Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_194_6_94261297_NVeeVA.cif"

There are 144 T-atoms per unit cell
There are 288 O-atoms per unit cell

Framework density = 25.19 T-atoms per nm^3
Material density = 2.513 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6662 Angstrom
T1  -- O2  = 1.6335 Angstrom
T1  -- O3  = 1.6100 Angstrom
T1  -- O4  = 1.5327 Angstrom
      mean = 1.6106 Angstrom
        t1 = 0.067927  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.060350  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6716 Angstrom
T2  -- O5  = 1.5898 Angstrom
T2  -- O6  = 1.6632 Angstrom
T2  -- O7  = 1.5898 Angstrom
      mean = 1.6286 Angstrom
        t1 = 0.046474  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.067821  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.5011 Angstrom
T3  -- O9  = 1.6120 Angstrom
T3  -- O8  = 1.6322 Angstrom
T3  -- O10 = 1.6528 Angstrom
      mean = 1.5995 Angstrom
        t1 = 0.028983  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.027474  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O11 = 1.6302 Angstrom
T4  -- O12 = 1.4266 Angstrom
T4  -- O13 = 2.0851 Angstrom
T4  -- O7  = 1.6035 Angstrom
T4  -- O12 = 1.7779 Angstrom
T4  -- O13 = 1.7104 Angstrom
      mean = 1.7056 Angstrom

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6464 Angstrom
T5  -- O11 = 1.3706 Angstrom
T5  -- O12 = 1.6484 Angstrom
T5  -- O14 = 1.6598 Angstrom
      mean = 1.5813 Angstrom
        t1 = 0.154266  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.136468  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T6  -- O13 = 1.6532 Angstrom
T6  -- O15 = 1.6584 Angstrom
T6  -- O16 = 1.6240 Angstrom
T6  -- O17 = 1.6291 Angstrom
      mean = 1.6412 Angstrom
        t1 = 0.032665  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021804  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.3706 A <--> 2.0851 A
          Mean   = 1.6338 A
          StdDev = 0.1213 A

       t1 Range  = 0.0290 <-- 0.0551 --> 0.1543
       t2 Range  = 0.0218 <-- 0.0523 --> 0.1365

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 110.951 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 117.164 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 113.047 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 114.945 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 106.960 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  91.973 deg; O3  -- O4  = 2 A
       91.973 deg <-- 109.173 deg --> 117.164 deg

O3  -- T2  -- O5  = 104.510 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 121.764 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 108.139 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 106.446 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 106.902 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.186 deg; O6  -- O7  = 3 A
       104.510 deg <-- 109.324 deg --> 121.764 deg

O4  -- T3  -- O9  = 111.701 deg; O4  -- O9  = 3 A
O4  -- T3  -- O8  = 107.384 deg; O4  -- O8  = 3 A
O4  -- T3  -- O10 = 106.169 deg; O4  -- O10 = 3 A
O9  -- T3  -- O8  = 109.590 deg; O9  -- O8  = 3 A
O9  -- T3  -- O10 = 112.472 deg; O9  -- O10 = 3 A
O8  -- T3  -- O10 = 109.344 deg; O8  -- O10 = 3 A
       106.169 deg <-- 109.443 deg --> 112.472 deg

O11 -- T4  -- O12 =  72.235 deg; O11 -- O12 = 2 A
O11 -- T4  -- O13 = 138.863 deg; O11 -- O13 = 3 A
O11 -- T4  -- O7  =  60.912 deg; O11 -- O7  = 2 A
O11 -- T4  -- O12 = 112.218 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 111.487 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 =  87.580 deg; O12 -- O13 = 2 A
O12 -- T4  -- O7  = 127.998 deg; O12 -- O7  = 3 A
O12 -- T4  -- O12 = 102.377 deg; O12 -- O12 = 3 A
O12 -- T4  -- O13 = 164.304 deg; O12 -- O13 = 3 A
O13 -- T4  -- O7  = 143.193 deg; O13 -- O7  = 4 A
O13 -- T4  -- O12 = 106.860 deg; O13 -- O12 = 3 A
O13 -- T4  -- O13 =  79.953 deg; O13 -- O13 = 2 A
O7  -- T4  -- O12 =  77.390 deg; O7  -- O12 = 2 A
O7  -- T4  -- O13 =  63.333 deg; O7  -- O13 = 2 A
O12 -- T4  -- O13 =  90.424 deg; O12 -- O13 = 2 A
       60.912 deg <-- 102.609 deg --> 164.304 deg

