Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_194_6_101581139_Nt6n9A.cif"

There are 144 T-atoms per unit cell
There are 288 O-atoms per unit cell

Framework density = 25.65 T-atoms per nm^3
Material density = 2.559 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6161 Angstrom
T1  -- O2  = 1.5992 Angstrom
T1  -- O3  = 1.5863 Angstrom
T1  -- O4  = 1.5455 Angstrom
      mean = 1.5867 Angstrom
        t1 = 0.053745  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.065620  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5560 Angstrom
T2  -- O5  = 1.7266 Angstrom
T2  -- O6  = 1.6530 Angstrom
T2  -- O7  = 1.7000 Angstrom
      mean = 1.6589 Angstrom
        t1 = 0.084174  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.057661  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.5721 Angstrom
T3  -- O8  = 1.6153 Angstrom
T3  -- O9  = 1.6364 Angstrom
T3  -- O10 = 1.4996 Angstrom
      mean = 1.5809 Angstrom
        t1 = 0.063557  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.053969  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.7319 Angstrom
T4  -- O11 = 1.6826 Angstrom
T4  -- O12 = 1.6450 Angstrom
T4  -- O13 = 1.7419 Angstrom
      mean = 1.7004 Angstrom
        t1 = 0.070636  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.032936  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.5727 Angstrom
T5  -- O14 = 1.6557 Angstrom
T5  -- O15 = 1.5733 Angstrom
T5  -- O16 = 1.6389 Angstrom
      mean = 1.6101 Angstrom
        t1 = 0.062379  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.040197  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T6  -- O13 = 1.5600 Angstrom
T6  -- O17 = 1.6111 Angstrom
T6  -- O13 = 1.7585 Angstrom
T6  -- O16 = 1.6479 Angstrom
T6  -- O18 = 1.6640 Angstrom
      mean = 1.6483 Angstrom

        T-O SUMMARY
          Range  = 1.4996 A <--> 1.7585 A
          Mean   = 1.6316 A
          StdDev = 0.0656 A

       t1 Range  = 0.0537 <-- 0.0557 --> 0.0842
       t2 Range  = 0.0329 <-- 0.0417 --> 0.0656

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.334 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 123.183 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 104.235 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 109.958 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 111.894 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  98.549 deg; O3  -- O4  = 2 A
       98.549 deg <-- 109.359 deg --> 123.183 deg

O3  -- T2  -- O5  = 111.326 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 106.357 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  =  90.081 deg; O3  -- O7  = 2 A
O5  -- T2  -- O6  = 113.239 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 120.217 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 112.451 deg; O6  -- O7  = 3 A
       90.081 deg <-- 108.945 deg --> 120.217 deg

O4  -- T3  -- O8  = 110.437 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 116.445 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 =  94.081 deg; O4  -- O10 = 2 A
O8  -- T3  -- O9  = 112.809 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 112.433 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.260 deg; O9  -- O10 = 3 A
       94.081 deg <-- 109.244 deg --> 116.445 deg

O7  -- T4  -- O11 = 106.066 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 105.587 deg; O7  -- O12 = 3 A
O7  -- T4  -- O13 = 114.619 deg; O7  -- O13 = 3 A
O11 -- T4  -- O12 = 102.788 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 117.457 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 109.090 deg; O12 -- O13 = 3 A
       102.788 deg <-- 109.268 deg --> 117.457 deg

O10 -- T5  -- O14 = 102.300 deg; O10 -- O14 = 3 A
O10 -- T5  -- O15 = 110.874 deg; O10 -- O15 = 3 A
O10 -- T5  -- O16 = 111.769 deg; O10 -- O16 = 3 A
O14 -- T5  -- O15 = 107.315 deg; O14 -- O15 = 3 A
O14 -- T5  -- O16 = 126.701 deg; O14 -- O16 = 3 A
O15 -- T5  -- O16 =  97.505 deg; O15 -- O16 = 2 A
       97.505 deg <-- 109.411 deg --> 126.701 deg

O13 -- T6  -- O17 =  78.354 deg; O13 -- O17 = 2 A
O13 -- T6  -- O13 = 110.393 deg; O13 -- O13 = 3 A
O13 -- T6  -- O16 = 137.510 deg; O13 -- O16 = 3 A
O13 -- T6  -- O18 = 122.670 deg; O13 -- O18 = 3 A
O17 -- T6  -- O13 =  72.823 deg; O17 -- O13 = 2 A
O17 -- T6  -- O16 = 129.680 deg; O17 -- O16 = 3 A
O17 -- T6  -- O18 =  92.939 deg; O17 -- O18 = 2 A
O13 -- T6  -- O16 =  62.560 deg; O13 -- O16 = 2 A
O13 -- T6  -- O18 = 120.789 deg; O13 -- O18 = 3 A
O16 -- T6  -- O18 =  90.735 deg; O16 -- O18 = 2 A
       62.560 deg <-- 101.845 deg --> 137.510 deg

