Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_194_5_2823123_Mz1xEA.cif"

There are 120 T-atoms per unit cell
There are 240 O-atoms per unit cell

Framework density = 19.34 T-atoms per nm^3
Material density = 1.930 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6112 Angstrom
T1  -- O2  = 1.6265 Angstrom
T1  -- O3  = 1.5853 Angstrom
T1  -- O4  = 1.6060 Angstrom
      mean = 1.6072 Angstrom
        t1 = 0.015041  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.009626  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6067 Angstrom
T2  -- O5  = 1.7224 Angstrom
T2  -- O6  = 1.6555 Angstrom
T2  -- O7  = 1.7199 Angstrom
      mean = 1.6761 Angstrom
        t1 = 0.069388  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.063362  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6050 Angstrom
T3  -- O8  = 1.6457 Angstrom
T3  -- O9  = 1.7026 Angstrom
T3  -- O10 = 1.6591 Angstrom
      mean = 1.6531 Angstrom
        t1 = 0.047411  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.024679  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.6369 Angstrom
T4  -- O11 = 1.7270 Angstrom
T4  -- O7  = 1.6911 Angstrom
T4  -- O9  = 1.7716 Angstrom
T4  -- O12 = 1.6111 Angstrom
      mean = 1.6875 Angstrom

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O12 = 1.4974 Angstrom
T5  -- O14 = 1.5467 Angstrom
T5  -- O10 = 1.6225 Angstrom
T5  -- O13 = 1.5161 Angstrom
      mean = 1.5457 Angstrom
        t1 = 0.117788  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.147593  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4974 A <--> 1.7716 A
          Mean   = 1.6365 A
          StdDev = 0.0684 A

       t1 Range  = 0.0150 <-- 0.0499 --> 0.1178
       t2 Range  = 0.0096 <-- 0.0491 --> 0.1476

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.888 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.901 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.768 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.472 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 112.334 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 106.408 deg; O3  -- O4  = 3 A
       106.408 deg <-- 109.462 deg --> 112.334 deg

O3  -- T2  -- O5  = 104.752 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 100.142 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 106.732 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 111.759 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 121.042 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 110.005 deg; O6  -- O7  = 3 A
       100.142 deg <-- 109.072 deg --> 121.042 deg

O4  -- T3  -- O8  = 106.969 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 108.847 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 104.065 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 111.562 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 106.312 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 118.327 deg; O9  -- O10 = 3 A
       104.065 deg <-- 109.347 deg --> 118.327 deg

O9  -- T4  -- O11 = 107.075 deg; O9  -- O11 = 3 A
O9  -- T4  -- O7  = 164.006 deg; O9  -- O7  = 3 A
O9  -- T4  -- O9  =  92.281 deg; O9  -- O9  = 2 A
O9  -- T4  -- O12 = 114.101 deg; O9  -- O12 = 3 A
O11 -- T4  -- O7  =  86.819 deg; O11 -- O7  = 2 A
O11 -- T4  -- O9  = 114.377 deg; O11 -- O9  = 3 A
O11 -- T4  -- O12 = 120.952 deg; O11 -- O12 = 3 A
O7  -- T4  -- O9  =  74.392 deg; O7  -- O9  = 2 A
O7  -- T4  -- O12 =  62.481 deg; O7  -- O12 = 2 A
O9  -- T4  -- O12 = 104.501 deg; O9  -- O12 = 3 A
       62.481 deg <-- 104.098 deg --> 164.006 deg

O12 -- T5  -- O14 = 127.748 deg; O12 -- O14 = 3 A
O12 -- T5  -- O10 =  77.113 deg; O12 -- O10 = 2 A
O12 -- T5  -- O13 = 119.582 deg; O12 -- O13 = 3 A
O14 -- T5  -- O10 = 111.143 deg; O14 -- O10 = 3 A
O14 -- T5  -- O13 = 110.915 deg; O14 -- O13 = 3 A
O10 -- T5  -- O13 =  96.004 deg; O10 -- O13 = 2 A
       77.113 deg <-- 107.084 deg --> 127.748 deg

        O-T-O SUMMARY
          Range  = 62.4811 deg <--> 164.0057 deg
          Mean   = 107.2152 deg
          StdDev = 16.9567 deg

        O--O SUMMARY
          Range  = 1.7140 A <--> 3.2956 A
          Mean   = 2.6132 A
          StdDev = 0.2892 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 158.771 deg ; T1  -- T1   3.1672 A

T1  -- O2  -- T1  = 135.825 deg ; T1  -- T1   3.0142 A

T1  -- O3  -- T2  = 133.387 deg ; T1  -- T2   2.9315 A

T1  -- O4  -- T3  = 151.283 deg ; T1  -- T3   3.1107 A

T2  -- O5  -- T2  = 151.781 deg ; T2  -- T2   3.3409 A

T2  -- O6  -- T2  = 134.147 deg ; T2  -- T2   3.0495 A

T2  -- O7  -- T4  = 155.281 deg ; T2  -- T4   3.3319 A

T3  -- O8  -- T3  = 131.636 deg ; T3  -- T3   3.0027 A

T3  -- O9  -- T4  = 142.169 deg ; T3  -- T4   3.2867 A
T3  -- O9  -- T4  =  79.758 deg ; T3  -- T4   2.1418 A
T4  -- O9  -- T4  =  79.397 deg ; T4  -- T4   2.1796 A

T3  -- O10 -- T5  = 141.916 deg ; T3  -- T5   3.1021 A

T4  -- O11 -- T4  = 166.697 deg ; T4  -- T4   3.4308 A

T4  -- O12 -- T5  = 112.969 deg ; T4  -- T5   2.5925 A

T5  -- O13 -- T5  = 130.661 deg ; T5  -- T5   2.7555 A

T5  -- O14 -- T5  = 128.640 deg ; T5  -- T5   2.7880 A


        T-O-T SUMMARY
          Range  = 79.3969° <--> 166.6974 deg
          Mean   = 133.3948 deg
          StdDev = 24.1265 deg

        T--T SUMMARY
          Range  = 2.1418 A <--> 3.4308 A
          Mean   = 2.9516 A
          StdDev = 0.3709 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O7  -- O9  = 2.0943 A
O7  -- O12 = 1.7140 A
O10 -- O12 = 1.9471 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 2.9315 Angstrom
  T2  -- T2  = 3.3409 Angstrom
  T2  -- T2  = 3.0495 Angstrom
  T2  -- T4  = 3.3319 Angstrom
  T2  -- T5  = 2.5673 Angstrom
T3  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T1  = 3.1107 Angstrom
  T3  -- T3  = 3.0027 Angstrom
  T3  -- T4  = 2.1418 Angstrom
  T3  -- T4  = 3.2867 Angstrom
  T3  -- T5  = 3.1021 Angstrom
T4  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T4  -- T3  = 2.1418 Angstrom
  T4  -- T4  = 2.1796 Angstrom
  T4  -- T4  = 3.4308 Angstrom
  T4  -- T2  = 3.3319 Angstrom
  T4  -- T3  = 3.2867 Angstrom
  T4  -- T5  = 2.5925 Angstrom
T5  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T5  -- T2  = 2.5673 Angstrom
  T5  -- T4  = 2.5925 Angstrom
  T5  -- T5  = 2.7555 Angstrom
  T5  -- T5  = 2.7880 Angstrom
  T5  -- T3  = 3.1021 Angstrom