Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_194_5_2916871_yKXWh6.cif"

There are 120 T-atoms per unit cell
There are 240 O-atoms per unit cell

Framework density = 18.14 T-atoms per nm^3
Material density = 1.810 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6384 Angstrom
T1  -- O2  = 1.5899 Angstrom
T1  -- O3  = 1.6403 Angstrom
T1  -- O4  = 1.6229 Angstrom
      mean = 1.6228 Angstrom
        t1 = 0.026134  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.025547  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6199 Angstrom
T2  -- O5  = 1.6105 Angstrom
T2  -- O6  = 1.6293 Angstrom
T2  -- O7  = 1.6475 Angstrom
      mean = 1.6268 Angstrom
        t1 = 0.025520  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021836  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6318 Angstrom
T3  -- O8  = 1.6228 Angstrom
T3  -- O9  = 1.6214 Angstrom
T3  -- O10 = 1.6122 Angstrom
      mean = 1.6221 Angstrom
        t1 = 0.011302  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006237  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O6  = 1.6139 Angstrom
T4  -- O10 = 1.6213 Angstrom
T4  -- O11 = 1.6398 Angstrom
T4  -- O12 = 1.5555 Angstrom
      mean = 1.6076 Angstrom
        t1 = 0.028036  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.032308  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O12 = 1.5754 Angstrom
T5  -- O13 = 1.6385 Angstrom
T5  -- O14 = 1.6315 Angstrom
T5  -- O7  = 1.6450 Angstrom
      mean = 1.6226 Angstrom
        t1 = 0.024707  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018238  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5555 A <--> 1.6475 A
          Mean   = 1.6204 A
          StdDev = 0.0229 A

       t1 Range  = 0.0113 <-- 0.0231 --> 0.0280
       t2 Range  = 0.0062 <-- 0.0208 --> 0.0323

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.559 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 112.911 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 111.671 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 106.905 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 104.813 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 111.495 deg; O3  -- O4  = 3 A
       104.813 deg <-- 109.392 deg --> 112.911 deg

O3  -- T2  -- O5  = 107.287 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 105.557 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 112.688 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 107.805 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 108.740 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 114.428 deg; O6  -- O7  = 3 A
       105.557 deg <-- 109.417 deg --> 114.428 deg

O4  -- T3  -- O8  = 111.009 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.821 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 107.116 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 109.848 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.181 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.821 deg; O9  -- O10 = 3 A
       107.116 deg <-- 109.466 deg --> 111.009 deg

O6  -- T4  -- O10 = 110.494 deg; O6  -- O10 = 3 A
O6  -- T4  -- O11 = 114.487 deg; O6  -- O11 = 3 A
O6  -- T4  -- O12 = 104.374 deg; O6  -- O12 = 3 A
O10 -- T4  -- O11 = 109.705 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 108.581 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 108.931 deg; O11 -- O12 = 3 A
       104.374 deg <-- 109.429 deg --> 114.487 deg

O12 -- T5  -- O13 = 114.759 deg; O12 -- O13 = 3 A
O12 -- T5  -- O14 = 108.552 deg; O12 -- O14 = 3 A
O12 -- T5  -- O7  = 103.510 deg; O12 -- O7  = 3 A
O13 -- T5  -- O14 = 110.569 deg; O13 -- O14 = 3 A
O13 -- T5  -- O7  = 109.725 deg; O13 -- O7  = 3 A
O14 -- T5  -- O7  = 109.431 deg; O14 -- O7  = 3 A
       103.510 deg <-- 109.425 deg --> 114.759 deg

        O-T-O SUMMARY
          Range  = 103.5104 deg <--> 114.7594 deg
          Mean   = 109.4135 deg
          StdDev = 2.8696 deg

        O--O SUMMARY
          Range  = 2.5042 A <--> 2.7548 A
          Mean   = 2.6443 A
          StdDev = 0.0621 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.2552 A
T1  - O1  - T1  - O3  - T2  = 137.006 deg; T1  -- T2  = 5.5181 A
T1  - O1  - T1  - O4  - T3  = 130.993 deg; T1  -- T3  = 5.3134 A
T1  - O2  - T1  - O3  - T2  = 112.052 deg; T1  -- T2  = 5.0280 A
T1  - O2  - T1  - O4  - T3  =  91.033 deg; T1  -- T3  = 4.2621 A
T2  - O3  - T1  - O4  - T3  =  86.732 deg; T2  -- T3  = 4.0419 A

T1  - O3  - T2  - O5  - T2  = 132.900 deg; T1  -- T2  = 5.4958 A
T1  - O3  - T2  - O6  - T4  =  81.603 deg; T1  -- T4  = 3.9565 A
T1  - O3  - T2  - O7  - T5  = 131.378 deg; T1  -- T5  = 5.7030 A
T2  - O5  - T2  - O6  - T4  = 125.000 deg; T2  -- T4  = 5.3864 A
T2  - O5  - T2  - O7  - T5  =  88.701 deg; T2  -- T5  = 4.3904 A
T4  - O6  - T2  - O7  - T5  =  94.132 deg; T4  -- T5  = 4.6394 A

