Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_194_6_105570507_Y4N_ib.cif"

There are 144 T-atoms per unit cell
There are 288 O-atoms per unit cell

Framework density = 18.70 T-atoms per nm^3
Material density = 1.866 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.4945 Angstrom
T1  -- O2  = 1.5843 Angstrom
T1  -- O7  = 1.8985 Angstrom
T1  -- O3  = 1.5535 Angstrom
T1  -- O4  = 1.6274 Angstrom
      mean = 1.6317 Angstrom

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5391 Angstrom
T2  -- O5  = 1.5037 Angstrom
T2  -- O6  = 1.5366 Angstrom
T2  -- O7  = 1.6878 Angstrom
      mean = 1.5668 Angstrom
        t1 = 0.064195  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.042707  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6508 Angstrom
T3  -- O7  = 1.6984 Angstrom
T3  -- O8  = 1.7843 Angstrom
T3  -- O9  = 1.8187 Angstrom
      mean = 1.7381 Angstrom
        t1 = 0.115666  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.076373  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.8603 Angstrom
T4  -- O10 = 1.7571 Angstrom
T4  -- O11 = 1.7403 Angstrom
T4  -- O12 = 1.6318 Angstrom
      mean = 1.7474 Angstrom
        t1 = 0.106947  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.058350  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O12 = 1.6177 Angstrom
T5  -- O13 = 1.6262 Angstrom
T5  -- O14 = 1.6021 Angstrom
T5  -- O15 = 1.6173 Angstrom
      mean = 1.6158 Angstrom
        t1 = 0.012496  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.012217  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T6  -- O15 = 1.6228 Angstrom
T6  -- O16 = 1.6118 Angstrom
T6  -- O17 = 1.6118 Angstrom
T6  -- O18 = 1.6161 Angstrom
      mean = 1.6156 Angstrom
        t1 = 0.005261  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002562  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4945 A <--> 1.8985 A
          Mean   = 1.6517 A
          StdDev = 0.1042 A

       t1 Range  = 0.0053 <-- 0.0508 --> 0.1157
       t2 Range  = 0.0026 <-- 0.0320 --> 0.0764

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 121.064 deg; O1  -- O2  = 3 A
O1  -- T1  -- O7  =  96.061 deg; O1  -- O7  = 3 A
O1  -- T1  -- O3  = 112.676 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  69.840 deg; O1  -- O4  = 2 A
O2  -- T1  -- O7  = 114.624 deg; O2  -- O7  = 3 A
O2  -- T1  -- O3  = 114.972 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 106.804 deg; O2  -- O4  = 3 A
O7  -- T1  -- O3  =  91.903 deg; O7  -- O3  = 2 A
O7  -- T1  -- O4  = 137.321 deg; O7  -- O4  = 3 A
O3  -- T1  -- O4  =  60.539 deg; O3  -- O4  = 2 A
       60.539 deg <-- 102.580 deg --> 137.321 deg

O3  -- T2  -- O5  = 121.028 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 117.984 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 101.055 deg; O3  -- O7  = 2 A
O5  -- T2  -- O6  =  97.609 deg; O5  -- O6  = 2 A
O5  -- T2  -- O7  = 102.108 deg; O5  -- O7  = 2 A
O6  -- T2  -- O7  = 116.964 deg; O6  -- O7  = 3 A
       97.609 deg <-- 109.458 deg --> 121.028 deg

O4  -- T3  -- O7  = 114.226 deg; O4  -- O7  = 3 A
O4  -- T3  -- O8  =  97.065 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 106.807 deg; O4  -- O9  = 3 A
O7  -- T3  -- O8  = 117.942 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  =  93.829 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 127.530 deg; O8  -- O9  = 3 A
       93.829 deg <-- 109.567 deg --> 127.530 deg

O9  -- T4  -- O10 = 116.097 deg; O9  -- O10 = 3 A
O9  -- T4  -- O11 = 114.611 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 = 100.205 deg; O9  -- O12 = 3 A
O10 -- T4  -- O11 = 115.936 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 104.726 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 102.094 deg; O11 -- O12 = 3 A
       100.205 deg <-- 108.945 deg --> 116.097 deg

O12 -- T5  -- O13 = 111.345 deg; O12 -- O13 = 3 A
O12 -- T5  -- O14 = 107.598 deg; O12 -- O14 = 3 A
O12 -- T5  -- O15 = 110.902 deg; O12 -- O15 = 3 A
O13 -- T5  -- O14 = 109.940 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 109.545 deg; O13 -- O15 = 3 A
O14 -- T5  -- O15 = 107.414 deg; O14 -- O15 = 3 A
       107.414 deg <-- 109.457 deg --> 111.345 deg

