 Angstrom

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T4  has 5 oxygen-bridged T-atoms within 3.50 A
  T4  -- T4  = 3.2097 Angstrom
  T4  -- T5  = 1.9518 Angstrom
  T4  -- T2  = 3.3020 Angstrom
  T4  -- T4  = 2.1183 Angstrom
  T4  -- T5  = 3.2534 Angstrom
T5  -- T4  = 1.9518 Angstrom
T6  -- T3  = 2.7783 Angstrom
T6  -- T6  = 2.7961 Angstrom