Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_194_5_3835223_5ByYcc.cif"

There are 108 T-atoms per unit cell
There are 216 O-atoms per unit cell

Framework density = 20.49 T-atoms per nm^3
Material density = 2.045 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5871 Angstrom
T1  -- O2  = 1.6540 Angstrom
T1  -- O3  = 1.6304 Angstrom
T1  -- O4  = 1.6403 Angstrom
      mean = 1.6279 Angstrom
        t1 = 0.038827  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.029095  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6625 Angstrom
T2  -- O5  = 1.6472 Angstrom
T2  -- O6  = 1.6967 Angstrom
T2  -- O7  = 1.6470 Angstrom
      mean = 1.6633 Angstrom
        t1 = 0.060949  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.032315  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6320 Angstrom
T3  -- O8  = 1.6521 Angstrom
T3  -- O9  = 1.6153 Angstrom
T3  -- O10 = 1.6068 Angstrom
      mean = 1.6266 Angstrom
        t1 = 0.024499  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.016198  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6359 Angstrom
T4  -- O11 = 1.6173 Angstrom
T4  -- O12 = 1.6666 Angstrom
T4  -- O13 = 1.5288 Angstrom
      mean = 1.6121 Angstrom
        t1 = 0.058374  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.074830  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O13 = 1.5930 Angstrom
T5  -- O13 = 1.5930 Angstrom
T5  -- O14 = 1.5652 Angstrom
T5  -- O15 = 1.5852 Angstrom
      mean = 1.5841 Angstrom
        t1 = 0.029355  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021741  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5288 A <--> 1.6967 A
          Mean   = 1.6271 A
          StdDev = 0.0380 A

       t1 Range  = 0.0245 <-- 0.0424 --> 0.0609
       t2 Range  = 0.0162 <-- 0.0348 --> 0.0748

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.941 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 106.720 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 102.150 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 118.971 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.324 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.373 deg; O3  -- O4  = 3 A
       102.150 deg <-- 109.246 deg --> 118.971 deg

O3  -- T2  -- O5  = 115.531 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 106.829 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 105.053 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 113.750 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  =  96.685 deg; O5  -- O7  = 2 A
O6  -- T2  -- O7  = 118.894 deg; O6  -- O7  = 3 A
       96.685 deg <-- 109.457 deg --> 118.894 deg

O4  -- T3  -- O8  = 116.018 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 107.641 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 108.215 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 107.790 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 108.283 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 108.710 deg; O9  -- O10 = 3 A
       107.641 deg <-- 109.443 deg --> 116.018 deg

O7  -- T4  -- O11 = 109.581 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 122.523 deg; O7  -- O12 = 3 A
O7  -- T4  -- O13 =  98.537 deg; O7  -- O13 = 2 A
O11 -- T4  -- O12 = 110.392 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 107.918 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 106.391 deg; O12 -- O13 = 3 A
       98.537 deg <-- 109.223 deg --> 122.523 deg

O13 -- T5  -- O13 = 113.953 deg; O13 -- O13 = 3 A
O13 -- T5  -- O14 = 106.112 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 107.292 deg; O13 -- O15 = 3 A
O13 -- T5  -- O14 = 106.112 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 107.292 deg; O13 -- O15 = 3 A
O14 -- T5  -- O15 = 116.335 deg; O14 -- O15 = 3 A
       106.112 deg <-- 109.516 deg --> 116.335 deg

        O-T-O SUMMARY
          Range  = 96.6851 deg <--> 122.5227 deg
          Mean   = 109.1478 deg
          StdDev = 5.8331 deg

        O--O SUMMARY
          Range  = 2.3992 A <--> 2.8957 A
          Mean   = 2.6421 A
          StdDev = 0.1228 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.2199 A
T1  - O1  - T1  - O3  - T2  =  81.360 deg; T1  -- T2  = 4.0459 A
T1  - O1  - T1  - O4  - T3  = 113.189 deg; T1  -- T3  = 5.3226 A
T1  - O2  - T1  - O3  - T2  = 157.020 deg; T1  -- T2  = 5.7039 A
T1  - O2  - T1  - O4  - T3  =  89.625 deg; T1  -- T3  = 4.2331 A
T2  - O3  - T1  - O4  - T3  = 113.353 deg; T2  -- T3  = 5.2155 A

T1  - O3  - T2  - O5  - T2  = 109.282 deg; T1  -- T2  = 5.0623 A
T1  - O3  - T2  - O6  - T4  = 116.754 deg; T1  -- T4  = 5.0920 A
T1  - O3  - T2  - O7  - T2  =  81.790 deg; T1  -- T2  = 4.0459 A
T2  - O5  - T2  - O6  - T4  = 127.942 deg; T2  -- T4  = 5.4970 A
T2  - O5  - T2  - O7  - T2  = 128.468 deg; T2  -- T2  = 5.6875 A
T4  - O6  - T2  - O7  - T2  =  82.337 deg; T4  -- T2  = 4.0108 A

T1  - O4  - T3  - O8  - T3  = 156.807 deg; T1  -- T3  = 5.9571 A
T1  - O4  - T3  - O9  - T3  =  90.375 deg; T1  -- T3  = 4.2331 A
T1  - O4  - T3  - O10 - T3  = 109.740 deg; T1  -- T3  = 5.0852 A
T3  - O8  - T3  - O9  - T3  =  90.000 deg; T3  -- T3  = 3.9740 A
T3  - O8  - T3  - O10 - T3  =  90.000 deg; T3  -- T3  = 4.1628 A
T3  - O9  - T3  - O10 - T3  = 120.000 deg; T3  -- T3  = 4.9849 A