        O-T-O SUMMARY
          Range  = 62.5596 deg <--> 137.5096 deg
          Mean   = 107.4892 deg
          StdDev = 14.8548 deg

        O--O SUMMARY
          Range  = 1.7712 A <--> 2.9901 A
          Mean   = 2.6110 A
          StdDev = 0.2822 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 118.011 deg ; T1  -- T1   2.7706 A

T1  -- O2  -- T1  = 124.704 deg ; T1  -- T1   2.8332 A

T1  -- O3  -- T2  = 118.627 deg ; T1  -- T2   2.7023 A

T1  -- O4  -- T3  = 140.454 deg ; T1  -- T3   2.9338 A

T2  -- O5  -- T2  = 158.121 deg ; T2  -- T2   3.3905 A

T2  -- O6  -- T2  = 149.581 deg ; T2  -- T2   3.1905 A

T2  -- O7  -- T4  = 133.912 deg ; T2  -- T4   3.1581 A

T3  -- O8  -- T3  = 116.647 deg ; T3  -- T3   2.7494 A

T3  -- O9  -- T3  = 114.867 deg ; T3  -- T3   2.7581 A

T3  -- O10 -- T5  = 137.085 deg ; T3  -- T5   2.8595 A

T4  -- O11 -- T4  = 130.049 deg ; T4  -- T4   3.0505 A

T4  -- O12 -- T4  = 151.395 deg ; T4  -- T4   3.1883 A

T4  -- O13 -- T6  = 109.643 deg ; T4  -- T6   2.7009 A
T4  -- O13 -- T6  = 172.793 deg ; T4  -- T6   3.4935 A
T6  -- O13 -- T6  =  68.495 deg ; T6  -- T6   1.8748 A

T5  -- O14 -- T5  = 110.970 deg ; T5  -- T5   2.7285 A

T5  -- O15 -- T5  = 125.435 deg ; T5  -- T5   2.7964 A

T5  -- O16 -- T6  = 152.664 deg ; T5  -- T6   3.1938 A

T6  -- O17 -- T6  =  71.157 deg ; T6  -- T6   1.8748 A

T6  -- O18 -- T6  = 168.684 deg ; T6  -- T6   3.3120 A


        T-O-T SUMMARY
          Range  = 68.4947° <--> 172.7928 deg
          Mean   = 128.6646 deg
          StdDev = 26.8269 deg

        T--T SUMMARY
          Range  = 1.8748 A <--> 3.4935 A
          Mean   = 2.8780 A
          StdDev = 0.4118 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O4  -- O10 = 2.2486 A
O13 -- O16 = 1.7712 A
O13 -- O17 = 2.0037 A

T-T-T analysis was not conducted.
T1  -- T2  = 2.7023 Angstrom
T1  -- T1  = 2.7706 Angstrom

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 2.7023 Angstrom
  T2  -- T2  = 3.4296 Angstrom
  T2  -- T2  = 3.3905 Angstrom
  T2  -- T2  = 3.1905 Angstrom
  T2  -- T4  = 3.1581 Angstrom
T3  -- T3  = 2.7494 Angstrom
T3  -- T3  = 2.7581 Angstrom
T4  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T2  = 3.1581 Angstrom
  T4  -- T4  = 3.0505 Angstrom
  T4  -- T4  = 3.1883 Angstrom
  T4  -- T5  = 3.3157 Angstrom
  T4  -- T6  = 2.7009 Angstrom
  T4  -- T6  = 3.4935 Angstrom
T5  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T5  -- T3  = 2.8595 Angstrom
  T5  -- T4  = 3.3157 Angstrom
  T5  -- T5  = 2.7285 Angstrom
  T5  -- T5  = 2.7964 Angstrom
  T5  -- T6  = 3.1938 Angstrom
T6  has 5 oxygen-bridged T-atoms within 3.50 A
  T6  -- T4  = 2.7009 Angstrom
  T6  -- T6  = 3.3120 Angstrom
  T6  -- T4  = 3.4935 Angstrom
  T6  -- T5  = 3.1938 Angstrom
  T6  -- T6  = 1.8748 Angstrom