Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_194_5_5813872_CBnkPd.cif"

There are 76 T-atoms per unit cell
There are 152 O-atoms per unit cell

Framework density = 20.21 T-atoms per nm^3
Material density = 2.017 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6912 Angstrom
T1  -- O4  = 1.5404 Angstrom
T1  -- O2  = 1.6687 Angstrom
T1  -- O3  = 1.7077 Angstrom
      mean = 1.6520 Angstrom
        t1 = 0.063811  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.039601  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.5416 Angstrom
T2  -- O5  = 1.6012 Angstrom
T2  -- O6  = 1.6159 Angstrom
T2  -- O7  = 1.5614 Angstrom
      mean = 1.5800 Angstrom
        t1 = 0.028319  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014937  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O8  = 1.7369 Angstrom
T3  -- O9  = 1.6038 Angstrom
T3  -- O9  = 1.6038 Angstrom
T3  -- O9  = 1.6038 Angstrom
      mean = 1.6370 Angstrom
        t1 = 0.083286  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.073179  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6098 Angstrom
T4  -- O7  = 1.6097 Angstrom
T4  -- O10 = 1.6831 Angstrom
T4  -- O11 = 1.6437 Angstrom
      mean = 1.6366 Angstrom
        t1 = 0.065140  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.039881  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O9  = 1.5983 Angstrom
T5  -- O11 = 1.5390 Angstrom
T5  -- O12 = 1.6313 Angstrom
T5  -- O12 = 1.6314 Angstrom
      mean = 1.6000 Angstrom
        t1 = 0.074382  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.063177  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5390 A <--> 1.7369 A
          Mean   = 1.6178 A
          StdDev = 0.0561 A

       t1 Range  = 0.0283 <-- 0.0630 --> 0.0833
       t2 Range  = 0.0149 <-- 0.0462 --> 0.0732

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O4  = 104.719 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  = 110.254 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 119.058 deg; O1  -- O3  = 3 A
O4  -- T1  -- O2  = 104.164 deg; O4  -- O2  = 3 A
O4  -- T1  -- O3  = 102.812 deg; O4  -- O3  = 3 A
O2  -- T1  -- O3  = 113.929 deg; O2  -- O3  = 3 A
       102.812 deg <-- 109.156 deg --> 119.058 deg

O4  -- T2  -- O5  = 108.499 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 108.025 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 107.412 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 112.885 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 111.073 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.757 deg; O6  -- O7  = 3 A
       107.412 deg <-- 109.442 deg --> 112.885 deg

O8  -- T3  -- O9  = 118.606 deg; O8  -- O9  = 3 A
O8  -- T3  -- O9  = 118.606 deg; O8  -- O9  = 3 A
O8  -- T3  -- O9  = 118.606 deg; O8  -- O9  = 3 A
O9  -- T3  -- O9  =  98.984 deg; O9  -- O9  = 2 A
O9  -- T3  -- O9  =  98.984 deg; O9  -- O9  = 2 A
O9  -- T3  -- O9  =  98.984 deg; O9  -- O9  = 2 A
       98.984 deg <-- 108.795 deg --> 118.606 deg

O7  -- T4  -- O7  = 112.089 deg; O7  -- O7  = 3 A
O7  -- T4  -- O10 = 107.831 deg; O7  -- O10 = 3 A
O7  -- T4  -- O11 = 100.049 deg; O7  -- O11 = 2 A
O7  -- T4  -- O10 = 107.837 deg; O7  -- O10 = 3 A
O7  -- T4  -- O11 = 100.059 deg; O7  -- O11 = 2 A
O10 -- T4  -- O11 = 128.535 deg; O10 -- O11 = 3 A
       100.049 deg <-- 109.400 deg --> 128.535 deg