O10 -- T5  -- O11 = 101.938 deg; O10 -- O11 = 2 A
O10 -- T5  -- O12 = 122.861 deg; O10 -- O12 = 3 A
O10 -- T5  -- O14 = 114.401 deg; O10 -- O14 = 3 A
O11 -- T5  -- O12 =  72.986 deg; O11 -- O12 = 2 A
O11 -- T5  -- O14 = 101.958 deg; O11 -- O14 = 2 A
O12 -- T5  -- O14 = 122.405 deg; O12 -- O14 = 3 A
       72.986 deg <-- 106.091 deg --> 122.861 deg

O13 -- T6  -- O15 = 117.319 deg; O13 -- O15 = 3 A
O13 -- T6  -- O16 = 106.071 deg; O13 -- O16 = 3 A
O13 -- T6  -- O17 = 109.678 deg; O13 -- O17 = 3 A
O15 -- T6  -- O16 = 107.046 deg; O15 -- O16 = 3 A
O15 -- T6  -- O17 = 108.384 deg; O15 -- O17 = 3 A
O16 -- T6  -- O17 = 107.954 deg; O16 -- O17 = 3 A
       106.071 deg <-- 109.409 deg --> 117.319 deg

        O-T-O SUMMARY
          Range  = 60.9118 deg <--> 164.3044 deg
          Mean   = 106.5378 deg
          StdDev = 19.6509 deg

        O--O SUMMARY
          Range  = 1.6392 A <--> 3.5032 A
          Mean   = 2.6017 A
          StdDev = 0.3819 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 156.822 deg ; T1  -- T1   3.2646 A

T1  -- O2  -- T1  = 118.104 deg ; T1  -- T1   2.8019 A

T1  -- O3  -- T2  = 135.822 deg ; T1  -- T2   3.0408 A

T1  -- O4  -- T3  = 141.989 deg ; T1  -- T3   2.8684 A

T2  -- O5  -- T2  = 124.036 deg ; T2  -- T2   2.8079 A

T2  -- O6  -- T2  = 116.410 deg ; T2  -- T2   2.8272 A

T2  -- O7  -- T4  = 146.438 deg ; T2  -- T4   3.0573 A

T3  -- O8  -- T3  = 128.156 deg ; T3  -- T3   2.9359 A

T3  -- O9  -- T3  = 137.568 deg ; T3  -- T3   3.0056 A

T3  -- O10 -- T5  = 142.121 deg ; T3  -- T5   3.1205 A

T4  -- O11 -- T5  = 107.370 deg ; T4  -- T5   2.4229 A

T4  -- O12 -- T5  = 142.302 deg ; T4  -- T5   3.2429 A
T4  -- O12 -- T5  = 103.748 deg ; T4  -- T5   2.4229 A
T4  -- O12 -- T4  =  38.818 deg ; T4  -- T4   1.1152 A

T4  -- O13 -- T6  = 151.615 deg ; T4  -- T6   3.2609 A
T4  -- O13 -- T6  = 122.216 deg ; T4  -- T6   3.2796 A
T4  -- O13 -- T4  =  32.296 deg ; T4  -- T4   1.1152 A

T5  -- O14 -- T5  = 120.851 deg ; T5  -- T5   2.8871 A

T6  -- O15 -- T6  = 131.689 deg ; T6  -- T6   3.0264 A

T6  -- O16 -- T6  = 127.544 deg ; T6  -- T6   2.9135 A

T6  -- O17 -- T6  = 144.506 deg ; T6  -- T6   3.1031 A


        T-O-T SUMMARY
          Range  = 32.2959° <--> 156.8224 deg
          Mean   = 122.4011 deg
          StdDev = 31.3267 deg

        T--T SUMMARY
          Range  = 1.1152 A <--> 3.2796 A
          Mean   = 2.7867 A
          StdDev = 0.5889 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O4  = 2.2608 A
O7  -- O12 = 2.1183 A
O7  -- O13 = 1.7421 A
O7  -- O11 = 1.6392 A
O11 -- O12 = 1.8093 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T4  has 6 oxygen-bridged T-atoms within 3.50 A
  T4  -- T4  = 1.1152 Angstrom
  T4  -- T5  = 2.4229 Angstrom
  T4  -- T6  = 3.2796 Angstrom
  T4  -- T2  = 3.0573 Angstrom
  T4  -- T5  = 3.2429 Angstrom
  T4  -- T6  = 3.2609 Angstrom
T5  -- T4  = 2.4229 Angstrom
T6  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T6  -- T4  = 3.2796 Angstrom
  T6  -- T4  = 3.2609 Angstrom
  T6  -- T6  = 3.0264 Angstrom
  T6  -- T6  = 2.9135 Angstrom
  T6  -- T6  = 3.1031 Angstrom