T1  - O4  - T3  - O8  - T3  = 131.490 deg; T1  -- T3  = 5.3771 A
T1  - O4  - T3  - O9  - T4  =  88.256 deg; T1  -- T4  = 3.9565 A
T1  - O4  - T3  - O10 - T3  =  88.967 deg; T1  -- T3  = 4.2621 A
T3  - O8  - T3  - O9  - T4  =  88.357 deg; T3  -- T4  = 4.0342 A
T3  - O8  - T3  - O10 - T3  = 120.000 deg; T3  -- T3  = 5.3520 A
T4  - O9  - T3  - O10 - T3  = 142.974 deg; T4  -- T3  = 5.6557 A

T2  - O6  - T4  - O10 - T3  =  87.269 deg; T2  -- T3  = 4.0419 A
T2  - O6  - T4  - O11 - T4  = 161.744 deg; T2  -- T4  = 5.8318 A
T2  - O6  - T4  - O12 - T5  =  95.709 deg; T2  -- T5  = 4.4436 A
T3  - O10 - T4  - O11 - T4  =  91.643 deg; T3  -- T4  = 4.0342 A
T3  - O10 - T4  - O12 - T5  = 159.874 deg; T3  -- T5  = 5.6225 A
T4  - O11 - T4  - O12 - T5  =  91.565 deg; T4  -- T5  = 4.1335 A

T4  - O12 - T5  - O13 - T5  = 128.776 deg; T4  -- T5  = 5.2163 A
T4  - O12 - T5  - O14 - T5  =  88.435 deg; T4  -- T5  = 4.1335 A
T4  - O12 - T5  - O7  - T2  = 119.098 deg; T4  -- T2  = 5.3427 A
T5  - O13 - T5  - O14 - T5  = 120.000 deg; T5  -- T5  = 5.0745 A
T5  - O13 - T5  - O7  - T2  =  91.299 deg; T5  -- T2  = 4.3904 A
T5  - O14 - T5  - O7  - T2  = 110.768 deg; T5  -- T2  = 5.1613 A

        T-T-T SUMMARY
          Range  = 81.6033 deg <--> 161.7444 deg
          Mean   = 110.8272 deg
          StdDev = 23.4400 deg

        T--T SUMMARY
          Range  = 3.9565 A <--> 5.8318 A
          Mean   = 4.8201 A
          StdDev = 0.6430 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 127.765 deg ; T1  -- T1   2.9421 A

T1  -- O2  -- T1  = 150.396 deg ; T1  -- T1   3.0742 A

T1  -- O3  -- T2  = 132.877 deg ; T1  -- T2   2.9884 A

T1  -- O4  -- T3  = 125.788 deg ; T1  -- T3   2.8972 A

T2  -- O5  -- T2  = 137.952 deg ; T2  -- T2   3.0066 A

T2  -- O6  -- T4  = 141.923 deg ; T2  -- T4   3.0658 A

T2  -- O7  -- T5  = 166.074 deg ; T2  -- T5   3.2682 A

T3  -- O8  -- T3  = 156.706 deg ; T3  -- T3   3.1787 A

T3  -- O9  -- T3  = 135.401 deg ; T3  -- T3   3.0003 A

T3  -- O10 -- T4  = 118.864 deg ; T3  -- T4   2.7842 A

T4  -- O11 -- T4  = 120.026 deg ; T4  -- T4   2.8406 A

T4  -- O12 -- T5  = 138.324 deg ; T4  -- T5   2.9261 A

T5  -- O13 -- T5  = 121.447 deg ; T5  -- T5   2.8585 A

T5  -- O14 -- T5  = 133.717 deg ; T5  -- T5   3.0005 A


        T-O-T SUMMARY
          Range  = 118.8638° <--> 166.0742 deg
          Mean   = 136.2329 deg
          StdDev = 13.4684 deg

        T--T SUMMARY
          Range  = 2.7842 A <--> 3.2682 A
          Mean   = 2.9880 A
          StdDev = 0.1265 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T3  -- T4  = 2.7842 Angstrom
T4  -- T3  = 2.7842 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 18 32 48 68 96 126 155 190 234 282 328 377 438 507
TD10 = 747
Circuit symbol = 4.4.4.8_{3}.6.6_{2}
Weight = 16
Vertex symbol  = 4.4.4.8.6.8
Weight = 21

T2 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 19 31 49 71 94 122 159 199 236 279 334 391 444 506
TD10 = 759
Circuit symbol = 4.4.6.6.6.8_{3}
Weight = 20
Vertex symbol  = 4.4.6.6.6.8
Weight = 20

T3 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 17 30 49 73 99 127 160 197 236 279 330 389 451 513
TD10 = 766
Circuit symbol = 4.4.4.6.6.6
Weight = 11
Vertex symbol  = 4.4.4.6.8.8
Weight = 20

T4 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 18 31 46 67 96 126 155 191 237 285 333 388 447 509
TD10 = 744
Circuit symbol = 4.4.4.6_{2}.6.6
Weight = 14
Vertex symbol  = 4.4.4.6_{2}.10.10
Weight = 24

T5 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 19 31 48 70 96 125 158 197 239 283 333 392 456 515
TD10 = 759
Circuit symbol = 4.4.6.6.6.6
Weight = 18
Vertex symbol  = 4.4.6.6.6.6
Weight = 18

<TD10> = 755.000
Average ring size = 5.2468