O9  -- T5  -- O11 =  89.113 deg; O9  -- O11 = 2 A
O9  -- T5  -- O12 = 118.589 deg; O9  -- O12 = 3 A
O9  -- T5  -- O12 = 118.577 deg; O9  -- O12 = 3 A
O11 -- T5  -- O12 = 112.988 deg; O11 -- O12 = 3 A
O11 -- T5  -- O12 = 112.986 deg; O11 -- O12 = 3 A
O12 -- T5  -- O12 = 104.394 deg; O12 -- O12 = 3 A
       89.113 deg <-- 109.441 deg --> 118.589 deg

        O-T-O SUMMARY
          Range  = 89.1128 deg <--> 128.5354 deg
          Mean   = 108.3891 deg
          StdDev = 7.2221 deg

        O--O SUMMARY
          Range  = 2.2016 A <--> 2.9969 A
          Mean   = 2.6181 A
          StdDev = 0.1513 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.4504 A
T1  - O1  - T1  - O2  - T1  = 150.000 deg; T1  -- T1  = 6.1869 A
T1  - O1  - T1  - O3  - T2  =  97.190 deg; T1  -- T2  = 4.7216 A
T1  - O4  - T1  - O2  - T1  = 120.000 deg; T1  -- T1  = 5.3964 A
T1  - O4  - T1  - O3  - T2  =  85.949 deg; T1  -- T2  = 4.1711 A
T1  - O2  - T1  - O3  - T2  =  85.810 deg; T1  -- T2  = 4.2439 A

T1  - O4  - T2  - O5  - T2  =  94.051 deg; T1  -- T2  = 4.1711 A
T1  - O4  - T2  - O6  - T2  =  94.190 deg; T1  -- T2  = 4.2439 A
T1  - O4  - T2  - O7  - T4  =  95.095 deg; T1  -- T4  = 4.3098 A
T2  - O5  - T2  - O6  - T2  = 120.000 deg; T2  -- T2  = 4.6346 A
T2  - O5  - T2  - O7  - T4  = 170.759 deg; T2  -- T4  = 5.3836 A
T2  - O6  - T2  - O7  - T4  =  60.591 deg; T2  -- T4  = 2.7749 A

T3  - O8  - T3  - O9  - T5  = 132.125 deg; T3  -- T5  = 6.0221 A
T3  - O8  - T3  - O9  - T5  = 132.125 deg; T3  -- T5  = 6.0221 A
T3  - O8  - T3  - O9  - T5  = 132.125 deg; T3  -- T5  = 6.0221 A
T5  - O9  - T3  - O9  - T5  =  79.929 deg; T5  -- T5  = 3.9991 A
T5  - O9  - T3  - O9  - T5  =  79.929 deg; T5  -- T5  = 3.9991 A
T5  - O9  - T3  - O9  - T5  =  79.929 deg; T5  -- T5  = 3.9991 A

T2  - O7  - T4  - O7  - T2  =  58.815 deg; T2  -- T2  = 2.7251 A
T2  - O7  - T4  - O10 - T4  =  99.238 deg; T2  -- T4  = 4.1676 A
T2  - O7  - T4  - O11 - T5  = 110.264 deg; T2  -- T5  = 4.7313 A
T2  - O7  - T4  - O10 - T4  =  99.241 deg; T2  -- T4  = 4.1676 A
T2  - O7  - T4  - O11 - T5  = 110.267 deg; T2  -- T5  = 4.7314 A
T4  - O10 - T4  - O11 - T5  = 145.951 deg; T4  -- T5  = 5.4369 A

T3  - O9  - T5  - O11 - T4  =  81.924 deg; T3  -- T4  = 4.0018 A
T3  - O9  - T5  - O12 - T5  =  99.074 deg; T3  -- T5  = 4.6898 A
T3  - O9  - T5  - O12 - T5  =  99.078 deg; T3  -- T5  = 4.6898 A
T4  - O11 - T5  - O12 - T5  = 138.884 deg; T4  -- T5  = 5.6559 A
T4  - O11 - T5  - O12 - T5  = 138.892 deg; T4  -- T5  = 5.6559 A
T5  - O12 - T5  - O12 - T5  =  81.906 deg; T5  -- T5  = 3.9991 A

