Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_194_5_5274936_8QyAO2.cif"

There are 96 T-atoms per unit cell
There are 192 O-atoms per unit cell

Framework density = 17.34 T-atoms per nm^3
Material density = 1.730 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6195 Angstrom
T1  -- O3  = 1.6132 Angstrom
T1  -- O2  = 1.6211 Angstrom
T1  -- O4  = 1.6152 Angstrom
      mean = 1.6173 Angstrom
        t1 = 0.004971  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002181  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6107 Angstrom
T2  -- O5  = 1.6220 Angstrom
T2  -- O6  = 1.6288 Angstrom
T2  -- O7  = 1.6194 Angstrom
      mean = 1.6202 Angstrom
        t1 = 0.006954  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002169  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6162 Angstrom
T3  -- O6  = 1.6270 Angstrom
T3  -- O8  = 1.6204 Angstrom
T3  -- O9  = 1.6032 Angstrom
      mean = 1.6167 Angstrom
        t1 = 0.007367  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005493  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6205 Angstrom
T4  -- O7  = 1.6205 Angstrom
T4  -- O10 = 1.6146 Angstrom
T4  -- O11 = 1.6132 Angstrom
      mean = 1.6172 Angstrom
        t1 = 0.005201  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001741  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O9  = 1.6151 Angstrom
T5  -- O9  = 1.6151 Angstrom
T5  -- O12 = 1.6142 Angstrom
T5  -- O13 = 1.6155 Angstrom
      mean = 1.6150 Angstrom
        t1 = 0.004318  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002324  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6032 A <--> 1.6288 A
          Mean   = 1.6176 A
          StdDev = 0.0060 A

       t1 Range  = 0.0043 <-- 0.0058 --> 0.0074
       t2 Range  = 0.0017 <-- 0.0028 --> 0.0055

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 109.244 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.615 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.321 deg; O1  -- O4  = 3 A
O3  -- T1  -- O2  = 109.659 deg; O3  -- O2  = 3 A
O3  -- T1  -- O4  = 109.312 deg; O3  -- O4  = 3 A
O2  -- T1  -- O4  = 109.675 deg; O2  -- O4  = 3 A
       109.244 deg <-- 109.471 deg --> 109.675 deg

O3  -- T2  -- O5  = 109.677 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.206 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 109.535 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.846 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.715 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.845 deg; O6  -- O7  = 3 A
       108.845 deg <-- 109.471 deg --> 109.846 deg

O4  -- T3  -- O6  = 108.739 deg; O4  -- O6  = 3 A
O4  -- T3  -- O8  = 110.312 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 108.629 deg; O4  -- O9  = 3 A
O6  -- T3  -- O8  = 109.988 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 108.768 deg; O6  -- O9  = 3 A
O8  -- T3  -- O9  = 110.360 deg; O8  -- O9  = 3 A
       108.629 deg <-- 109.466 deg --> 110.360 deg

O7  -- T4  -- O7  = 109.770 deg; O7  -- O7  = 3 A
O7  -- T4  -- O10 = 109.324 deg; O7  -- O10 = 3 A
O7  -- T4  -- O11 = 109.699 deg; O7  -- O11 = 3 A
O7  -- T4  -- O10 = 109.324 deg; O7  -- O10 = 3 A
O7  -- T4  -- O11 = 109.699 deg; O7  -- O11 = 3 A
O10 -- T4  -- O11 = 109.008 deg; O10 -- O11 = 3 A
       109.008 deg <-- 109.471 deg --> 109.770 deg

O9  -- T5  -- O9  = 109.026 deg; O9  -- O9  = 3 A
O9  -- T5  -- O12 = 109.164 deg; O9  -- O12 = 3 A
O9  -- T5  -- O13 = 110.127 deg; O9  -- O13 = 3 A
O9  -- T5  -- O12 = 109.164 deg; O9  -- O12 = 3 A
O9  -- T5  -- O13 = 110.127 deg; O9  -- O13 = 3 A
O12 -- T5  -- O13 = 109.212 deg; O12 -- O13 = 3 A
       109.026 deg <-- 109.470 deg --> 110.127 deg

        O-T-O SUMMARY
          Range  = 108.6291 deg <--> 110.3602 deg
          Mean   = 109.4863 deg
          StdDev = 0.4611 deg

        O--O SUMMARY
          Range  = 2.6149 A <--> 2.6604 A
          Mean   = 2.6414 A
          StdDev = 0.0099 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T1  = 120.000 deg; T1  -- T1  = 5.3779 A
T1  - O1  - T1  - O2  - T2  = 118.950 deg; T1  -- T2  = 5.5077 A
T1  - O1  - T1  - O4  - T3  = 118.262 deg; T1  -- T3  = 5.3933 A
T1  - O3  - T1  - O2  - T2  =  90.159 deg; T1  -- T2  = 4.4292 A
T1  - O3  - T1  - O4  - T3  =  91.139 deg; T1  -- T3  = 4.3862 A
T2  - O2  - T1  - O4  - T3  = 111.958 deg; T2  -- T3  = 5.2438 A