T2  - O7  - T4  - O11 - T4  = 127.861 deg; T2  -- T4  = 5.3100 A
T2  - O7  - T4  - O12 - T4  = 137.419 deg; T2  -- T4  = 5.3032 A
T2  - O7  - T4  - O13 - T5  =  95.506 deg; T2  -- T5  = 4.2625 A
T4  - O11 - T4  - O12 - T4  =  90.000 deg; T4  -- T4  = 4.0426 A
T4  - O11 - T4  - O13 - T5  =  58.165 deg; T4  -- T5  = 2.8120 A
T4  - O12 - T4  - O13 - T5  =  88.897 deg; T4  -- T5  = 3.8926 A

T4  - O13 - T5  - O13 - T4  =  63.670 deg; T4  -- T4  = 2.9666 A
T4  - O13 - T5  - O14 - T5  =  91.103 deg; T4  -- T5  = 3.8926 A
T4  - O13 - T5  - O15 - T5  = 136.547 deg; T4  -- T5  = 5.1301 A
T4  - O13 - T5  - O14 - T5  =  91.103 deg; T4  -- T5  = 3.8926 A
T4  - O13 - T5  - O15 - T5  = 136.547 deg; T4  -- T5  = 5.1301 A
T5  - O14 - T5  - O15 - T5  = 120.000 deg; T5  -- T5  = 4.6319 A

        T-T-T SUMMARY
          Range  = 58.1648 deg <--> 157.0201 deg
          Mean   = 106.3196 deg
          StdDev = 25.7336 deg

        T--T SUMMARY
          Range  = 2.8120 A <--> 5.9571 A
          Mean   = 4.6052 A
          StdDev = 0.8078 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 174.153 deg ; T1  -- T1   3.1700 A

T1  -- O2  -- T1  = 114.717 deg ; T1  -- T1   2.7855 A

T1  -- O3  -- T2  = 134.335 deg ; T1  -- T2   3.0349 A

T1  -- O4  -- T3  = 156.850 deg ; T1  -- T3   3.2058 A

T2  -- O5  -- T2  = 145.224 deg ; T2  -- T2   3.1438 A

T2  -- O6  -- T2  = 138.349 deg ; T2  -- T2   3.1716 A

T2  -- O7  -- T4  = 127.538 deg ; T2  -- T4   2.9448 A

T3  -- O8  -- T3  = 120.946 deg ; T3  -- T3   2.8750 A

T3  -- O9  -- T3  = 116.261 deg ; T3  -- T3   2.7435 A

T3  -- O10 -- T3  = 139.038 deg ; T3  -- T3   3.0105 A

T4  -- O11 -- T4  = 133.030 deg ; T4  -- T4   2.9666 A

T4  -- O12 -- T4  = 110.957 deg ; T4  -- T4   2.7463 A

T4  -- O13 -- T5  = 128.510 deg ; T4  -- T5   2.8120 A

T5  -- O14 -- T5  = 119.956 deg ; T5  -- T5   2.7102 A

T5  -- O15 -- T5  = 112.629 deg ; T5  -- T5   2.6381 A


        T-O-T SUMMARY
          Range  = 110.9566° <--> 174.1534 deg
          Mean   = 132.5857 deg
          StdDev = 17.0643 deg

        T--T SUMMARY
          Range  = 2.6381 A <--> 3.2058 A
          Mean   = 2.9489 A
          StdDev = 0.1745 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7855 Angstrom
T3  -- T3  = 2.7435 Angstrom
T4  -- T4  = 2.7463 Angstrom
T5  -- T5  = 2.6381 Angstrom
T5  -- T5  = 2.7102 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 19 35 51 70 100 138 179 220 264 320 389 463 532 596
TD10 = 826
Circuit symbol = 4.4.4.6.6.6
Weight = 11
Vertex symbol  = 4.4.4.6.10_{2}.12_{3}
Weight = 36

T2 (Si): multiplicity = 24
Coordination Sequence =
    1 4 11 21 33 53 77 106 144 183 225 278 340 402 466 537 613
TD10 = 858
Circuit symbol = 4.6.6.6.6.8
Weight = 18
Vertex symbol  = 4.6.6.6.6.10_{2}
Weight = 25

T3 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 16 28 50 79 108 133 160 200 256 324 392 455 517 584
TD10 = 788
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.10_{4}
Weight = 22

T4 (Si): multiplicity = 24
Coordination Sequence =
    1 4 8 17 32 51 74 101 134 180 236 281 323 382 449 518 601
TD10 = 838
Circuit symbol = 3.6.4.6.4.7
Weight = 13
Vertex symbol  = 3.6.4.6.4.10_{4}
Weight = 21

T5 (Si): multiplicity = 12
Coordination Sequence =
    1 4 8 13 22 40 64 91 122 162 212 266 316 367 424 489 564
TD10 = 739
Circuit symbol = 3.6.4.6.4.6
Weight = 16
Vertex symbol  = 3.6.4.6.4.6
Weight = 16

<TD10> = 817.667
Average ring size = 5.9677