Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_194_5_3269992_3ulL14.cif"

There are 108 T-atoms per unit cell
There are 216 O-atoms per unit cell

Framework density = 15.15 T-atoms per nm^3
Material density = 1.512 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6291 Angstrom
T1  -- O2  = 1.6207 Angstrom
T1  -- O3  = 1.6092 Angstrom
T1  -- O4  = 1.5948 Angstrom
      mean = 1.6135 Angstrom
        t1 = 0.009919  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006130  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.5977 Angstrom
T2  -- O5  = 1.6312 Angstrom
T2  -- O6  = 1.6460 Angstrom
T2  -- O7  = 1.6381 Angstrom
      mean = 1.6282 Angstrom
        t1 = 0.024634  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.025282  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6139 Angstrom
T3  -- O8  = 1.6422 Angstrom
T3  -- O9  = 1.5646 Angstrom
T3  -- O10 = 1.6040 Angstrom
      mean = 1.6062 Angstrom
        t1 = 0.025777  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.029414  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.5690 Angstrom
T4  -- O11 = 1.6277 Angstrom
T4  -- O7  = 1.6401 Angstrom
T4  -- O12 = 1.6296 Angstrom
      mean = 1.6166 Angstrom
        t1 = 0.016290  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019068  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6159 Angstrom
T5  -- O13 = 1.6103 Angstrom
T5  -- O10 = 1.6159 Angstrom
T5  -- O13 = 1.6103 Angstrom
      mean = 1.6131 Angstrom
        t1 = 0.007439  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008637  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5646 A <--> 1.6460 A
          Mean   = 1.6158 A
          StdDev = 0.0227 A

       t1 Range  = 0.0074 <-- 0.0168 --> 0.0258
       t2 Range  = 0.0061 <-- 0.0177 --> 0.0294

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.971 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.994 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 111.897 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.353 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.188 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 108.435 deg; O3  -- O4  = 3 A
       108.188 deg <-- 109.473 deg --> 111.897 deg

O4  -- T2  -- O5  = 107.761 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 104.729 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 110.421 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 111.506 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.973 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 113.262 deg; O6  -- O7  = 3 A
       104.729 deg <-- 109.442 deg --> 113.262 deg

O6  -- T3  -- O8  = 114.676 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 104.916 deg; O6  -- O9  = 3 A
O6  -- T3  -- O10 = 108.951 deg; O6  -- O10 = 3 A
O8  -- T3  -- O9  = 108.588 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.941 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.590 deg; O9  -- O10 = 3 A
       104.916 deg <-- 109.443 deg --> 114.676 deg

O9  -- T4  -- O11 = 112.283 deg; O9  -- O11 = 3 A
O9  -- T4  -- O7  = 106.500 deg; O9  -- O7  = 3 A
O9  -- T4  -- O12 = 108.308 deg; O9  -- O12 = 3 A
O11 -- T4  -- O7  = 110.204 deg; O11 -- O7  = 3 A
O11 -- T4  -- O12 = 110.096 deg; O11 -- O12 = 3 A
O7  -- T4  -- O12 = 109.345 deg; O7  -- O12 = 3 A
       106.500 deg <-- 109.456 deg --> 112.283 deg

O10 -- T5  -- O13 = 108.294 deg; O10 -- O13 = 3 A
O10 -- T5  -- O10 = 111.077 deg; O10 -- O10 = 3 A
O10 -- T5  -- O13 = 110.160 deg; O10 -- O13 = 3 A
O13 -- T5  -- O10 = 110.160 deg; O13 -- O10 = 3 A
O13 -- T5  -- O13 = 108.833 deg; O13 -- O13 = 3 A
O10 -- T5  -- O13 = 108.294 deg; O10 -- O13 = 3 A
       108.294 deg <-- 109.469 deg --> 111.077 deg

        O-T-O SUMMARY
          Range  = 104.7292 deg <--> 114.6756 deg
          Mean   = 109.4575 deg
          StdDev = 2.1655 deg

        O--O SUMMARY
          Range  = 2.5205 A <--> 2.7427 A
          Mean   = 2.6370 A
          StdDev = 0.0494 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 3.9480 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.0981 A
T1  - O1  - T1  - O4  - T2  = 146.371 deg; T1  -- T2  = 5.7342 A
T1  - O2  - T1  - O3  - T1  = 120.000 deg; T1  -- T1  = 4.9955 A
T1  - O2  - T1  - O4  - T2  =  90.917 deg; T1  -- T2  = 4.2600 A
T1  - O3  - T1  - O4  - T2  = 118.126 deg; T1  -- T2  = 5.2957 A

T1  - O4  - T2  - O5  - T2  =  89.083 deg; T1  -- T2  = 4.2600 A
T1  - O4  - T2  - O6  - T3  = 125.659 deg; T1  -- T3  = 5.5549 A
T1  - O4  - T2  - O7  - T4  = 114.160 deg; T1  -- T4  = 5.3779 A
T2  - O5  - T2  - O6  - T3  = 134.740 deg; T2  -- T3  = 5.4827 A
T2  - O5  - T2  - O7  - T4  =  90.609 deg; T2  -- T4  = 4.3446 A
T3  - O6  - T2  - O7  - T4  =  98.227 deg; T3  -- T4  = 4.7494 A