T1  - O3  - T2  - O5  - T2  =  89.841 deg; T1  -- T2  = 4.4292 A
T1  - O3  - T2  - O6  - T3  = 103.736 deg; T1  -- T3  = 4.8452 A
T1  - O3  - T2  - O7  - T4  = 111.720 deg; T1  -- T4  = 5.2126 A
T2  - O5  - T2  - O6  - T3  = 151.611 deg; T2  -- T3  = 5.8064 A
T2  - O5  - T2  - O7  - T4  =  91.441 deg; T2  -- T4  = 4.3892 A
T3  - O6  - T2  - O7  - T4  = 105.948 deg; T3  -- T4  = 4.8038 A

T2  - O4  - T3  - O6  - T3  = 148.252 deg; T2  -- T3  = 5.8627 A
T2  - O4  - T3  - O8  - T5  = 104.622 deg; T2  -- T5  = 4.8117 A
T2  - O4  - T3  - O9  - T1  = 109.915 deg; T2  -- T1  = 4.9503 A
T3  - O6  - T3  - O8  - T5  =  89.781 deg; T3  -- T5  = 4.4453 A
T3  - O6  - T3  - O9  - T1  =  88.861 deg; T3  -- T1  = 4.3862 A
T5  - O8  - T3  - O9  - T1  = 113.743 deg; T5  -- T1  = 5.2332 A

T2  - O7  - T4  - O7  - T2  = 111.577 deg; T2  -- T2  = 5.0921 A
T2  - O7  - T4  - O10 - T4  = 119.935 deg; T2  -- T4  = 5.4522 A
T2  - O7  - T4  - O11 - T4  =  88.559 deg; T2  -- T4  = 4.3892 A
T2  - O7  - T4  - O10 - T4  = 119.935 deg; T2  -- T4  = 5.4522 A
T2  - O7  - T4  - O11 - T4  =  88.559 deg; T2  -- T4  = 4.3892 A
T4  - O10 - T4  - O11 - T4  = 120.000 deg; T4  -- T4  = 5.5643 A

T3  - O9  - T5  - O9  - T3  = 115.387 deg; T3  -- T3  = 5.3097 A
T3  - O9  - T5  - O12 - T5  = 117.447 deg; T3  -- T5  = 5.4393 A
T3  - O9  - T5  - O13 - T5  =  90.219 deg; T3  -- T5  = 4.4453 A
T3  - O9  - T5  - O12 - T5  = 117.447 deg; T3  -- T5  = 5.4393 A
T3  - O9  - T5  - O13 - T5  =  90.219 deg; T3  -- T5  = 4.4453 A
T5  - O12 - T5  - O13 - T5  = 120.000 deg; T5  -- T5  = 5.5051 A

        T-T-T SUMMARY
          Range  = 88.5591 deg <--> 151.6110 deg
          Mean   = 107.8481 deg
          StdDev = 16.7312 deg

        T--T SUMMARY
          Range  = 4.3862 A <--> 5.8627 A
          Mean   = 4.9779 A
          StdDev = 0.4843 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 157.233 deg ; T1  -- T1   3.1754 A

T1  -- O2  -- T1  = 138.717 deg ; T1  -- T1   3.0340 A

T1  -- O3  -- T2  = 173.317 deg ; T1  -- T2   3.2184 A

T1  -- O4  -- T3  = 148.205 deg ; T1  -- T3   3.1078 A

T2  -- O5  -- T2  = 140.383 deg ; T2  -- T2   3.0518 A

T2  -- O6  -- T3  = 128.893 deg ; T2  -- T3   2.9373 A

T2  -- O7  -- T4  = 143.708 deg ; T2  -- T4   3.0788 A

T3  -- O8  -- T3  = 153.962 deg ; T3  -- T3   3.1575 A

T3  -- O9  -- T5  = 154.845 deg ; T3  -- T5   3.1411 A

T4  -- O10 -- T4  = 170.602 deg ; T4  -- T4   3.2184 A

T4  -- O11 -- T4  = 167.413 deg ; T4  -- T4   3.2067 A

T5  -- O12 -- T5  = 173.381 deg ; T5  -- T5   3.2230 A

T5  -- O13 -- T5  = 151.803 deg ; T5  -- T5   3.1336 A


        T-O-T SUMMARY
          Range  = 128.8926° <--> 173.3810 deg
          Mean   = 151.8964 deg
          StdDev = 13.3141 deg

        T--T SUMMARY
          Range  = 2.9373 A <--> 3.2230 A
          Mean   = 3.1175 A
          StdDev = 0.0832 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 20 33 50 73 102 134 165 196 232 277 333 399 464 521
TD10 = 788
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6
Weight = 19

T2 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 21 35 51 72 97 127 162 202 247 289 333 385 440 503
TD10 = 782
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.12
Weight = 25

T3 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 21 35 51 72 97 127 162 202 247 289 333 385 440 503
TD10 = 782
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.12
Weight = 25

T4 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 73 102 134 165 196 232 277 333 399 464 521
TD10 = 788
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6
Weight = 19

T5 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 73 102 134 165 196 232 277 333 399 464 521
TD10 = 788
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6
Weight = 19

<TD10> = 785.000
Average ring size = 5.3333