        T-T-T SUMMARY
          Range  = 58.8149 deg <--> 170.7590 deg
          Mean   = 103.5301 deg
          StdDev = 26.9572 deg

        T--T SUMMARY
          Range  = 2.7251 A <--> 6.1869 A
          Mean   = 4.5309 A
          StdDev = 0.8565 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 145.781 deg ; T1  -- T1   3.2328 A

T1  -- O2  -- T1  = 132.823 deg ; T1  -- T1   3.0586 A

T1  -- O3  -- T1  = 136.513 deg ; T1  -- T1   3.1723 A

T1  -- O4  -- T2  = 166.421 deg ; T1  -- T2   3.0604 A

T2  -- O5  -- T2  = 110.178 deg ; T2  -- T2   2.6262 A

T2  -- O6  -- T2  = 114.960 deg ; T2  -- T2   2.7251 A

T2  -- O7  -- T4  = 122.094 deg ; T2  -- T4   2.7749 A

T3  -- O8  -- T3  = 180.000 deg ; T3  -- T3   3.4738 A

T3  -- O9  -- T5  = 152.914 deg ; T3  -- T5   3.1131 A

T4  -- O10 -- T4  = 106.412 deg ; T4  -- T4   2.6957 A

T4  -- O11 -- T5  = 139.866 deg ; T4  -- T5   2.9897 A

T5  -- O12 -- T5  = 138.475 deg ; T5  -- T5   3.0506 A


        T-O-T SUMMARY
          Range  = 106.4120° <--> 180.0000 deg
          Mean   = 133.9205 deg
          StdDev = 18.7518 deg

        T--T SUMMARY
          Range  = 2.6262 A <--> 3.4738 A
          Mean   = 2.9622 A
          StdDev = 0.2184 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O9  -- O11 = 2.2016 A
T2  -- T2  = 2.6262 Angstrom
T2  -- T2  = 2.7251 Angstrom
T2  -- T4  = 2.7749 Angstrom
T4  -- T2  = 2.7749 Angstrom
T4  -- T2  = 2.7749 Angstrom
T4  -- T4  = 2.6957 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 16 28 47 71 100 138 186 231 284 343 408 482 552 630
TD10 = 831
Circuit symbol = 4.4.4.8_{2}.6.6_{2}
Weight = 11
Vertex symbol  = 4.4.4.12.6.8
Weight = 25

T2 (Si): multiplicity = 24
Coordination Sequence =
    1 4 8 16 29 44 66 96 131 169 214 267 325 381 440 517 601
TD10 = 778
Circuit symbol = 3.4.4.7_{2}.5.6_{2}
Weight = 10
Vertex symbol  = 3.4.4.8.6.8
Weight = 20

T3 (Si): multiplicity = 4
Coordination Sequence =
    1 4 9 16 32 61 84 103 128 169 234 274 308 364 441 547 641
TD10 = 841
Circuit symbol = 4.6.4.6.4.6
Weight = 17
Vertex symbol  = 4.6.4.6.4.6
Weight = 17

T4 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 31 48 76 108 138 174 221 269 326 393 460 523 593
TD10 = 831
Circuit symbol = 3.6.8.8.8.8
Weight = 28
Vertex symbol  = 3.6.8.8.8.8
Weight = 28

T5 (Si): multiplicity = 12
Coordination Sequence =
    1 4 9 19 35 54 78 103 138 183 217 264 322 376 453 541 622
TD10 = 841
Circuit symbol = 4.6.4.8_{2}.4.8_{2}
Weight = 21
Vertex symbol  = 4.6.4.8.4.8
Weight = 21

<TD10> = 816.368
Average ring size = 5.1818