O15 -- T6  -- O16 = 108.993 deg; O15 -- O16 = 3 A
O15 -- T6  -- O17 = 109.470 deg; O15 -- O17 = 3 A
O15 -- T6  -- O18 = 110.400 deg; O15 -- O18 = 3 A
O16 -- T6  -- O17 = 109.456 deg; O16 -- O17 = 3 A
O16 -- T6  -- O18 = 109.504 deg; O16 -- O18 = 3 A
O17 -- T6  -- O18 = 109.002 deg; O17 -- O18 = 3 A
       108.993 deg <-- 109.471 deg --> 110.400 deg

        O-T-O SUMMARY
          Range  = 60.5393 deg <--> 137.3206 deg
          Mean   = 107.4229 deg
          StdDev = 13.6265 deg

        O--O SUMMARY
          Range  = 1.6047 A <--> 3.2857 A
          Mean   = 2.6529 A
          StdDev = 0.3049 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 171.650 deg ; T1  -- T1   2.9812 A

T1  -- O2  -- T1  = 108.464 deg ; T1  -- T1   2.5710 A

T1  -- O3  -- T2  =  84.699 deg ; T1  -- T2   2.0834 A

T1  -- O4  -- T3  = 139.469 deg ; T1  -- T3   3.0753 A

T2  -- O5  -- T2  = 151.250 deg ; T2  -- T2   2.9132 A

T2  -- O6  -- T2  = 103.950 deg ; T2  -- T2   2.4209 A

T1  -- O7  -- T2  =  70.753 deg ; T1  -- T2   2.0834 A
T1  -- O7  -- T3  =  92.603 deg ; T1  -- T3   2.6042 A
T2  -- O7  -- T3  = 130.979 deg ; T2  -- T3   3.0810 A

T3  -- O8  -- T3  = 136.895 deg ; T3  -- T3   3.3192 A

T3  -- O9  -- T4  = 155.535 deg ; T3  -- T4   3.5955 A

T4  -- O10 -- T4  = 161.568 deg ; T4  -- T4   3.4690 A

T4  -- O11 -- T4  = 153.751 deg ; T4  -- T4   3.3897 A

T4  -- O12 -- T5  = 131.432 deg ; T4  -- T5   2.9620 A

T5  -- O13 -- T5  = 128.408 deg ; T5  -- T5   2.9282 A

T5  -- O14 -- T5  = 166.116 deg ; T5  -- T5   3.1805 A

T5  -- O15 -- T6  = 121.923 deg ; T5  -- T6   2.8328 A

T6  -- O16 -- T6  = 168.745 deg ; T6  -- T6   3.2081 A

T6  -- O17 -- T6  = 133.359 deg ; T6  -- T6   2.9602 A

T6  -- O18 -- T6  = 135.971 deg ; T6  -- T6   2.9965 A


        T-O-T SUMMARY
          Range  = 70.7531° <--> 171.6498 deg
          Mean   = 132.3760 deg
          StdDev = 27.8228 deg

        T--T SUMMARY
          Range  = 2.0834 A <--> 3.5955 A
          Mean   = 2.9328 A
          StdDev = 0.4021 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O4  = 1.7904 A
O1  -- O4  = 1.7904 A
O3  -- O4  = 1.6047 A
O5  -- O6  = 2.2878 A
O5  -- O6  = 2.2878 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 oxygen-bridged T-atoms within 3.50 A
  T1  -- T1  = 2.9812 Angstrom
  T1  -- T1  = 2.5710 Angstrom
  T1  -- T2  = 2.0834 Angstrom
  T1  -- T3  = 2.6042 Angstrom
  T1  -- T3  = 3.0753 Angstrom
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 2.0834 Angstrom
  T2  -- T2  = 2.9132 Angstrom
  T2  -- T2  = 2.4209 Angstrom
  T2  -- T3  = 3.4796 Angstrom
  T2  -- T3  = 3.0810 Angstrom
T3  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T1  = 2.6042 Angstrom
  T3  -- T1  = 3.0753 Angstrom
  T3  -- T2  = 3.4796 Angstrom
  T3  -- T2  = 3.0810 Angstrom
  T3  -- T3  = 3.3192 Angstrom
T4  has only 3 neighboring T-atoms within 3.50 A, but 4 bridging O-atoms
  T4  -- T4  = 3.3897 Angstrom
  T4  -- T5  = 2.9620 Angstrom
  T4  -- T4  = 3.4690 Angstrom