T2  - O6  - T3  - O8  - T3  = 158.440 deg; T2  -- T3  = 5.8152 A
T2  - O6  - T3  - O9  - T4  =  85.596 deg; T2  -- T4  = 4.2001 A
T2  - O6  - T3  - O10 - T5  = 109.530 deg; T2  -- T5  = 5.0525 A
T3  - O8  - T3  - O9  - T4  =  91.103 deg; T3  -- T4  = 4.2754 A
T3  - O8  - T3  - O10 - T5  =  92.016 deg; T3  -- T5  = 4.3116 A
T4  - O9  - T3  - O10 - T5  = 101.154 deg; T4  -- T5  = 4.8276 A

T3  - O9  - T4  - O11 - T4  = 132.729 deg; T3  -- T4  = 5.5630 A
T3  - O9  - T4  - O7  - T4  =  88.897 deg; T3  -- T4  = 4.2754 A
T3  - O9  - T4  - O12 - T2  = 110.315 deg; T3  -- T2  = 5.2074 A
T4  - O11 - T4  - O7  - T4  = 120.000 deg; T4  -- T4  = 5.1356 A
T4  - O11 - T4  - O12 - T2  =  89.391 deg; T4  -- T2  = 4.3446 A
T4  - O7  - T4  - O12 - T2  = 117.848 deg; T4  -- T2  = 5.3139 A

T3  - O10 - T5  - O13 - T5  =  87.984 deg; T3  -- T5  = 4.3116 A
T3  - O10 - T5  - O10 - T5  = 133.361 deg; T3  -- T5  = 5.7004 A
T3  - O10 - T5  - O13 - T3  =  98.704 deg; T3  -- T3  = 4.7447 A
T5  - O13 - T5  - O10 - T5  = 120.000 deg; T5  -- T5  = 5.3360 A
T5  - O13 - T5  - O13 - T3  = 133.361 deg; T5  -- T3  = 5.7004 A
T5  - O10 - T5  - O13 - T3  =  87.984 deg; T5  -- T3  = 4.3116 A

        T-T-T SUMMARY
          Range  = 85.5959 deg <--> 158.4399 deg
          Mean   = 109.2702 deg
          StdDev = 20.0767 deg

        T--T SUMMARY
          Range  = 3.9480 A <--> 5.8152 A
          Mean   = 4.9085 A
          StdDev = 0.5739 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 118.793 deg ; T1  -- T1   2.8044 A

T1  -- O2  -- T1  = 118.031 deg ; T1  -- T1   2.7788 A

T1  -- O3  -- T1  = 136.406 deg ; T1  -- T1   2.9882 A

T1  -- O4  -- T2  = 171.999 deg ; T1  -- T2   3.1847 A

T2  -- O5  -- T2  = 124.014 deg ; T2  -- T2   2.8807 A

T2  -- O6  -- T3  = 139.538 deg ; T2  -- T3   3.0588 A

T2  -- O7  -- T4  = 158.721 deg ; T2  -- T4   3.2218 A

T3  -- O8  -- T3  = 121.133 deg ; T3  -- T3   2.8607 A

T3  -- O9  -- T4  = 170.440 deg ; T3  -- T4   3.1227 A

T3  -- O10 -- T5  = 152.371 deg ; T3  -- T5   3.1268 A

T4  -- O11 -- T4  = 129.896 deg ; T4  -- T4   2.9492 A

T4  -- O12 -- T4  = 132.303 deg ; T4  -- T4   2.9809 A

T5  -- O13 -- T5  = 146.096 deg ; T5  -- T5   3.0807 A


        T-O-T SUMMARY
          Range  = 118.0310° <--> 171.9989 deg
          Mean   = 139.7354 deg
          StdDev = 18.3393 deg

        T--T SUMMARY
          Range  = 2.7788 A <--> 3.2218 A
          Mean   = 2.9998 A
          StdDev = 0.1403 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7788 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 17 28 43 64 90 118 144 170 202 243 295 355 413 464
TD10 = 688
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.12
Weight = 23

T2 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 18 28 43 62 86 113 143 177 209 249 298 348 405 459
TD10 = 685
Circuit symbol = 4.5.4.8_{2}.6.6_{2}
Weight = 17
Vertex symbol  = 4.5.4.8.6.6
Weight = 17

T3 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 19 30 44 60 82 111 143 177 213 252 294 343 395 451
TD10 = 681
Circuit symbol = 4.5.4.6_{2}.5.7
Weight = 13
Vertex symbol  = 4.5.4.6.5.12_{2}
Weight = 28

T4 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 18 27 40 61 89 119 146 170 199 240 297 360 416 464
TD10 = 685
Circuit symbol = 4.4.5.6.6.6
Weight = 18
Vertex symbol  = 4.4.5.6.6.6
Weight = 18

T5 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 19 30 43 58 78 104 138 178 219 256 291 328 378 440
TD10 = 663
Circuit symbol = 4.4.5_{2}.6.7_{3}.7_{3}
Weight = 16
Vertex symbol  = 4.4.5_{2}.6.8.8
Weight = 22

<TD10> = 682.333
Average ring size = 5.2615